Recently worldwide researches have been devoted to the use of steel fibers recovered from used tires in concrete. In Syria the amount of recovered steel from used tires is estimated about 6000 tons/year.
For this purpose a bead wire having a diamete
r of 0.8 mm from burnt tires was extracted and used. Three mixes with cement content 300- 350 -400kg/m3 were produced incorporating three different volumes of fiber 0.5%, 1.0%, and 1.5% and three different length 30-40-60 mm. The concrete obtained by adding these fibers evidenced a satisfactory improvement of the fragile matrix mostly in terms of toughness and post cracking behavior On the other hand it was improvements in compressive strength by steel fiber inclusion the interesting results confirm the promising application of concrete reinforced with steel fibers extracted from used tires in aircraft pavement hydraulic structures and ground slab in fabrics.