Effect of Multiple usage and surface coarseness of diamond burs on Marginal Microleakage of Resin Composite Restorations (An In- vitro study)

تأثير الاستخدام المتعدد للسنابل الماسية و خشونة سطحها على التسرب الحفافي لترميمات الراتنج المركب (دراسة مخبرية)

936   0   3   0 ( 0 )
 Publication date 2016
and research's language is العربية
 Created by Shamra Editor




Ask ChatGPT about the research

Aim: to compare the effect of multiple usage and surface coarseness of diamond burs on marginal microleakage of cervical resin composite restorations. Materials and methods: sixty extracted premolars without caries were chosen. The sample was randomly divided into three groups: n1=n2=n3=20. Group(1): class v cavities were prepared using super coarse diamond burs, group(2): prepared by coarse diamond burs, whereas group)3(: prepared by medium coarse diamond burs. All cavities were restored by resin composite, then The teeth were thermocycled and immersedIn5%solution of methylene blue dye for 12hours.Then the teeth were sectioned vertically, Dye penetration was evaluated using a 10X stereomicroscope at the occlusal and gingival margins. Data were collected and statistical analysis was conducted. Results: The results showed that the multiple use of super coarse diamond burs caused no significantly statistically affect on occlusal and gingival microleakage (P>0.05). However, the multiple use of coarse and medium diamond burs caused significantly statistically affect on gingival marginal microleakage (P<0.05).


Artificial intelligence review:
Research summary
تهدف هذه الدراسة إلى مقارنة تأثير الاستخدام المتعدد للسنابل الماسية ودرجة خشونتها على التسرب الحفافي لترميمات الراتنج المركب العنقية. تم استخدام 60 ضاحكًا بشريًا مقسمة إلى ثلاث مجموعات، حيث تم تحضير حفر الصنف الخامس باستخدام سنابل ماسية عالية الخشونة، خشنة، ومتوسطة الخشونة. بعد الترميم، خضعت الأسنان لدورات حرارية وتم غمرها في محلول أزرق الميتيلين لتقييم التسرب الحفافي. أظهرت النتائج أن الاستخدام المتعدد للسنابل الماسية عالية الخشونة لم يؤثر بشكل كبير على التسرب الحفافي، بينما أثر الاستخدام المتعدد للسنابل الخشنة ومتوسطة الخشونة على التسرب الحفافي اللثوي دون الإطباقي. توصلت الدراسة إلى أن درجة خشونة السنبلة لا تؤثر بشكل كبير على التسرب الحفافي.
Questions related to the research
  1. ما هو الهدف الرئيسي من هذه الدراسة؟

    تهدف الدراسة إلى مقارنة تأثير الاستخدام المتعدد للسنابل الماسية ودرجة خشونتها على التسرب الحفافي لترميمات الراتنج المركب العنقية.

  2. ما هي المواد والأساليب المستخدمة في الدراسة؟

    تم استخدام 60 ضاحكًا بشريًا مقسمة إلى ثلاث مجموعات، حيث تم تحضير حفر الصنف الخامس باستخدام سنابل ماسية عالية الخشونة، خشنة، ومتوسطة الخشونة. بعد الترميم، خضعت الأسنان لدورات حرارية وتم غمرها في محلول أزرق الميتيلين لتقييم التسرب الحفافي.

  3. ما هي النتائج الرئيسية التي توصلت إليها الدراسة؟

    أظهرت النتائج أن الاستخدام المتعدد للسنابل الماسية عالية الخشونة لم يؤثر بشكل كبير على التسرب الحفافي، بينما أثر الاستخدام المتعدد للسنابل الخشنة ومتوسطة الخشونة على التسرب الحفافي اللثوي دون الإطباقي.

  4. ما هي التوصيات التي قدمتها الدراسة؟

    أوصت الدراسة بإجراء دراسات إضافية لتحديد تأثير استخدام السنبلة على البنية المجهرية للنسج السنية، ودراسة التغيرات الحاصلة للسنابل الماسية عقب التحضير، وإجراء دراسة استقصائية بين أطباء الأسنان حول طرق استخدامهم للسنابل الماسية.


References used
GARG N, GARG A. Text book of Operative Dentistry, 1st edition, Jaypee Brothers Medical Publishers (P)Ltd. 2010; 314
A. ABDUL AZIZ, N.H. ABU KASIM, C. RAMASINDARUM, M.Y.P. MOHAMAD YUSOF M.PAIIZI, R. AHMAD. Wear of rotary instruments: A pilot study. Annal Dent Univ Malaya 2011; 18: 1–7
MOWERY AS JR, PARKER M, DAVIS EL. Dentin bonding: the effect of surface roughness on shear bond strength. Oper Dent 1987 Summer;12(3):91
rate research

Read More

Regarding the sealing ability of restorative dental materials, this study was done to assess the microleakage of class V cavities restored with a new self-adhesive flowable composite resin and compare to different flowable materials.
The aim of this study is to evaluate the microleakage resultant from; Silorane resin composite restorations in primary teeth Prepared Using Burs And Er:YAG Laser with or without using additional etching.
The aims of this study were to evaluate the microleakage in the Class II Cavities Restored with methacrylate resin composite (Tetric Ceram HB) or silorane resin composite (P90 Filtek) that had been stored in different situations and temperatures. Mat erials and Methods: thirty six intact human upper first premolars were employed. Two Class II cavities with specific dimensions had prepared on each tooth mesially and distally. Teeth were Restored by Methacrylate Resin (HB IVOCLAR), Silorane Resin (P90), Under three different conditions: Group (A): application of composite and Adhesive System at room temperature (24°C), Group (B): application of composite and Adhesive System, immediately after removal from refrigerator temperature (4°C), Group (C): application of composite and Adhesive System, 30 minutes after removal from the refrigerator at room temperature (24°C).Results: This study observed a statistically significant increase in microleakage when applying each of methacrylate composite (HB IVOCLAR) and silorane composite (P90) immediately after removal from refrigerator temperature (4°C) Compared when applied at room temperature (24°C) and when applied 30 minutes after removing from refrigerator temperature, no significant differences were found between silorane composite (P90) and Methacrylate composite (Tetric HB) in microleakage when comparing the two types of resin in the three ways used in storing both resins.
Resin based composite considers substantially as a restorative material in clinic. Dentists concern in placement resin composite restorations with Long term survival. Materials and Methods: 20 Non carious human third molars, class I cavity was pr epared in every molar, restored with methacrylate resin composite Tetric EvoCeram. The restored teeth were subjected to thermocycles. Specimen was randomly divided into two groups : the first group 10 restorations, were repaired by Cojet® (3M ESPE, Germany) and restored by Filtek™ P90, the second group 10 restorations also repaired by Cojet ® but restored by Filtek™ Z350 XT. After that all teeth were subjected to thermocycles again, later immersed in 0.5% basic fuchsin solution for 1 s. The teeth were transversely sectioned and observed under a stereomicroscope. The degree of dye penetration was recorded and analyzed. Results: No statistically significant differences in microleakage were observed between two groups either with low shrinkage Silorane resin composite or methacrylate resin composite
comments
Fetching comments Fetching comments
Sign in to be able to follow your search criteria
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا