Low-temperature, high-field (H[-110] <= 7.5 T), neutron diffraction experiments on single-crystal Ce0.70Pr0.30B6 are reported. Two successive incommensurate phases are found to exist in zero field. The appearance, for H >= 4.6 T at T = 2 K, of an antiferromagnetic structure, k{AF} = (1/2, 1/2, 1/2), most likely due to an underlying antiferroquadrupolar order, is discussed in connection with recent x-ray diffraction experiments.
قيم البحث
اقرأ أيضاً
Magnetic structure of single crystalline TmB4 has been studied by magnetization, magnetoresistivity and specific heat measurements. A complex phase diagram with different antiferromagnetic (AF) phases was observed below TN1 = 11.7 K. Besides the plat
eau at half-saturated magnetization (1/2 MS), also plateaus at 1/9, 1/8 and 1/7 of MS were observed as function of applied magnetic field B//c. From additional neutron scattering experiments on TmB4, we suppose that those plateaus arise from a stripe structure which appears to be coherent domain boundaries between AF ordered blocks of 7 or 9 lattice constants. The received results suggest that the frustration among the Tm3+ magnetic ions, which maps to a geometrically frustrated Shastry-Sutherland lattice lead to strong competition between AF and ferromagnetic (FM) order. Thus, stripe structures in intermediate field appear to be the best way to minimize the magnetostatic energy against other magnetic interactions between the Tm ions combined with very strong Ising anisotropy.
The magnetic, thermal and transport properties as well as electronic band structure of MnPtSi are reported. MnPtSi is a metal that undergoes a ferromagnetic transition at $T_{mathrm{C}}=340$(1) K and a spin-reorientation transition at $T_{mathrm{N}}=
326$(1) K to an antiferromagnetic phase. First-principles electronic structure calculations indicate a not-fully polarized spin state of Mn in a $d^5$ electron configuration with $J=S=3$/2, in agreement with the saturation magnetization of 3~$mu_{mathrm{B}}$ in the ordered state and the observed paramagnetic effective moment. A sizeable anomalous Hall effect in the antiferromagnetic phase alongside the computational study suggests that the antiferromagnetic structure is non-collinear. Based on thermodynamic and resistivity data we construct a magnetic phase diagram. Magnetization curves $M$($H$) at low temperatures reveal a metamagnetic transition of spin-flop type. The spin-flopped phase terminates at a critical point with $T_{mathrm{cr}}approx 300$ K and $H_{mathrm{cr}}approx 10$ kOe, near which a peak of the magnetocaloric entropy change is observed. Using Arrott plot analysis and magnetoresistivity data we argue that the metamagnetic transition is of a first-order type, whereas the strong field dependence of $T_{mathrm{N}}$ and the linear relationship of the $T_{mathrm{N}}$ with $M^2$ hint at its magnetoelastic nature.
A new U-based compound of the U2Rh2Pb, a new compound of the U2T2X series was prepared in a single-crystal form. Its structure was determined as belonging to the tetragonal Mo2FeB2 structure type with the shortest U-U spacing along the c. U2Rh2Pb und
ergoes an antiferromagnetic transition at TN of 20 K and exhibits an enhanced Sommerfeld coefficient 150 mJ/molK2. In contrast to the two rhodium analogues U2Rh2In and U2Rh2Sn, the easy-magnetization direction is the c with rather low value of the critical field 4.3 T of the metamagnetic transition of a spin-flip type. The observed dependences of TN and Hc on temperature and magnetic field have been used for constructing a magnetic phase diagram. The experimental observations are mostly supported by first-principles calculations.
CeAu2Ge2 single crystals (tetragonal ThCr2Si2 structure) have been grown in Au-Ge flux (AGF) as well as in Sn flux (SF). X-ray powder-diffraction and EDX measurements indicate that in the latter case Sn atoms from the flux are incorporated in the sam
ples, leading to a decrease of the lattice constants by ~ 0.3% compared to AGF samples. For both types of samples, a strong anisotropy of the magnetization M for the magnetic field B parallel and perpendicular to the c direction is observed with M||/M^{bot} ~ 6 - 7 in low fields just above 10 K. This anisotropy is preserved to high fields and temperatures and can be quantitatively explained by crystal electric field effects. Antiferromagnetic ordering sets in around 10 K as previously found for polycrystalline samples. From the magnetization data of our single crystals we obtain the phase diagrams for the AGF and SF samples. The magnetic properties depend strongly on the flux employed. While the AGF samples exhibit a complex behavior indicative of several magnetic transitions, the SF samples adopt a simpler antiferromagnetic structure with a single spin-flop transition. This effect of a more ordered state induced by disorder in form of Sn impurities is qualitatively explained within the ANNNI model, which assumes ferromagnetic and antiferromagnetic interactions in agreement with the magnetic structure previously inferred from neutron-scattering experiments on polycrystalline CeAu2Ge2 by Loidl et al. [Phys. Rev. B 46, 9341, (1992)].
We have measured temperature and magnetic field dependences of the thermal conductivity along the c-axis, kc, and that along the [110] direction, k110, of CuB2O4 single crystals in zero field and magnetic fields along the c-axis and along the [110] d
irection. It has been found that the thermal conductivity is nearly isotropic and very large in zero field and that the thermal conductivity due to phonons is dominant in CuB2O4. The temperature and field dependences of kc and k110 have markedly changed at phase boundaries in the magnetic phase diagram, which has been understood to be due to the change of the mean free path of phonons caused by the change of the phonon-spin scattering rate at the phase boundaries. It has been concluded that thermal conductivity measurements are very effective for detecting magnetic phase boundaries.