Improve the rheological properties of asphalt (60-70) by adding polypropylene

تحسين الخواص الريولوجية للبيتومين (60-70) بإضافة البولي بروبلين

1460   2   20   0.0 ( 0 )
 Publication date 2018
  fields Transportation
and research's language is العربية
 Created by Shamra Editor




Ask ChatGPT about the research

Asphalt plays the role of envelope and bonding in asphalt gable, and is exposed to a range of changes that start from the stage of production of asphalt mosses to the stage of investment under the influence of traffic loads and weather factors. The aim of this research is to investigate the possibility of using polypropylene polymer to modify the properties of the asphalt binder and to increase its resistance to high temperatures and different climatic conditions by modifying the asphalt by adding polypropylene by (1, 2, 3, 4, 6, 8%) And perform traditional tests on modified asphalt samples . Using Thin film oven test RTFOT test to perform the short-term Aging on normal and modified asphalt samples, heat loss, residual Penetration and aging index, And conduct a structural composition test to determine asphalt compounds. The results of the study showed that the values of Penetration tend to decrease with the increase of the percentage of addition while the degree of Softening point. The results showed increased resistance of asphalt modified to the thermal conditions. The optimum percentage of polypropylene is 3% Loss on heat at the lowest level.


Artificial intelligence review:
Research summary
يلعب البيتومين دورًا حيويًا في صناعة المجبول البيتوميني، حيث يعمل كمادة رابطة للحصويات. يتعرض البيتومين لمجموعة من التغيرات بدءًا من مرحلة الإنتاج وحتى مرحلة الاستخدام تحت تأثير الحمولات المرورية والعوامل الجوية. يهدف هذا البحث إلى تحسين خواص البيتومين (60-70) بإضافة بوليمير البولي بروبلين بنسب مختلفة (1، 2، 3، 4، 6، 8%). تم إجراء اختبارات تقليدية على العينات المعدلة، مثل اختبار الغرز، الاستطالة، ونقطة التمييع، بالإضافة إلى حساب دليل الغرز. كما تم استخدام فرن الطبقة الرقيقة الدوار لإجراء اختبار التقادم قصير الأمد. أظهرت النتائج أن قيم الغرز تنخفض مع زيادة نسبة الإضافة، بينما ترتفع درجة التمييع. كما زادت مقاومة البيتومين المعدل للظروف الحرارية، وكانت النسبة المثلى لإضافة البولي بروبلين هي 7%، حيث يكون دليل التقادم في الحالة الموجبة والفاقد بالحرارة في أدنى مستوى.
Critical review
دراسة نقدية: يعتبر البحث خطوة مهمة نحو تحسين خواص البيتومين باستخدام البولي بروبلين، وقد تم تقديم منهجية علمية دقيقة لإجراء التجارب والاختبارات. ومع ذلك، كان من الممكن تقديم تحليل أكثر تفصيلًا حول تأثير إضافة البولي بروبلين على الخواص الميكانيكية للبيتومين، مثل مقاومة التشوه والزحف. كما أن الدراسة لم تتطرق بشكل كافٍ إلى تأثير العوامل البيئية المختلفة مثل الرطوبة والأمطار على أداء البيتومين المعدل. بالإضافة إلى ذلك، كان من المفيد تضمين مقارنة مع أنواع أخرى من البوليميرات المستخدمة في تعديل البيتومين لتقديم رؤية شاملة حول الفوائد والعيوب.
Questions related to the research
  1. ما هو الهدف الرئيسي من البحث؟

    الهدف الرئيسي من البحث هو تحسين خواص البيتومين (60-70) بإضافة بوليمير البولي بروبلين لزيادة مقاومته لدرجات الحرارة المرتفعة والظروف المناخية المختلفة.

  2. ما هي النسبة المثلى لإضافة البولي بروبلين إلى البيتومين؟

    النسبة المثلى لإضافة البولي بروبلين هي 7%، حيث يكون دليل التقادم في الحالة الموجبة والفاقد بالحرارة في أدنى مستوى.

  3. ما هي الاختبارات التي تم إجراؤها على العينات المعدلة؟

    تم إجراء اختبارات الغرز، الاستطالة، نقطة التمييع، وحساب دليل الغرز على العينات المعدلة، بالإضافة إلى اختبار التقادم قصير الأمد باستخدام فرن الطبقة الرقيقة الدوار.

  4. ما هي النتائج الرئيسية التي توصلت إليها الدراسة؟

    أظهرت النتائج أن قيم الغرز تنخفض مع زيادة نسبة الإضافة، بينما ترتفع درجة التمييع. كما زادت مقاومة البيتومين المعدل للظروف الحرارية، وكانت النسبة المثلى لإضافة البولي بروبلين هي 7%.


References used
Henglong Zhang, Zihao Chen, Guoqing Xu, Caijun Shi. Evaluation of aging behaviors of asphalt binders through different rheological indices . Fuel 221 (2018) 78–88
Samy Dekhli, Khedidja Ait Mokhtar, Ferhat Hammoum and Djaffar Si Bachir . Rheological Behaviour of Ethylene-Vinyl-Acetate (EVA) Modified Road Bitumen . Journal of Applied Sciences Volume 15 (3): 444-455, 2015
Maria A. Vargas , Miguel A. Vargas , Antonio Sanchez-Solis , Octavio Manero . Asphalt/polyethylene blends: Rheological properties, microstructure and viscosity modeling . Construction and Building Materials 45 (2013) 243–250
rate research

Read More

The objective of this research is to study the effect of wood ash in rheological properties of Self – compacting mortar (SCM). By implemented some mixtures with different percentage from wood ash with two kinds of cement and three kinds of super plasticizer and study the effect in slump flow and yield stress to this mixtures.
This paper is targeting towards studying on the possibility to modify some properties of unsaturated Polyester compounds by adding rubber materials in order to improve its flexibility property. For this target, Waste of cars' tires was used in two forms powder and pieces, and the liquid rubber Styrene-butadiene was used as another type of rubber. After that the modification was detected by measuring the possibility of the resulted compound materials to absorb vibration power, and reduce the noise that is produced by eccentric crankshaft circulation at different rotating speeds, (300, 500, 700) rpm. Test results demonstrate that there will be Modification in the construction of the compounds at low rotating speeds (300 rpm). On the other hand, it demonstrates different results at high rotating speeds.
The purpose of this research is to study the improvement of soil properties by the addition of lime in certain percentages. The soil used in this study was obtained from the Baseet region, which is located by the Syrian coast. We have studied the e ffect of lime on the consistency, the swell characteristics and the shear strength of soil. The results of this study have shown a remarkable reduction of both liquid and shrinkage limits, and the plasticity index with the increase of lime percentage. As for plasticity limit, it increases in the beginning then decreases slightly with the rising of lime percentage. For the volumetric variation, the susceptibility of swelling and the shrinkage of improved soil with lime decrease, and the free swelling and the swelling pressure become almost negligible with 4% of lime. Based on the shear strength results, we can indicate a notable increase in the friction angle and cohesion of soil with increasing of lime percentage up to 8% of lime. After that, these two factors decrease.
Some kinetic parameters have been determined in this work for thermal and catalytic cracking of the mixed of polyethylene and polypropylene using batch method. The cracking reaction was carried out at different temperature 470,490 and 510oC under atmospheric pressure. The mass of products (liquid and gas fractions) were determined and used to plot the curves of the thermal and catalytic decomposition. We used two types of catalysts: Syrian natural Zeolite and the same after loading with sulfate ions using impregnation method. The thermal cracking has a long time and has firs-pseud order reaction. While in the case of catalytic process we note that the reaction finished in the short time and the process is the Zero-pseud order reaction. The rate of the cracking increased very much, the rate constant was k1=0.0032.min-1 in the thermal cracking at 4700C and ko=0.111.min-1 in the case of catalytic cracking in presence of Z catalyst and ko= 0.206 min-1 in presence of 15-SO4 2-/Z as catalytic at the same temperature. In the other hand activation energy was 208.7 kj/mol in the thermal process and decreased to 116.6 kj/mol at Z catalytic presence and to 87.3 kj/mol at 15-SO4 2-/Z catalytic presence.
This research with additives of kaolin is being carried out in order to improve different types of clay soil. It was studied the nature and extent of the change on final product.

suggested questions

comments
Fetching comments Fetching comments
Sign in to be able to follow your search criteria
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا