Effect of natural pozzolan on the durability of precast products of Glass Fiber Reinforced Concrete (GFRC)

أثر البوزولانا الطبيعية على ديمومة المنتجات المسبقة الصنع من الخرسانة المسلحة بالألياف الزجاجية GFRC

1497   2   13   0.0 ( 0 )
 Publication date 2018
and research's language is العربية
 Created by Shamra Editor




Ask ChatGPT about the research

The aim of this study is improving the durability of precast products of Glass Fiber Reinforced Concrete (GRC) and in the context of sustainability applications, reduction of cement consumption and replacement of it with green materials. This study has been done to test the role of the natural pozzolan from Shihan Hill in As Suwayda as supplementary cementing material by 10% -15% -20% - 25%, and to determine the effect of it on the consistency and flexure strength over 180 days, as well as to test its role in improving the micro-structure of the mixture by reducing the content of Ca(OH)2 and increasing C-S-H & C-A-S-H gel, which were tested using X-Ray Diffraction (XRD) and Energy Dispersive X-Ray (EDX) techniques, and as a result reduced the erosion of fibers as shown in images by Scanning Electronic Electron Microscopy (SEM). Moreover the role of pozzolana has been studied in controlling the degradation of the material over time which tested by immersion in hot water 50° for 150 days and by drying – wetting cycles. Also the effect of pozzolana on absorption, porosity and resistance of sulfates attacks was studied. The results have shown that the used natural pozzolana has no negative effect on consistency or mechanical properties, and it improved all the studied durability factors.


Artificial intelligence review:
Research summary
تهدف هذه الدراسة إلى تحسين ديمومة المنتجات المسبقة الصنع من الخرسانة المسلحة بالألياف الزجاجية (GFRC) من خلال استبدال جزء من الأسمنت بالبوزولانا الطبيعية المستخرجة من تل شيحان في السويداء. تم اختبار تأثير نسب مختلفة من البوزولانا (10%، 15%، 20%، 25%) على قوام الخلطة ومقاومة الشد بالانعطاف على مدى 180 يومًا. كما تم دراسة تأثير البوزولانا على البنية الداخلية للخلطة باستخدام تقنيات الأشعة السينية (XRD) والتحليل الطيفي (EDX) والمجهر الإلكتروني الماسح (SEM). أظهرت النتائج أن البوزولانا الطبيعية لم تؤثر سلبًا على قوام الخلطة أو الخصائص الميكانيكية، بل حسنت جميع عوامل الديمومة المدروسة مثل تقليل محتوى هيدروكسيد الكالسيوم وزيادة الجل الهلامي (C-S-H) وتقليل تهتك الألياف. بالإضافة إلى ذلك، تم تحسين مقاومة الامتصاص والمسامية ومقاومة هجمات الكبريتات.
Critical review
تعتبر الدراسة قيمة ومهمة في مجال تحسين ديمومة الخرسانة المسلحة بالألياف الزجاجية باستخدام مواد طبيعية ومستدامة. ومع ذلك، يمكن أن تكون هناك بعض النقاط التي تحتاج إلى مزيد من البحث والتوضيح. على سبيل المثال، لم تتناول الدراسة تأثير البوزولانا على خصائص الانكماش ومقاومة الأحماض والقلويات، وهي عوامل مهمة في تقييم ديمومة الخرسانة. كما أن الدراسة اقتصرت على استخدام بوزولانا تل شيحان فقط، مما يحد من تعميم النتائج على أنواع أخرى من البوزولانا. بالإضافة إلى ذلك، لم يتم التطرق إلى التكلفة الاقتصادية لاستخدام البوزولانا مقارنة بالمواد التقليدية، وهو جانب مهم يجب مراعاته في التطبيقات العملية.
Questions related to the research
  1. ما هو الهدف الرئيسي من الدراسة؟

    الهدف الرئيسي من الدراسة هو تحسين ديمومة المنتجات المسبقة الصنع من الخرسانة المسلحة بالألياف الزجاجية باستخدام البوزولانا الطبيعية كمستبدل للأسمنت.

  2. ما هي النسب التي تم اختبارها من البوزولانا في الدراسة؟

    تم اختبار نسب 10%، 15%، 20%، و25% من البوزولانا كمستبدل للأسمنت في الدراسة.

  3. ما هي التقنيات المستخدمة لتحليل البنية الداخلية للخلطة؟

    تم استخدام تقنيات الأشعة السينية (XRD) والتحليل الطيفي (EDX) والمجهر الإلكتروني الماسح (SEM) لتحليل البنية الداخلية للخلطة.

