In this research, specimens of aluminum alloy 6061 were
received, and chemical composition was investigated. After
that solution heat treatment was applied on it at 530°C, a
section of these specimens was quenched in water and anther
quenched in
oil, and two sections were aged at 160°C for
times (1,3,5 h), and thus obtained six samples differ in
condition of heat treatment in addition to as received
specimen.
This study aimed to compare the effects of different enamel
etching techniques for bracket bonding strength. The sample
consisted of eighty human premolars were randomly divided into
four equal groups. The enamel surfaces of the teeth were etched
with 35% orthophosphoric acid in Group 1 , air abraded with
50 μm aluminum oxide prior to acid etching in Group 2, Trans
bond Plus Self-etching Primer (TPSEP) in Group 3 , Er: YAG
laser in Group 4. After enamel etching procedures, brackets were
bonded with Trans bond XT , then shear bonding test was
performed using a testing machine (Tinius Olsen).
The aim of this research to study the Abrasion on carbonate rocks which comes from specific mines in Syria, and possibility finding correlation between Abrasion test(L.A) and some physical properties of carbonate rocks .
Results or Finding:
- Most
of studied carbonate rocks are resistance(18-41%).
- There is correlations between some physical properties of carbonate rocks and Abrasion test(L.A) .
Ring-opening monomers with a reduced shrinkage stress “silorane" are being
used as matrix resins for recently introduced dental composites. Thisstudy aimed to analyzethe
mechanical behavior(Flexural StrengthFS, Abrasion Resistance AR) of the silora
ne-based composite
(Filtek P90) in comparison to two methacrylate-based composites (Tetric- Evo Ceram & packable
hybridTetric Ceram HB).