We report directional point-contact spectroscopy data on the novel Bi2Te3/Fe1+yTe interfacial superconductor for a Bi2Te3 thickness of 9 quintuple layers, bonded by van der Waals epitaxy to a Fe1+yTe film at an atomically sharp interface. Our data sh
ow a very large superconducting twin-gap structure with an energy scale exceeding that of bulk FeSe or FeSe1-xTex by a factor of 4. While the larger gap is isotropic and attributed to a thin FeTe layer in proximity of the interface, the smaller gap has a pronounced anisotropy and is associated with proximity-induced superconductivity in the topological insulator Bi2Te3. Zero resistance is lost above 8 K, but superconducting fluctuations are visible up to at least 12 K and the large gap is replaced by a pseudogap that persists up to 40 K. The spectra show a pronounced zero-bias conductance peak in the superconducting state, which may be a signature of an unconventional pairing mechanism.
Oxygen was systematically incorporated in MBE grown MgB2 films using in-situ post-growth anneals in an oxygen environment. Connectivity analysis in combination with measurements of the critical temperature and resistivity indicate that oxygen is dist
ributed both within and between the grains. High values of critical current densities in field (~4x10^5 A/cm^2 at 8 T and 4.2 K), extrabolated critical fields (>45 T) and slopes of critical field versus temperature (1.4 T/K) are observed. Our results suggest that low growth temperatures (300oC) and oxygen doping (>0.65%) can produce MgB2 with high Jc values in field and Hc2 for high-field magnet applications.
We propose to study hadron-hadron scattering using lattice QCD in an asymmetric box which allows one to access more non-degenerate low-momentum modes for a given volume. The conventional L{u}schers formula applicable in a symmetric box is modified ac
cordingly. To illustrate the feasibility of this approach, pion-pion elastic scattering phase shifts in the I=2, J=0 channel are calculated within quenched approximation using improved gauge and Wilson fermion actions on anisotropic lattices in an asymmetric box. After the chiral and continuum extrapolation, we find that our quenched results for the scattering phase shifts in this channel are consistent with the experimental data when the three-momentum of the pion is below 300MeV. Agreement is also found when compared with previous theoretical results from lattice and other means. Moreover, with the usage of asymmetric volume, we are able to compute the scattering phases in the low-momentum range (pion three momentum less than about 350MeV in the center of mass frame) for over a dozen values of the pion three-momenta, much more than using the conventional symmetric box with comparable volume.
The amount of oxygen incorporated into MgB2 thin films upon exposure to atmospheric gasses is found to depend strongly on the materials stoichiometry. Rutherford backscattering spectroscopy was used to monitor changes in oxygen incorporation resultin
g from exposure to: (a) ambient atmosphere, (b) humid atmospheres, (c) anneals in air and (d) anneals in oxygen. The study investigated thin-film samples with compositions that were systematically varied from Mg0.9B2 to Mg1.1B2. A significant surface oxygen contamination was observed in all of these films. The oxygen content in the bulk of the film, on the other hand, increased significantly only in Mg rich films and in films exposed to humid atmospheres.
Our Rutherford backscattering spectrometry (RBS) study has found that concentrations up to 7 atomic percent of Rb and Cs can be introduced to a depth of ~700 A in MgB2 thin films by annealing in quartz ampoules containing elemental alkali metals at <
350 degree centigrade. No significant change in transition temperature (Tc) was observed, in contrast to an earlier report of very high Tc (>50 K) for similar experiments on MgB2 powders. The lack of a significant change in Tc and intra-granular carrier scattering suggests that Rb and Cs diffuse into the film, but do not enter the grains. Instead, the observed changes in the electrical properties, including a significant drop in Jc and an increase in delta rho (rho300-rho40), arise from a decrease in inter-granular connectivity due to segregation of the heavy alkaline metals and other impurities (i.e. C and O) introduced into the grain boundary regions during the anneals.