  4. ما هي النتائج الرئيسية التي توصلت إليها الدراسة؟

    أظهرت الدراسة أن البوزولانا الطبيعية لم تؤثر سلبًا على قوام الخلطة أو الخصائص الميكانيكية، بل حسنت جميع عوامل الديمومة المدروسة مثل تقليل محتوى هيدروكسيد الكالسيوم وزيادة الجل الهلامي (C-S-H) وتقليل تهتك الألياف.


References used
ABOUBAKAR, M. and et al. A Study on the Effect the addition of thermally treated Libyan Natural Pozzolan on the Mechanical Properties of Ordinary Portland Cement Mortar. International Journal of Science and Technology, Vol. 3, No, 1, 2014, 79-84
ACI Committee 201.2R-01. Guide to Durable Concrete. American Concrete Institute, Farmington Hills, Michigan, 2001, 41
ACI Committee 232. 1R. Use of Raw or Processed Natural Pozzolans in Concrete. American Concrete Institute, Farmington Hills, Michigan, 2001
rate research

Read More

This research aims to study the effect of heat treatment on curing of reinforced Unsaturated Polyester Resin (UPR) with fiberglass, and to study the effect of storage time and the time of exposure to natural aging on curves absorption. The results showed that it is very difficult to reach a fully curing to UPR matrix, and Storage samples for three years reveal resistance to degradation in fresh and seawater comparing with storage samples for three months, or aging by exposed to environmental for three years. The results showed also that the absorption occurs by thin film, and not prevent by increasing the layers of reinforcement
Thepaper studies the mechanical properties ofsteel fibers reinforced lightweight concrete.This kind of concrete is produced by usingscoria aggregateswhich can be found abundantly in Syria. Thelightweight concrete mixeswere designed for three differ ent percentage of steel fibers (0, 0.5, 0.75)%. Different tests were performed to determine mechanical properties of product concrete such as compressive strength, elasticity modulus, splitting tensile strengthand flexural strengthalso; the stress–strain diagram of produced lightweight concrete was established under compression. The results showedanincrease of the compressive, splitting tensile and flexural strengths reach up 16.9%, 25.6%, and 53.6% respectivelywhen the steel fibers were used. Also the results indicated the importance of using the steel fibers to improve the performance of concrete and change its brittle behavior to ductile behavior.
This research aims to study the effect of addition the filling materials (sodium aluminosilicate, Talc) to the unsaturated polyester(unsaturated polyester resign)(UPR) first, and unsaturated polyester reinforced by fiberglass (20%) secondly, Number o f mechanical tests were done, they included (Tensile, Flexural Strength). The effect of addition of filling materials sodium aluminosilicate (SAS), Talc, and a mixture of sodium aluminosilicate and Talc to the unreinforced polyester with fiberglass was studied in the first step of the research, and the results showed that the best values were gotten when adding a mixture of ((SAS) and Talc) at ratio (10% SAS,5% Talc), where the tensile strength value raised up from (31.2 MPa) to (33 MPa), and the elastic module value also raised up from (2330 MPa) to (2750.5 MPa) , and the flexural strength value also raised up from (0.057 GPa) to (0.0729 GPa). The effect of addition of filling materials (sodium aluminosilicate, Talc, and a mixture of sodium aluminosilicate and Talc ) to the reinforced polyester with fiberglass (20%) was studied in the second step of the research, and the results showed that the best values were gotten when adding a mixture of ((SAS) and Talc) at ratio (5% SAS,5% Talc), where the tensile strength value raised up from (101.7 MPa) to (108.8 MPa), and the elastic module value also raised up from (5616 MPa) to (6367.9 MPa), and the flexural strength value raised up from (0.1203 GPa) to (0.1597 GPa).
This paper makes an experimental and analytical investigation of cracks characteristics in Fiber Reinforced Polymer strengthened RC beams under different levels of sustained load and Reinforced ratio. As the equations available for conventional RC b eams are inappropriate for the calculation of the short-term crack width in FRP-strengthened RC beams[8], a statistical analysis is carried out on available test data from international sources [6-9-10] and from the test results obtained in the current study (Concrete Labor- Civil engineering Department- Damascus University-2014) to establish a new equation that considers the effect of the FRP laminates. This equation is a correlation of stress in steel bars, concrete surface tension , and effective side cover. The long-term crack width is then related to the instantaneous crack width by empirical equations which are derived from the test results obtained in the current study.