Spin current injection from sputtered yttrium iron garnet (YIG) films into an adjacent platinum layer has been investigated by means of the spin pumping and the spin Seebeck effects. Films with a thickness of 83 and 96 nanometers were fabricated by on-axis magnetron rf sputtering at room temperature and subsequent post-annealing. From the frequency dependence of the ferromagnetic resonance linewidth, the damping constant has been estimated to be $(7.0pm1.0)times 10^{-4}$. Magnitudes of the spin current generated by the spin pumping and the spin Seebeck effect are of the same order as values for YIG films prepared by liquid phase epitaxy. The efficient spin current injection can be ascribed to a good YIG|Pt interface, which is confirmed by the large spin-mixing conductance $(2.0pm0.2)times 10^{18}$ m$^{-2}$.
Electrical generation of THz spin waves is theoretically explored in an antiferromangetic nanostrip via the current-induced spin-orbit torque. The analysis based on micromagnetic simulations clearly illustrates that the Neel-vector oscillations excit
We report very efficient spin current generation by the spin Hall effect in the alloy Au0.25Pt0.75, which, as determined by two different direct spin-orbit torque measurements, exhibits a giant internal spin Hall ratio of > 0.58 (anti-damping spin-or
After one decade of the intensive theoretical and experimental explorations, whether interfacial spin-orbit coupling (ISOC) at metallic magnetic interfaces can effectively generate a spin current has remained in dispute. Here, utilizing the Ti/FeCoB
The charge and spin diffusion equations taking into account spin-flip and spin-transfer torque were numerically solved using a finite element method in complex non-collinear geometry with strongly inhomogeneous current flow. As an illustration, spin-
Topological materials with large spin-orbit coupling and immunity to disorder-induced symmetry breaking show great promise for efficiently converting charge to spin. Here, we report that long-range disordered sputtered WTex thin films exhibit local c