Register a new userStudy of Parameters of heat treatment for Alloys (Aluminum-Copper)
دراسة بارامترات المعالجة الحرارية لسبائك الألمنيوم – نحاس
1917
2 86
0
(
0
)
Authors
وردان وحود( باحث )
Created by
Shamra Editor
Ask ChatGPT about the research
في هذا العمل, تم تجهيز سبائك من الألمنيوم – نحاس, حيث أُضيفت كميات من النحاس إلى الألمنيوم بنسب مختلفة ( 2.5- 4 - 4.5 ) بحيث لا تتعدى حد الإشباع للألمنيوم ( 6% نحاس ).
In this work, the processing of aluminum alloys - copper, which added amounts of copper to aluminum in different parentages (2.5- 4-4.5%) so as not to exceed the limit of saturation Aluminum 6 %( copper).
Artificial intelligence review:
Research summary
تتناول هذه الدراسة تأثير بارامترات المعالجة الحرارية على سبائك الألمنيوم-نحاس، حيث تمت إضافة نسب مختلفة من النحاس إلى الألمنيوم (2.5%، 4%، و4.5%) وتمت دراسة تأثير هذه النسب على الخواص الميكانيكية للسبائك. تم استخدام جهاز نووب لقياس القساوة بعد إجراء المعالجة الحرارية التي تضمنت تسخين السبائك إلى درجات حرارة معينة ثم تبريدها بسرعة. أظهرت النتائج أن زيادة نسبة النحاس تؤدي إلى زيادة القساوة، حيث كانت أعلى قساوة للسبيكة بنسبة 4% نحاس بعد معالجتها لمدة 12 ساعة. تم تحليل النتائج باستخدام مخططات توازن الألمنيوم مع النحاس وبيان تأثير زمن المعالجة الحرارية على القساوة. توصلت الدراسة إلى أن لكل نسبة وزنية من النحاس منحنى مختلف للوصول إلى أفضل خصائص ميكانيكية، مما يتيح استخدام هذه السبائك في تطبيقات صناعية متعددة.
Critical review
دراسة نقدية: تعتبر هذه الدراسة قيمة من حيث تقديمها لتحليل شامل لتأثير المعالجة الحرارية على سبائك الألمنيوم-نحاس. ومع ذلك، يمكن توجيه بعض النقد البناء لتحسين البحث في المستقبل. أولاً، كان من الممكن تضمين تفاصيل أكثر حول تأثير العناصر الأخرى الموجودة في السبائك مثل المغنيسيوم والسيليكون على الخواص الميكانيكية. ثانياً، كان من المفيد إجراء تجارب إضافية على نسب نحاس مختلفة لتحديد النسبة المثلى بشكل أكثر دقة. وأخيراً، كان من الممكن استخدام تقنيات تحليلية أخرى مثل التحليل المجهري لدراسة البنية الداخلية للسبائك بشكل أكثر تفصيلاً.
Questions related to the research
-
ما هي النسب المختلفة من النحاس التي تمت دراستها في هذه الورقة؟
تمت دراسة نسب مختلفة من النحاس وهي 2.5%، 4%، و4.5%.
-
ما هو الهدف الرئيسي من هذه الدراسة؟
الهدف الرئيسي هو دراسة تأثير بارامترات المعالجة الحرارية والنسب المختلفة من النحاس على الخواص الميكانيكية لسبائك الألمنيوم-نحاس.
-
ما هي أعلى قساوة تم الحصول عليها في الدراسة؟
أعلى قساوة تم الحصول عليها كانت للسبيكة بنسبة 4% نحاس بعد معالجتها حرارياً لمدة 12 ساعة.
-
ما هي العمليات الرئيسية للمعالجة التكريمية للألمنيوم التي تمت دراستها؟
العمليات الرئيسية تشمل إذابة النحاس في الألمنيوم، التبريد السريع، والتعتيق الطبيعي أو التصلد القسري.
References used
Burg,T., Crosky, A. (2001). School of Material Science and Engineering University of New South Wales
Huang, R. (2003). Web site. Dept of Aerospace Engineering and Engineering Mechanics, The University of Texas at Austin Fall
Lecture7-8. (2003). Heat treatable aluminum alloys. Engineering Mechanics The University of Texas at Austin Fall
rate research
Read More
In this research, specimens of aluminum alloy 6061 were
received, and chemical composition was investigated. After
that solution heat treatment was applied on it at 530°C, a
section of these specimens was quenched in water and anther
quenched in
oil, and two sections were aged at 160°C for
times (1,3,5 h), and thus obtained six samples differ in
condition of heat treatment in addition to as received
specimen.
In this research the effect of Nickel addition by various
percentages on the mechanical properties of
Aluminum-Copper alloy was studied. After
adding Nickel the alloys was artificially aged for different
times, and the effect of Nickel on
the re
sponse of alloy to precipitation hardening was studied.
Where the effect of Nickel on the microscope structure was
studied, and on the mechanical properties as hardness, tensile
strength, yield strength and elongation. The results showed that
the increase of Nickel improve this properties, where the highest
values were obtained when the Nickel's percentage was 5% Wt.
In this issue, the effect of gas heat treatment ambient at the temperature of 950C
for 8hours using the gases NH3 or CH4 and using the gases NH3 and CH4 for
(4+4)hours of the distribution of the doping elements on Titanium alloys BT9 was
studied.
Oxide formation at the different treatment ambient as a reason of gas-phase
oxygen distribution to high depths in the samples was discovered.
The effect of artificial aging on the revolution of mechanical
properties of aluminum alloy 6063-T5 has been studied. Samples of
aluminum profiles which are formed by extrusion process have
chosen, then studied the effect of artificial aging on th
e hardness
and mechanical properties by applied two aging stages and many
stages comparing to the traditional way which be done in one stage.
In this work, Ck85 carbon steel was subjected to cyclic heat
treatment.
Process that consisted of cyclic short-duration (3.4 minutes)
holding at 800 C (above Ac3 temperature) followed by forced air
cooling. After 8 cycles (about a total 1 hour du
ration of heating and cooling cyclic), the microstructure mostly contained fine ferrite
grains and spheroidzed cementite. This microstructure possessed
an excellent combination of strength and ductility. The disintegration of lamellar pearlite through dissolution of cementite
at boundaries lamellar during short-duration holding above Ac3
temperature, and the generation of lamellar defects during nonequilibrium forced air cooling were the main reasons of
accelerated spheroidization. The strength initially increased mainly
due to the presence of finer microconstituents (ferrite and pearlite)
and then marginally decreased with the elimination of lamellar
pearlite and appearance of spheroid cementite in the microstructure.