This research aims to increase the production lifetime of oil and gas
wells through avoiding the problems that production casing string
may be exposed to. Such problems are caused by the effect of different
drilling fluids as well as other fluids normally existed in the annular
behind casing at the none-cemented intervals.
This research aims to decrease the cost of last production stages
through decreasing the cost of potential casing repair by avoiding the
problems that casing string may be exposed to. Such problems are
caused by the temperature effect of salt dril
ling fluids as well as other
fluids normally existed in the annular behind casing at the nonecemented
intervals.
The corrosion inhibition of transmision steel in 1M HCl solution in
the presence of Vanillin at temperature (20,30,40,50,60)°C at
concentration between (100-500) ppm for two hours were studied
using weight loss method.
The corrosion inhibition of transmision steel in 1M HCl solution in
the presence of Succinic acid at temperature (20,30,40,50,60)°C at
concentration between (10-6- 10-4) M for two hours were studied
using weight loss method.
Corrosion is the most important problem in the process of oil production, Its results are: sudden fracture, high economic cost and great loss in oil equipment. Appropriate solutions have been suggested to extend the life of facilities, and to avoid c
orrosion phenomenon which may get the facility out of service, But, finding the main
reasons causing this phenomenon, and studying the factors that contribute to increase or reduce the spread of corrosion requires more urgent attention.
In this paper, the data of the pressure has been analyzed in three crude oil pipelines and focus was on the values during the days where changes were irregular. In the same period, the study of internal corrosion rate was being done, using weight loss method. It has been noticed that when the value of pressure is greater than 2 Mpa, the
internal corrosion rate will be above the maximum. allowable limit which is 4 mil per year (MPY), while the internal corrosion rate will be within the acceptable range when the pressure is not greater than 1 Mpa.