The thickness of the diffusion layers was studied, along with the phases and the microstructure and
composition, across the depth in diffusion zone. The obtained results proved the effect of nitriding
system in the growth of the diffusion layers on
surface of double composite martensitic - austenitic alloy
steel.
Analysis of mechanical and tribological characteristics of treated double composite steel under dry
friction was also studied. It was found that diffusion treatment had a significant influence on work
capacity of tested alloy. Stability of alloy after nitriding was (2.5-4) times higher in magnitude
compared to untreated alloy.
فولاذ سبائكي ذو بنية مركبة
تقسية و إرجاع
نتردة غازية
بنية و تركيب طوري
طبقات انتشارية
قساوة سطحية
خواص ميكانيكية و تريبولوجية
Double composite alloy steel
hardening and tempering
gas nitriding
diffusion layers
microstructure and phase composition
surface hardness
mechanical and tribological properties
المزيد..
The influence of thermomechanical treatments on the microstructural properties of stainless steel D9 alloy
steel was studied.
This paper provides a mechanism to study aluminum diffusion microstructure, phase
structure and different properties of the aluminized layer in carbon steel.
The results of aluminized treatment in saturated medium lead to the formation of diffusion
layer coating that contains iron aluminide and a- solid solution of aluminum in the unit cell of
iron.
The effect of aluminizing process parameters on the aluminizing layer, especially the
effect of temperature and time, has been shown to increase the depth of the aluminized layer
when temperature and time increase, but the effect of temperature is greater than time.