تسجيل مستخدم جديدSuperconducting properties of high-entropy-alloy tellurides M-Te (M: Ag, In, Cd, Sn, Sb, Pb, Bi) with a NaCl-type structure
226
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
High-entropy-alloy-type tellurides M-Te, which contain five different metals of M = Ag, In, Cd, Sn, Sb, Pb, and Bi, were synthesized using high pressure synthesis. Structural characterization revealed that all the obtained samples have a cubic NaCl-type structure. Six samples, namely AgCdSnSbPbTe5, AgInSnSbPbTe5, AgCdInSnSbTe5, AgCdSnPbBiTe5, AgCdInPbBiTe5, and AgCdInSnBiTe5 showed superconductivity. The highest transition temperature (Tc) among those samples was 1.4 K for AgInSnSbPbTe5. A sample of AgCdInSbPbTe5 showed a semiconductor-like transport behavior. From the relationship between Tc and lattice constant, it was found that a higher Tc is observed for a telluride with a larger lattice constant.
قيم البحث
اقرأ أيضاً
Research on high-entropy-alloy (HEA) superconductors is a growing field in material science. In this study, we explored new HEA-type superconductors and discovered a CuAl2-type superconductor Co0.2Ni0.1Cu0.1Rh0.3Ir0.3Zr2 with a HEA-type transition me
tal site. A superconducting transition was observed at 8.0 K after electrical resistivity, magnetization, and specific heat measurements. The bulk characteristics of the superconductivity were confirmed through the specific heat measurements. The discovery of superconductivity in HEA-type Co0.2Ni0.1Cu0.1Rh0.3Ir0.3Zr2 will provide a novel pathway to explore new HEA-type superconductors and investigate the relationship between the mixing entropy and superconductivity of HEA-type compounds.
The effects of pressure on the superconducting properties of a Bi-based layered superconductor La2O2Bi3Ag0.6Sn0.4S6, which possesses a four-layer-type conducting layer, have been studied through the electrical resistance and magnetic susceptibility m
easurements. The crystal structure under pressure was examined using synchrotron X-ray diffraction at SPring-8. In the low-pressure regime, bulk superconductivity with a transition temperature Tc of ~ 4.5 K was induced by pressure, which was achieved by in-plane chemical pressure effect owing to the compression of the tetragonal structure. In the high-pressure regime above 6.4 GPa, a structural symmetry lowering was observed, and superconducting transitions with a Tc ~ 8 K were observed. Our results suggest the possible commonality on the factor essential for Tc in Bi-based superconductors with two-layer-type and four-layer-type conducting layers.
A high-entropy-alloy-type (HEA-type) superconductor is new category of highly disordered superconductors. Therefore, finding brand-new superconducting characteristics in the HEA-type superconductors would open new avenue to investigate the relationsh
ip between structural disorder and superconductivity. Here, we report on the remarkable broadening of specific heat jump near a superconducting transition tempreature (Tc) in transition-metal zirconides (TrZr2) with different mixing entropy ({Delta}Smix) at the Tr site. With increasing {Delta}Smix, the superconducting transition seen in specific heat became broader, whereas those seen in magnetization were commonly sharp. Therefore the broadening of specific heat jump would be related to the microscopic inhomogeneity of the formation of Cooper pairs behind the emergence of bulk superconductivity states.
We report on the synthesis and superconductivity of high-entropy-alloy-type (HEA-type) compounds TrZr2 (Tr = Fe, Co, Ni, Rh, Ir), in which the Tr site satisfies the criterion of HEA. Polycrystalline samples of HEA-type TrZr2 with four different compo
sitions at the Tr site were synthesized by arc melting method. The phase purity and crystal structure were examined by Rietveld refinement of X-ray diffraction profile. It has been confirmed that the obtained samples have a CuAl2-type tetragonal structure. From analyses of elemental composition and mixing entropy at the Tr site, the HEA state for the Tr site was confirmed. The physical properties of obtained samples were characterized by electrical resistivity and magnetization measurements. All the samples show bulk superconductivity with various transition temperature (Tc). The Tc varied according to the compositions and showed correlations with the lattice constant c and Tr-Zr bond lengths. Introduction of an HEA site in TrZr2 is useful to achieve systematic tuning of Tc with a wide temperature range, which would be a merit for superconductivity application.
Lead and tin chalcogenides have been studied widely due to their promising thermoelectric (TE) properties. Further enhancement in their TE efficiency has been reported upon the reduction of the dimension, which is an important feature in modern devic
e fabrications. Using density functional theory combined with the Semi-classical Boltzmann transport theory, we studied the structural, electronic and TE properties of two-dimensional (2D) MX (M = Sn, Pb; X = S, Te) monolayers. Spin-orbit coupling was found to have significant effects on their electronic structure, particularly for the heavy compounds. Structural optimization followed by phonon transport studies prevailed that the rectangular ({gamma}-) phase is energetically the most favorable for SnS and SnTe monolayers, whereas the square structure is found the most stable for PbS and PbTe monolayers. Our results are in good agreement with previous studies. These 2D materials exhibit high Seebeck coefficients and power factors along with low lattice thermal conductivities, which are essential features of good TE materials. The maximum figure of merits (ZT) of 1.04, 1.46, 1.51 and 1.94 are predicted for n-type SnS, SnTe, PBS and p-type PbTe monolayers respectively at 700 K, which are higher than their bulk ZT values. Hence, these monolayers are promising candidates for TE applications.