We investigated the crystal structure and superconducting properties of As-grown and high-pressure-annealed PrO0.5F0.5BiS2. We found that the high-pressure annealing generates uniaxial lattice contraction along the c axis. Both As-grown and high-pres
sure-annealed PrO0.5F0.5BiS2 show bulk superconductivity. The Tc of PrO0.5F0.5BiS2 is clearly enhanced from Tczero = 3.6 K to Tczero = 5.5 K by high-pressure annealing. Unexpectedly, the semiconducting characteristics is relatively enhanced by high-pressure annealing. Namely, we assume that the enhancement of Tc can not be understood by an increase of electron carriers. Having considered these facts, we conclude that the enhancement of Tc correlates with uniaxial lattice contraction along the c axis in PrO0.5F0.5BiS2.
We show the observation of the coexistence of bulk superconductivity and ferromagnetism in CeO1-xFxBiS2(x = 0 - 1.0) prepared by annealing under high-pressure. In CeO1-xFxBiS2 system, both superconductivity and two types of ferromagnetism with respec
tive magnetic transition temperatures of 4.5 K and 7.5 K are induced upon systematic F substitution. This fact suggests that carriers generated by the substitution of O by F are supplied to not only the BiS2 superconducting layers but also the CeO blocking layers. Furthermore, the highest superconducting transition temperature is observed when the ferromagnetism is also enhanced, which implies that superconductivity and ferromagnetism are linked to each other in the CeO1-xFxBiS2 system.
F-substituted NdOBiS2 superconducting single crystals were grown using CsCl/KCl flux. This is the first example of the single-crystal growth of a BiS2-based superconductor. The obtained single crystals had a plate-like shape with a size of 1-2 mm and
a well-developed ab-plane. The crystal structure of the grown crystals was determined by single-crystal X-ray diffraction analysis to be the tetragonal space group P4/nmm (#129) with a = 3.996(3) A and c = 13.464(6) A. The chemical formula of the grown crystals was approximately Nd0.98(0.06)O0.7(0.1)F0.3(0.1)Bi0.98(0.04)S2, and Cs, K, and Cl were not detected in the grown crystals by electron probe microanalysis. The grown crystals had a critical temperature of approximately 5 K. The superconducting anisotropy of the single crystals was estimated to be about 30 from the effective mass model and the upper critical field.
Correlation between crystal structure and superconducting properties of the BiS2-based superconductor LaO0.5F0.5BiS2 was investigated. We have prepared LaO0.5F0.5BiS2 polycrystalline samples with various lattice constants. It was found that the annea
ling the sample under high pressure generated uniaxial strain along the c axis. Further, the highly-strained sample showed higher superconducting properties. We concluded that the uniaxial strain along the c axis was positively linked with the enhancement of superconductivity in the LaO1-xFxBiS2 system.
We report the evolution of superconductivity and the phase diagram of the KxFe2-ySe2-zTez (z=0-0.6) crystals grown by a simple one-step synthesis. No structural transition is observed in any crystals, while lattice parameters exhibit a systematic exp
ansion with Te content. The Tc exhibits a gradual decrease with increasing Te content from Tconset = 32.9 K at z = 0 to Tconset = 27.9 K at z = 0.5, followed by a sudden suppression of superconductivity at z = 0.6. Upon approaching a Te concentration of 0.6, the shielding volume fraction decreases and eventually drops to zero. Simultaneously, hump positions in r-T curve shift to lower temperatures. These results suggest that isovalent substitution of Te for Se in KxFe2-ySe2 crystals suppresses the superconductivity in this system.
We have successfully synthesized a new BiS2-based superconductor NdOBiS2 with F-doping. This compound is composed of superconducting BiS2 layers and blocking NdO layers, which indicates that the BiS2 layer is the one of the common superconducting lay
ers like the CuO2 layer of cuprates or Fe-As layer of Fe-based superconductors. We can obtain NdO1-xFxBiS2 with bulk superconductivity by a solid-state reaction under ambient pressure. Therefore, NdO1-xFxBiS2 should be the suitable material to elucidate the mechanism of superconductivity in the BiS2-layer.
Layered superconductors have provided some interesting fields in condensed matter physics owing to the low dimensionality of their electronic states. For example, the high-Tc (high transition temperature) cuprates and the Fe-based superconductors pos
sess a layered crystal structure composed of a stacking of spacer (blocking) layers and conduction (superconducting) layers, CuO2 planes or Fe-Anion layers. The spacer layers provide carriers to the conduction layers and induce exotic superconductivity. Recently, we have reported superconductivity in the novel BiS2-based layered compound Bi4O4S3. It was found that superconductivity of Bi4O4S3 originates from the BiS2 layers. The crystal structure is composed of a stacking of BiS2 superconducting layers and the spacer layers, which resembles those of high-Tc cuprate and the Fe-based superconductors. Here we report a discovery of a new type of BiS2-based layered superconductor LaO1-xFxBiS2, with a Tc as high as 10.6 K.
The red wine dependence of superconductivity in FeTe0.8S0.2 was investigated. Samples with a higher shielding volume fraction had a tendency to show a higher concentration of tartaric acid in red wine. We found the tartaric acid is one of the key factors to induce superconductivity in FeTe0.8S0.2.