Studying the Corrosion Behavior of Plain-Carbon Steels in Water Environments

دراسة سلوك تآكل الفولاذ الكربوني في الأوساط المائية

2908   2   69   0 ( 0 )
 Publication date 2011
and research's language is العربية
 Created by Shamra Editor




Ask ChatGPT about the research

The corrosion behaviour of plain-carbon steels in water environments has been studied. In this study, a wide range of carbon steels are used in the most common corrosion environments which are salt water and drinking water. The specimens were immersed in the water media and corrosion rates evaluated, using the weight loss method. The effect of carbon content, corrosion environments and time of immersing on the specimens corrosion rates of Hypo-eutectoid plain carbon steels have been studied. The aim of this work is to study the effect of carbon content on the corrosion rate of carbon steels in different corrosion media and various time intervals. The obtained results showed that there is a clear correlation with the microstructure where higher Pearlite show higher corrosion rate, so the corrosion rate increases with the carbon content. The results also show that the corrosion rate of carbon-steel in salt water is higher than its value in drinking water. It is also found that longer exposure time, leads to a lower corrosion rate while weight loss is still increasing.


Artificial intelligence review:
Research summary
تناولت الدراسة سلوك تآكل الفولاذ الكربوني في الأوساط المائية المختلفة مثل الماء المالح وماء الشرب. استخدمت الدراسة مجموعة من أنواع الفولاذ الكربوني ذات نسب كربون مختلفة، وتم غمر العينات في الأوساط المائية لفترات زمنية مختلفة (30، 45، 60 يوماً). تم حساب معدلات التآكل باستخدام طريقة فقدان الوزن. أظهرت النتائج أن معدل التآكل يزداد مع زيادة نسبة الكربون في الفولاذ، وأن الفولاذ الكربوني يتآكل بشكل أسرع في الماء المالح مقارنة بماء الشرب. كما تبين أن زيادة زمن التعرض لوسط التآكل يقلل من معدل التآكل، وذلك بسبب تشكل طبقات من مخلفات التآكل التي تعيق استمرار التفاعل الكهروكيميائي. تم تحليل النتائج بيانياً وأظهرت العلاقة بين نسبة الكربون ومعدل التآكل، وكذلك تأثير نوع الوسط المائي وزمن التعرض على معدلات التآكل.
Critical review
دراسة نقدية: تعتبر الدراسة شاملة ومفصلة في تحليل سلوك تآكل الفولاذ الكربوني في الأوساط المائية المختلفة. ومع ذلك، يمكن أن تكون هناك بعض النقاط التي تحتاج إلى مزيد من التوضيح. على سبيل المثال، لم يتم التطرق بشكل كافٍ إلى تأثير العوامل البيئية الأخرى مثل درجة الحرارة والرطوبة على معدلات التآكل. كما أن الدراسة اعتمدت بشكل رئيسي على طريقة فقدان الوزن لحساب معدلات التآكل، وكان من الممكن استخدام تقنيات أخرى مثل التحليل الطيفي أو الفحص المجهري الإلكتروني للحصول على نتائج أكثر دقة. بالإضافة إلى ذلك، لم يتم مناقشة الحلول الممكنة لتقليل معدلات التآكل أو تحسين مقاومة الفولاذ الكربوني للتآكل بشكل كافٍ.
Questions related to the research
  1. ما هو الهدف الرئيسي من الدراسة؟

    الهدف الرئيسي من الدراسة هو دراسة تأثير محتوى الكربون في معدلات التآكل للفولاذ الكربوني في أوساط تآكل مختلفة وبفترات زمنية متغيرة.

  2. ما هي الأوساط المائية التي تم استخدامها في الدراسة؟

    تم استخدام الماء المالح وماء الشرب كأوساط مائية في الدراسة.

  3. كيف تم حساب معدلات التآكل في الدراسة؟

    تم حساب معدلات التآكل باستخدام طريقة فقدان الوزن، حيث تم وزن العينات قبل وبعد غمرها في الأوساط المائية لفترات زمنية محددة.

  4. ما هي النتائج الرئيسية التي توصلت إليها الدراسة؟

    أظهرت النتائج أن معدل التآكل يزداد مع زيادة نسبة الكربون في الفولاذ، وأن الفولاذ الكربوني يتآكل بشكل أسرع في الماء المالح مقارنة بماء الشرب. كما تبين أن زيادة زمن التعرض لوسط التآكل يقلل من معدل التآكل.


References used
ASM Handbook Volume13A: Corrosion: Fundamentals, Testing, and Protection ASM International, 2003
Mars G. Fontana, “Corrosion Engineering” Third Edition, 2006
K.R. Trethewey & J. Chaberlain, “Corrosion for Science and Engineering” 2nd ed., printed in Singapore, 1996
rate research

Read More

This research showed the great importance for following studies of the effect of polluted phosphoric acid, produced in General Fertilizer Company, on the high corrosion resisting alloys, to reach suitable alloys for equipments and machines used for its production, because of its high corrosion rates that create many corrosion problems in these equipments and machines.
This paper provides a mechanism to study aluminum diffusion microstructure, phase structure and different properties of the aluminized layer in carbon steel. The results of aluminized treatment in saturated medium lead to the formation of diffusion layer coating that contains iron aluminide and a- solid solution of aluminum in the unit cell of iron. The effect of aluminizing process parameters on the aluminizing layer, especially the effect of temperature and time, has been shown to increase the depth of the aluminized layer when temperature and time increase, but the effect of temperature is greater than time.
Welded joints corrosion phenomena for some kinds of stainless steels and nickel alloy was studied in polluted phosphoric acid 37.7%H3Po4 using electrochemical techniques like Tafel polarization. Corrosion rate of base metal and weld metal had calcu lated & compared among these alloys. Laboratory Test results showed the change in both corrosion rate and corrosion current densities (Icorr) for tested alloys, and there is a clear difference between base metal and weld metal in most of tested alloys , which lead to high corrosion rates of welded joint, and change in its properties then gets out of service in some service conditions. The stainless steel 904L has low corrosion rates and low difference in corrosion rates between base metal and weld metal, so it may be the most suitable alloy, among all the studied alloys, for exploitation in polluted phosphoric acid 37.7%H3Po4 produced at the General Fertilizer Company in Homs city.
In this work, Ck85 carbon steel was subjected to cyclic heat treatment. Process that consisted of cyclic short-duration (3.4 minutes) holding at 800 C (above Ac3 temperature) followed by forced air cooling. After 8 cycles (about a total 1 hour du ration of heating and cooling cyclic), the microstructure mostly contained fine ferrite grains and spheroidzed cementite. This microstructure possessed an excellent combination of strength and ductility. The disintegration of lamellar pearlite through dissolution of cementite at boundaries lamellar during short-duration holding above Ac3 temperature, and the generation of lamellar defects during nonequilibrium forced air cooling were the main reasons of accelerated spheroidization. The strength initially increased mainly due to the presence of finer microconstituents (ferrite and pearlite) and then marginally decreased with the elimination of lamellar pearlite and appearance of spheroid cementite in the microstructure.
We studying in this research the reaction with Zinc sulphate in an aqueous solution by physical - chemical method in presence of Succinic Acid , and determined compounds which are formed in this solution and we calculated of it formation the const ants. After we used these electrolytes in plating by Zinc , that is by electro precipitation of this metal on the solid electrodes (steel, copper) so that we definite the best of these electrolytes for galvany and the set necessary conditions for its use.
comments
Fetching comments Fetching comments
Sign in to be able to follow your search criteria
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا