تسجيل مستخدم جديدSpin wave propagation in ferrimagnetic $Gd_{x}Co_{1-x}$
144
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Recent advances in antiferromagnetic spin dynamics using rare-earth (RE) and transition-metal (TM) ferrimagnets have attracted much interest for spintronic devices with a high speed and density. In this study, the spin wave properties in the magnetostatic backward volume mode and surface mode in RE-TM ferrimagnetic $Gd_{x}Co_{1-x}$ films with various composition x are investigated using spin wave spectroscopy. The obtained group velocity and attenuation length are well explained by the ferromagnet-based spin wave theory when the composition of $Gd_{x}Co_{1-x}$ is far from the compensation point.
قيم البحث
اقرأ أيضاً
We report the discovery of a new spin glass ground state in the transition metal monosilicides with the B20 crystallographic structure. Magnetic, transport, neutron and muon investigation of the solid solution Mn$_{1-x}$Co$_{x}$Si have revealed a new
dome in the phase diagram with evidence of antiferromagnetic interactions. For Mn rich compounds, a sharp decrease of the Curie temperature is observed upon Co doping and neutron elastic scattering shows that helimagnetic order of MnSi persists up to $x=0.05$ with a shortening of the helix period. For higher Co ($0.05<x<0.90$) concentrations, the Curie-Weiss temperature changes sign and the system enters a spin glass state upon cooling ($T_g=9$ K for $x_{Co}=0.50$), due to chemical disorder. In this doping range, a minimum appears in the resistivity, attributed to scattering of conduction electron by localized magnetic moments.
We report a systematic investigation on the magnetization relaxation properties of iron-based half-metallic Heusler alloy Fe$_{2}$Cr$_{1-x}$Co_${x}$Si (FCCS) thin films using broadband angular-resolved ferromagnetic resonance. Band structure engineer
ing through Co doping (x) demonstrated by first-principles calculations is shown to tune the intrinsic magnetic damping over an order of magnitude, namely 0.01-0.0008. Notably, the intrinsic damping constants for samples with high Co concentration are among the lowest reported for Heusler alloys and even comparable to magnetic insulator yttrium iron garnet. Furthermore, a significant reduction of both isotropic and anisotropic contributions of extrinsic damping of the FCCS alloys was found in the FCCS films with x=0.5-0.75, which is of particular importance for applications. These results demonstrate a practical recipe to tailor functional magnetization for Heusler alloy-based spintronics at room temperature
The information carrier of modern technologies is the electron charge whose transport inevitably generates Joule heating. Spin-waves, the collective precessional motion of electron spins, do not involve moving charges and thus avoid Joule heating. In
this respect, magnonic devices in which the information is carried by spin-waves attract interest for low-power computing. However implementation of magnonic devices for practical use suffers from low spin-wave signal and on/off ratio. Here we demonstrate that cubic anisotropic materials can enhance spin-wave signals by improving spin-wave amplitude as well as group velocity and attenuation length. Furthermore, cubic anisotropic material shows an enhanced on/off ratio through a laterally localized edge mode, which closely mimics the gate-controlled conducting channel in traditional field-effect transistors. These attractive features of cubic anisotropic materials will invigorate magnonics research towards wave-based functional devices.
In this article we study the effects of a partial substitution of Ba with the smaller cation Ca in the layered cobaltites YBaCo_2O_{5+delta} for delta approx 0.5. Neutron thermodiffractograms are reported for the compounds YBa_{0.95}Ca_{0.05}Co_2O_{5
.5} (x_{Ca}=0.05) and YBa_{0.90}Ca_{0.10}Co_2O_{5.5} (x_{Ca}=0.10) in the temperature range 20 K leq T leq 300 K, as well as high resolution neutron diffraction experiments at selected temperatures for the samples x_{Ca}=0.05, x_{Ca}=0.10 and the parent compound x_{Ca}=0. We have found the magnetic properties to be strongly affected by the cationic substitution. Although the 122 perovskite structure seems unaffected by Ca addition, the magnetic arrangements of Co ions are drastically modified: the antiferromagnetic (AFM) long-range order is destroyed, and a ferrimagnetic phase with spin state order is stabilized below T sim 290 K. For the sample with x_{Ca}=0.05 a fraction of AFM phase coexists with the ferrimagnetic one below T sim 190 K, whereas for x_{Ca}=0.10 the AFM order is completely lost. The systematic refinement of the whole series has allowed for a better understanding of the observed low-temperature diffraction patterns of the parent compound, YBaCo_2O_{5.5}, which had not yet been clarified. A two-phase scenario is proposed for the x_{Ca}=0 compound which is compatible with the phase coexistence observed in the x_{Ca}=0.05 sample.
$Ni_{50-x}Co_{x}Mn_{40}Sn_{10}$ shape memory alloys in the approximate range $5 le x le 10$ display desirable properties for applications as well as intriguing magnetism. These off-stoichiometric Heusler alloys undergo a martensitic phase transformat
ion at a temperature $T_{M}$ of 300 - 400 K, from ferromagnetic (F) to nonferromagnetic, with unusually low thermal hysteresis and a large change in magnetization. The low temperature magnetic structures in the martensitic phase of such alloys, which are distinctly inhomogeneous, are of great interest but are not well understood. Our present use of spin echo NMR, in the large hyperfine fields at $^{55}Mn$ sites, provides compelling evidence that nanoscale magnetic phase separation into F and antiferromagnetic (AF) regions occurs below $T_{M}$ in alloys with x in the range 0 to 7. At finite Co substitution the F regions are found to be of two distinct types, corresponding to high and low local concentrations of Co on Ni sites. Estimates of the size distributions of both the F and AF nanoregions have been made. At x = 7 the AF component is not long-range ordered, even below 4 K, and is quite different to the AF component found at x = 0; by x = 14 the F phase is completely dominant. Of particular interest, we find, for x = 7, that field cooling leads to dramatic changes in the AF regions. These findings provide insight into the origins of magnetic phase separation and superparamagnetism in these complex alloys, particularly their intrinsic exchange bias, which is of considerable current interest.