تسجيل مستخدم جديدLarge magnetocrystalline anisotropy in tetragonally distorted Heuslers: a systematic study
108
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
With a view to the design of hard magnets without rare earths we explore the possibility of large magnetocrystalline anisotropy energies in Heusler compounds that are unstable with respect to a tetragonal distortion. We consider the Heusler compounds Fe$_2$YZ with Y = (Ni, Co, Pt), and Co$_2$YZ with Y = (Ni, Fe, Pt) where, in both cases, Z = (Al, Ga, Ge, In, Sn). We find that for the Co$_2$NiZ, Co$_2$PtZ, and Fe$_2$PtZ families the cubic phase is always, at $T=0$, unstable with respect to a tetragonal distortion, while, in contrast, for the Fe$_2$NiZ and Fe$_2$CoZ families this is the case for only 2 compounds -- Fe$_2$CoGe and Fe$_2$CoSn. For all compounds in which a tetragonal distortion occurs we calculate the MAE finding remarkably large values for the Pt containing Heuslers, but also large values for a number of the other compounds (e.g. Co$_2$NiGa has an MAE of -2.11~MJ/m$^3$). The tendency to a tetragonal distortion we find to be strongly correlated with a high density of states at the Fermi level in the cubic phase. As a corollary to this fact we observe that upon doping compounds for which the cubic structure is stable such that the Fermi level enters a region of high DOS, a tetragonal distortion is induced and a correspondingly large value of the MAE is then observed.
قيم البحث
اقرأ أيضاً
We experimentally investigated the magnetic properties of NiCo$_2$O$_4$ epitaxial films known to be conductive oxides with perpendicular magnetic anisotropy (PMA) at room temperature. Both magneto-torque and magnetization measurements at various temp
eratures provide clear experimental evidence of the spin reorientation transition at which the MA changes from PMA to easy-cone magnetic anisotropy (ECMA) at a certain temperature ($T_{rm{SR}}$). ECMA was commonly observed in films grown by pulsed laser deposition and reactive radio frequency magnetron sputtering, although $T_{mathrm{SR}}$ is dependent on the growth method as well as the conditions. The cone angles measured from the $c$-axis increased successively at $T_{mathrm{SR}}$ and approached a maximum of 45-50 degrees at the lowest measurement temperature of 5 K. Calculation with the cluster model suggests that the Ni$^{3+}$ ions occupying the $T_d$ site could be the origin of the ECMA. Both the magnetic properties and the results of the calculation based on the cluster model indicate that the ECMA is attributable to the cation anti-site distribution of Ni$^{3+}$, which is possibly formed during the growth process of the thin films.
GeCu2O4 exhibits a tetragonal spinel structure due to the strong Jahn-Teller distortion associated with Cu2+ ions. We show that its magnetic structure can be described as slabs composed of a pair of layers with orthogonally oriented spin 1/2 Cu chain
s in the basal ab plane. The spins between the two layers within a slab are collinearly aligned while the spin directions of neighboring slabs are perpendicular to each other. Interestingly, we find that spins along each chain form an unusual up-up-down-down (UUDD) pattern, suggesting a non-negligible nearest-neighbor biquadratic exchange interaction in the effective classical spin Hamiltonian. We hypothesize that spin-orbit coupling and orbital mixing of Cu2+ ions in this system is non-negligible, which calls for future calculations using perturbation theory with extended Hilbert (spin and orbital) space and calculations based on density functional theory including spin-orbit coupling and looking at the global stability of the UUDD state.
The origin of large perpendicular magneto-crystalline anisotropy (PMCA) in Fe/MgO (001) is revealed by comparing Fe layers with and without the MgO. Although Fe-O $p$-$d$ hybridization is weakly present, it cannot be the main origin of the large PMCA
as claimed in previous study. Instead, perfect epitaxy of Fe on the MgO is more important to achieve such large PMCA. As an evidence, we show that the surface layer in a clean free-standing Fe (001) dominantly contributes to $E_{MCA}$, while in the Fe/MgO, those by the surface and the interface Fe layers contribute almost equally. The presence of MgO does not change positive contribution from $langle xz|ell_Z|yzrangle$, whereas it reduces negative contribution from $langle z^2|ell_X|yzrangle$ and $langle xy|ell_X|xz,yzrangle$.
We demonstrate that chiral skyrmionic magnetization configurations can be found as the minimum energy state in B20 thin film materials with easy-plane magnetocrystalline anisotropy with an applied magnetic field perpendicular to the film plane. Our o
bservations contradict results from prior analytical work, but are compatible with recent experimental investigations. The size of the observed skyrmions increases with the easy-plane magnetocrystalline anisotropy. We use a full micromagnetic model including demagnetization and a three-dimensional geometry to find local energy minimum (metastable) magnetization configurations using numerical damped time integration. We explore the phase space of the system and start simulations from a variety of initial magnetization configurations to present a systematic overview of anisotropy and magnetic field parameters for which skyrmions are metastable and global energy minimum (stable) states.
We have studied the Co layer thickness dependences of magnetocrystalline anisotropy (MCA), Dzyaloshinskii-Moriya interaction (DMI), and orbital moment anisotropy (OMA) in W/Co/Pt trilayers. We find the MCA favors magnetization along the film normal a
nd monotonically increases with decreasing effective magnetic layer thickness ($t_mathrm{eff}$). The magnitude of the Dzyaloshinskii-Moriya exchange constant ($|D|$) increases with decreasing $t_mathrm{eff}$ until $t_mathrm{eff} sim$1 nm, below which $|D|$ decreases. MCA and $|D|$ scale with $1/t_mathrm{eff}$ for $t_mathrm{eff}$ larger than $sim$1.0 nm, indicating an interfacial origin. To clarify the cause of the $t_mathrm{eff}$ dependences of MCA and DMI, the OMA of Co in W/Co/Pt trilayers is studied using x-ray magnetic circular dichroism (XMCD). We find non-zero OMA when $t_mathrm{eff}$ is smaller than $sim$0.8 nm. The OMA increases with decreasing $t_mathrm{eff}$ at a rate that is larger than what is expected from the MCA and Brunos formula, indicating that other factors contribute to the MCA at small $t_mathrm{eff}$ to break the $1/t_mathrm{eff}$ scaling. The $t_mathrm{eff}$ dependence of the OMA also suggests that $|D|$ at $t_mathrm{eff}$ smaller than $sim$1 nm is independent of the OMA at the interface. We consider the growth of Co on W results in a strain that reduces the interfacial MCA and DMI at small $t_mathrm{eff}$, indicating the importance of lattice structure to control their properties.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها