We experimentally investigated the magnetic properties of NiCo$_2$O$_4$ epitaxial films known to be conductive oxides with perpendicular magnetic anisotropy (PMA) at room temperature. Both magneto-torque and magnetization measurements at various temperatures provide clear experimental evidence of the spin reorientation transition at which the MA changes from PMA to easy-cone magnetic anisotropy (ECMA) at a certain temperature ($T_{rm{SR}}$). ECMA was commonly observed in films grown by pulsed laser deposition and reactive radio frequency magnetron sputtering, although $T_{mathrm{SR}}$ is dependent on the growth method as well as the conditions. The cone angles measured from the $c$-axis increased successively at $T_{mathrm{SR}}$ and approached a maximum of 45-50 degrees at the lowest measurement temperature of 5 K. Calculation with the cluster model suggests that the Ni$^{3+}$ ions occupying the $T_d$ site could be the origin of the ECMA. Both the magnetic properties and the results of the calculation based on the cluster model indicate that the ECMA is attributable to the cation anti-site distribution of Ni$^{3+}$, which is possibly formed during the growth process of the thin films.
قيم البحث
اقرأ أيضاً
AB$_2$O$_4$ normal spinels with a magnetic B site can host a variety of magnetic and orbital frustrations leading to spin-liquid phases and field-induced phase transitions. Here we report the first epitaxial growth of (111)-oriented MgCr$_2$O$_4$ thi
n films. By characterizing the structural and electronic properties of films grown along (001) and (111) directions, the influence of growth orientation has been studied. Despite distinctly different growth modes observed during deposition, the comprehensive characterization reveals no measurable disorder in the cation distribution nor multivalency issue for Cr ions in either orientation. Contrary to a naive expectation, the (111) stabilized films exhibit a smoother surface and a higher degree of crystallinity than (001)-oriented films. The preference in growth orientation is explained within the framework of heteroepitaxial stabilization in connection to a significantly lower (111) surface energy. These findings open broad opportunities in the fabrication of 2D kagome-triangular heterostructures with emergent magnetic behavior inaccessible in bulk crystals.
GeCu2O4 exhibits a tetragonal spinel structure due to the strong Jahn-Teller distortion associated with Cu2+ ions. We show that its magnetic structure can be described as slabs composed of a pair of layers with orthogonally oriented spin 1/2 Cu chain
s in the basal ab plane. The spins between the two layers within a slab are collinearly aligned while the spin directions of neighboring slabs are perpendicular to each other. Interestingly, we find that spins along each chain form an unusual up-up-down-down (UUDD) pattern, suggesting a non-negligible nearest-neighbor biquadratic exchange interaction in the effective classical spin Hamiltonian. We hypothesize that spin-orbit coupling and orbital mixing of Cu2+ ions in this system is non-negligible, which calls for future calculations using perturbation theory with extended Hilbert (spin and orbital) space and calculations based on density functional theory including spin-orbit coupling and looking at the global stability of the UUDD state.
The direct liquid injection chemical vapor deposition (DLI-CVD) technique has been used for the growth of cobalt ferrite (CFO) films on (100)-oriented MgAl$_2$O$_4$ (MAO) substrates. Smooth and highly epitaxial cobalt ferrite thin films, with the epi
taxial relationship $mathrm{MAO} (100):[001] parallel mathrm{CFO} (100):[001]$, are obtained under optimized deposition conditions. The films exhibit bulk-like structural and magnetic properties with an out-of-plane lattice constant of $8.370;mathrm{AA}$ and a saturation magnetization of $420;mathrm{kA/m}$ at room temperature. The Raman spectra of films on MgAl$_2$O$_4$ support the fact that the Fe$^{3+}$- and the Co$^{2+}$-ions are distributed in an ordered fashion on the B-site of the inverse spinel structure. The DLI-CVD technique has been extended for the growth of smooth and highly oriented cobalt ferrite thin films on a variety of other substrates, including MgO, and piezoelectric lead magnesium niobate-lead titanate and lead zinc niobate-lead titanate substrates.
We performed a Raman scattering study of thin films of LiTi$_2$O$_4$ spinel oxide superconductor. We detected four out of five Raman active modes, with frequencies in good accordance with our first-principles calculations. Three T$_{2g}$ modes show a
Fano lineshape from 5 K to 295 K, which suggests an electron-phonon coupling in LiTi$_2$O$_4$. Interestingly, the electron-phonon coupling shows an anomaly across the negative to positive magnetoresistance transition at 50 K, which may be due to the unset of other competing orders. The strength of the electron-phonon interaction estimated from the Allens formula and the observed lineshape parameters suggests that the three T$_{2g}$ modes contribute little to superconductivity.
Magnetite epitaxial thin films have been prepared by pulsed laser deposition at 340 C on MgO and Si substrates. One key result is that the thin film properties are almost identical to the properties of bulk material. For 40 - 50 nm thick films, the s
aturation magnetization and conductivity are respectively 453 emu/cm^3 and 225 1/(Ohm cm) at room temperature. The Verwey transition is at 117 K. The Hall effect indicates an electron concentration corresponding to 0.22 electrons per formula unit at room temperature. Normal and anomalous Hall effect both have a negative sign.