High-pressure superconductivity in a rare-earth doped Ca0.86Pr0.14Fe2As2 single crystalline sample has been studied up to 12 GPa and temperatures down to 11 K using designer diamond anvil cell under a quasi-hydrostatic pressure medium. The electrical
resistance measurements were complemented by high pressure and low temperature x-ray diffraction studies at a synchrotron source. The electrical resistance measurements show an intriguing observation of superconductivity under pressure, with Tc as high as ~51 K at 1.9 GPa, presenting the highest Tc reported in the intermetallic class of 1-2-2 iron-based superconductors. The resistive transition observed suggests a possible existence of two superconducting phases at low pressures of 0.5 GPa: one phase starting at Tc1 ~48 K, and the other starting at Tc2~16 K. The two superconducting transitions show distinct variations with increasing pressure. High pressure low temperature structural studies indicate that the superconducting phase is a collapsed tetragonal ThCr2Si2-type (122) crystal structure. Our high pressure studies indicate that high Tc state attributed to non-bulk superconductivity in rare-earth doped 1-2-2 iron-based superconductors is stable under compression over a broad pressure range.
High pressure electrical resistance and x-ray diffraction measurements have been performed on ruthenium-doped Ba(Fe0.9Ru0.1)2As2, up to pressures of 32 GPa and down to temperatures of 10 K, using designer diamond anvils under quasi-hydrostatic condit
ions. At 3.9 GPa, there is an evidence of pressure-induced superconductivity with Tc onset of 24 K and zero resistance at Tc zero of ~14.5 K. The superconducting transition temperature reaches maximum at ~5.5 GPa and then decreases gradually with increase in pressure before completely disappearing above 11.5 GPa. Upon increasing pressure at 200 K, an isostructural phase transition from a tetragonal (I4/mmm) phase to a collapsed tetragonal phase is observed at 14 GPa and the collapsed phase persists up to at least 30 GPa. The changes in the unit cell dimensions are highly anisotropic across the phase transition and are qualitatively similar to those observed in undoped BaFe2As2 parent.
Simultaneous high pressure x-ray diffraction and electrical resistance measurements have been carried out on a PbO type {alpha}-FeSe0.92 compound to a pressure of 44 GPa and temperatures down to 4 K using designer diamond anvils at synchrotron source
. At ambient temperature, a structural phase transition from a tetragonal (P4/nmm) phase to an orthorhombic (Pbnm) phase is observed at 11 GPa and the Pbnm phase persists up to 74 GPa. The superconducting transition temperature (TC) increases rapidly with pressure reaching a maximum of ~28 K at ~ 6 GPa and decreases at higher pressures, disappearing completely at 14.6 GPa. Simultaneous pressure-dependent x-ray diffraction and resistance measurements at low temperatures show superconductivity only in a low pressure orthorhombic (Cmma) phase of the {alpha}-FeSe0.92. Upon increasing pressure at 10 K near TC, crystalline phases change from a mixture of orthorhombic (Cmma) and hexagonal (P63/mmc) to a high pressure orthorhombic (Pbnm) phase near 6.4 GPa where TC is maximum.
High-pressure electrical resistance measurements have been performed on single crystal Ba0.5Sr0.5Fe2As2 platelets to pressures of 16 GPa and temperatures down to 10 K using designer diamond anvils under quasi-hydrostatic conditions with an insulating
steatite pressure medium. The resistance measurements show evidence of pressure-induced superconductivity with an onset transition temperature at ~31 K and zero resistance at ~22 K for a pressure of 3.3 GPa. The transition temperature decreases gradually with increasing in pressure before completely disappearing for pressures above 12 GPa. The present results provide experimental evidence that a solid solution of two 122-type materials, e.g., Ba1-x.SrxFe2As2 (0 < x <1), can also exhibit superconductivity under high pressure
The structural properties of EuCo2As2 have been studied up to 35 GPa, through the use of x-ray diffraction in a diamond anvil cell at a synchrotron source. At ambient conditions, EuCo2As2 (I4/mmm) has a tetragonal lattice structure with a bulk modulu
s of 48 +/-4 GPa. With the application of pressure, the a-axis exhibits negative compressibility with a concurrent sharp decrease in c-axis length. The anomalous compressibility of the a-axis continues until 4.7 GPa, at which point the structure undergoes a second-order phase transition to a collapsed tetragonal (CT) state with a bulk modulus of 111 +/- 2 GPa. We found a strong correlation between the ambient pressure volume of 122 parents of superconductors and the corresponding tetragonal to collapsed tetragonal phase transition pressures
We have investigated structural and magnetic phase transitions under high pressures in a quaternary rare earth transition metal arsenide oxide NdCoAsO compound that is isostructural to high temperature superconductor NdFeAsO. Four-probe electrical re
sistance measurements carried out in a designer diamond anvil cell show that the ferromagnetic Curie temperature and anti-ferromagnetic Neel temperature increase with an increase in pressure. High pressure x-ray diffraction studies using a synchrotron source show a structural phase transition from a tetragonal phase to a new crystallographic phase at a pressure of 23 GPa at 300 K. The NdCoAsO sample remained anti-ferromagnetic and non-superconducting to temperatures down to 10 K and to the highest pressure achieved in this experiment of 53 GPa. A P-T phase diagram for NdCoAsO is presented to a pressure of 53 GPa and low temperatures of 10 K.
The crystal structure and electrical resistance of the structurally-layered EuFe2As2 have been studied up to 70 GPa and down to temperature of 10 K, using a synchrotron x-ray source and the designer diamond anvils. The room-temperature compression of
the tetragonal phase of EuFe2As2 (I4/mmm) results in an increase in the a-axis and a rapid decrease in c-axis with increasing pressure. This anomalous compression reaches a maximum at 8 GPa and the tetragonal lattice behaves normal above 10 GPa with a nearly constant c/a axial ratio. The rapid rise in superconducting transition temperature (Tc) to 41 K with increasing pressure is correlated to this anomalous compression and a decrease in Tc is observed above 10 GPa. We present P-V data or equation of state of EuFe2As2 in both the ambient tetragonal phase and the high pressure collapsed tetragonal phase to 70 GPa.