دراسة الخصائص البنيوية والميكانيكية وسرعة وتردد الأمواج فوق الصوتية المتولدة من مُركب الانضغاط المغناطيسي 〖Co〗_x 〖Ni〗_(1-x) 〖Fe〗_2 O_4 عند النسب x= (0.0, 1.0)

This research includes prepare magnetostrictive compound at ratio x = (0.0, 1.0) by ceramic method at 1200 ℃ sintering temperature. studied some of structural properties by X-ray diffraction technique, and mechanical properties by Fourier-transform infrared FT-IR technique. This is to determine the speed and frequency of ultrasonic waves that's can be generated using the prepared compound. The results show formation the cubic spinel structure of ferrite, and values of Average crystallite size at nm. We observed at ratio x = 1.0 increase in values of Average crystallite size, lattice parameter, and decrease in values of density, and Young's coefficient. The results also showed the frequency of ultrasonic generated at the kHz and MHz ranges, the speed and frequency of the ultrasonic waves generated by are higher than the speed and frequency of the cobalt Ferrite .

يتضمن هذا البحث تحضير مُركب الانضغاط المغناطيسي عند النسب x= (0.0, 1.0) بالطريقة السيراميكية عند درجة حرارة تلبيد 1200 . دُرست بعض خصائصه البنيوية بتقنية انعراج الأشعة السينية XRD، والميكانيكية بتقنية تحويل فُورييه للأشعة تحت الحمراء FT-IR. وذلك بهدف تحديد سرعة وتردد الأمواج التي يمكن توليدها باستخدام المُركب المُحضر. تُظهر النتائج تَشكُل بنية السبينيل المكعب المميز للفرايت، وأن متوسط أبعاد الحبيبة من مرتبة الـ nm. كما لاحظنا عند النسبة x=1.0 زيادة في قيم كل من متوسط أبعاد الحبيبة وثابت الشبكة البلورية، وبالمقابل نقصان قيم كل من الكثافة، ومعامل يونغ للمُركب. تُبين النتائج أيضاً أن تردد الأمواج فوق الصوتية التي يمكن توليدها يقع ضمن المجالين kHz والـ MHz، أما الأمواج فوق الصوتية المتولدة من فرايت النيكل لها سرعة وتردد أعلى مقارنة مع الأمواج فوق الصوتية المتولدة من فرايت الكوبالت .