Spectral Properties of Tinged Glasses with Silver Bromide by Porous Glasses Method

الخصائص الطيفية لزجاج مشوب ببروميد الفضة بطريقة الزجاج المسامي

1116   0   79   0 ( 0 )
 Publication date 2017
and research's language is العربية
 Created by Shamra Editor




Ask ChatGPT about the research

Porous glasses were produced using sheet glass cullet with added magnesium carbonate MgCO3 as foams agents .The structure of glasses tinged with silver bromide by porous glasses, was studied by UV–VIS spectroscopy,transmission of light and X-ray diffraction XRD techniques. glasses plates were obtained by impregnation of porous glasses at first with AgNO3 aqueous solution , next in the KBr aqueous solution. Then the samples was sintered at temperatures 950°C up to closing of the pores. The results of spectroscopy study have shown that the glasses tinged plates, according to XRD data, the glasses tinged contain the AgBr phase.


Artificial intelligence review:
Research summary
تتناول هذه الدراسة الخصائص الطيفية للزجاج المشوب ببروميد الفضة باستخدام طريقة الزجاج المسامي. تم تحضير الزجاج المسامي باستخدام نفايات زجاجية مضافًا إليها كربونات المغنيزيوم كعامل مولد لطور غازي. بعد ذلك، تم غمر العينات بمحلول نترات الفضة ثم بمحلول بروميد البوتاسيوم، وتم تسخينها إلى درجة حرارة 950°C لإغلاق المسام. أظهرت النتائج الطيفية باستخدام تقنيات الأشعة فوق البنفسجية والمرئية (UV-VIS) وتقنية انعراج الأشعة السينية (XRD) أن الزجاج المشوب يحتوي على طور بروميد الفضة (AgBr). تم دراسة نفوذية العينات الضوئية وأظهرت النتائج أن الزجاج المشوب ببروميد الفضة يقلل من نفوذية الضوء مقارنة بالزجاج غير المشوب، مما يجعله مناسبًا للاستخدام في تطبيقات البصريات والتحكم في شدة الضوء النافذ.
Critical review
دراسة نقدية: تعتبر هذه الدراسة مهمة في مجال تحسين خصائص الزجاج الضوئية باستخدام مواد مشوبة مثل بروميد الفضة. ومع ذلك، يمكن توجيه بعض الانتقادات البناءة للدراسة. أولاً، لم يتم التطرق بشكل كافٍ إلى تأثيرات تركيزات مختلفة من بروميد الفضة على الخصائص الطيفية للزجاج، مما قد يفتح المجال لمزيد من الدراسات المستقبلية. ثانيًا، لم يتم مناقشة تأثيرات العوامل البيئية مثل الرطوبة ودرجة الحرارة على استقرار الزجاج المشوب ببروميد الفضة. أخيرًا، كان من الممكن تحسين الدراسة بتقديم مقارنة مع مواد مشوبة أخرى لمعرفة مدى فعالية بروميد الفضة مقارنة بمواد أخرى.
Questions related to the research
  1. ما هي المواد المستخدمة في تحضير الزجاج المسامي في هذه الدراسة؟

    تم استخدام نفايات زجاجية مضافًا إليها كربونات المغنيزيوم كعامل مولد لطور غازي لتحضير الزجاج المسامي.

  2. ما هي التقنية المستخدمة للتأكد من وجود بروميد الفضة في الزجاج المشوب؟

    تم استخدام تقنية انعراج الأشعة السينية (XRD) للتأكد من وجود بروميد الفضة في الزجاج المشوب.

  3. ما هو الهدف الرئيسي من هذه الدراسة؟

    الهدف الرئيسي من الدراسة هو تحضير زجاج مشوب ببروميد الفضة ودراسة خصائصه الضوئية عند تعرضه لأطوال موجية مختلفة من الضوء.

  4. كيف يؤثر بروميد الفضة على نفوذية الزجاج للضوء؟

    يقلل بروميد الفضة من نفوذية الزجاج للضوء، مما يجعله مناسبًا للاستخدام في تطبيقات البصريات والتحكم في شدة الضوء النافذ.


References used
SHELBY,J,E, 1997- “Introduction to Glass Science and Technology”, RSC
ELLIOTT, S.R. 1984 -“Physics of Amorphous Materials”, Longman, London. Revised Edition, Elsevier, 416Pages
ARBAB, L.J. SHELESTAK, C.S. HARRIS, AM. 2005-Ceram. Soc. Bull. 84
rate research

Read More

We will first introduce the basic ingredient of Fourier methods in section 1, then we will do some analysis on the Fourier approximation, in the last section, we will apply the Fourier method to solve some ODEs . we will write Matlab code for num erical result .
CaMnO3 was synthesized by a Solid State method. MnO2 and CaO were used as precursors. The temperature of synthesis was 1100°C. X-ray diffraction analysis (XRD) revealed that the CaMnO3 was synthesized. XRD results showed that the prepared compound was polycrystalline and had orothohombic structure.
In this study we used electro spinning technology to obtain nonwoven webs of Nano fibers of poly vinyl alcohol and Nano particles of silver . we dissolve the polymer poly vinyl alcohol in it's solvent (water) to form a polymeric solution that we c harged it by positive charge and ejected it to leaving it on a collector that we charged it by negative charge and used a high voltage. and we mixed the polymer poly vinyl alcohol with silver nitrate with different concentrations and electro spinning the mixture to obtain Nano fibers and Nano particles of silver then we applied heat treatment for the whole samples at 155°c for 5 minutes for tow aims the first one is to make crosslinking between series of PVA and the second is for the stability of silver nanoparticles , finally we analyze samples on Scanning Electron Microscopy SEM .
Most of the previous Rhetorical Structure Theory (RST) parsing methods are based on supervised learning such as neural networks, that require an annotated corpus of sufficient size and quality. However, the RST Discourse Treebank (RST-DT), the benchm ark corpus for RST parsing in English, is small due to the costly annotation of RST trees. The lack of large annotated training data causes poor performance especially in relation labeling. Therefore, we propose a method for improving neural RST parsing models by exploiting silver data, i.e., automatically annotated data. We create large-scale silver data from an unlabeled corpus by using a state-of-the-art RST parser. To obtain high-quality silver data, we extract agreement subtrees from RST trees for documents built using the RST parsers. We then pre-train a neural RST parser with the obtained silver data and fine-tune it on the RST-DT. Experimental results show that our method achieved the best micro-F1 scores for Nuclearity and Relation at 75.0 and 63.2, respectively. Furthermore, we obtained a remarkable gain in the Relation score, 3.0 points, against the previous state-of-the-art parser.
In this paper we present the structural, optical and electrical characteristics of ZnO thin films grown for different parameters by the atomic layer deposition (ALD) method. The films were grown on glass and silicon substrates at low temperatures. We used diethyl-zinc (DEZn) and deionized water as zinc and an oxygen sources, respectively. Measurements of surface morphology, photoluminescence at room temperature (RT PL) and Hall Effect were made for ZnO layers. The films obtained at 130°C show the highest carrier concentration (1.1×1019 cm-3) and the lowest resistivity (2.84×10-2 Wcm). The films exhibit mobility up to 19.98 cm2/Vs that we associate to the technological process used.
comments
Fetching comments Fetching comments
Sign in to be able to follow your search criteria
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا