In Vitro Comparative Study Between Glass ionomer and calcium silicate cements for solubility evaluation

دراسة مخبرية مقارنة بين الإسمنت الزجاجي الأيوني و إسمنت سيلكات الكالسيوم لتقييم الذوبانية

660   0   2   0 ( 0 )
 Publication date 2018
and research's language is العربية
 Created by Shamra Editor




Ask ChatGPT about the research

A comparative study was conducted between GIC and Biodentine Cements by assessing their solubility, their effect on pH, their ability to absorb water, and calcium release in the same laboratory conditions.


Artificial intelligence review:
Research summary
أجريت دراسة مقارنة بين الإسمنت الزجاجي الأيوني (GIC) وإسمنت سيلكات الكالسيوم (Biodentine) لتقييم ذوبانيتهما وتأثيرهما على درجة حموضة الوسط وقدرتهما على امتصاص الماء وتحرير الكالسيوم في الشروط المخبرية ذاتها. أظهرت النتائج أن ذوبانية كل من المادتين ترتبط بشكل مباشر بطبيعة المواد المكونة لها. بالنسبة لـ Biodentine، لوحظت زيادة واضحة في درجة حموضة محاليل الغمر نتيجة إماهة سيلكات الكالسيوم، مع زيادة ملحوظة في قيم الذوبانية خلال المراحل الأولى من الغمر بسبب ذوبان البوليمر وكربونات الكالسيوم. أما بالنسبة لـ GIC، فإنّ قيماً عالية للذوبانية خلال المراحل الأولى من الغمر ترافقت مع انخفاض في قيمة درجة الحموضة وشراهة واضحة للماء. تساهم نتائج الدراسة في تقديم فهم أفضل لسلوك كل من Biodentine و GIC وآلية تفاعلهما، مما يساهم في سهولة تقييم الأداء السريري لكل من المادتين وفهم المشاكل التي يمكن أن تترافق مع استعمالهما في الوسط الفموي.
Critical review
دراسة نقدية: تعتبر هذه الدراسة خطوة مهمة نحو فهم أفضل لسلوك المواد الترميمية المستخدمة في طب الأسنان. ومع ذلك، يمكن أن تكون هناك بعض النقاط التي تحتاج إلى مزيد من التوضيح. على سبيل المثال، لم يتم التطرق بشكل كافٍ إلى تأثير العوامل البيئية المختلفة مثل درجة الحرارة والرطوبة على النتائج. كما أن الدراسة تركز بشكل كبير على الشروط المخبرية، مما قد يجعل من الصعب تطبيق النتائج بشكل مباشر على الحالات السريرية. بالإضافة إلى ذلك، يمكن أن تكون هناك حاجة لمزيد من الدراسات المقارنة مع مواد ترميمية أخرى للحصول على صورة أكثر شمولية.
Questions related to the research
  1. ما هي المواد التي تم دراستها في هذه البحث؟

    تم دراسة الإسمنت الزجاجي الأيوني (GIC) وإسمنت سيلكات الكالسيوم (Biodentine).

  2. ما هي العوامل التي تم تقييمها في هذه الدراسة؟

    تم تقييم الذوبانية، تأثيرها على درجة حموضة الوسط، قدرتها على امتصاص الماء، وتحرير الكالسيوم.

  3. ما هي النتائج الرئيسية للدراسة بالنسبة لـ Biodentine؟

    لوحظت زيادة واضحة في درجة حموضة محاليل الغمر وزيادة ملحوظة في قيم الذوبانية خلال المراحل الأولى من الغمر بسبب ذوبان البوليمر وكربونات الكالسيوم.

  4. ما هي الفائدة العملية من نتائج هذه الدراسة؟

    تساهم نتائج الدراسة في تقديم فهم أفضل لسلوك كل من Biodentine وGIC وآلية تفاعلهما، مما يسهل تقييم الأداء السريري لكل من المادتين وفهم المشاكل التي يمكن أن تترافق مع استعمالهما في الوسط الفموي.


References used
ABU ZEID, S. T. H., ALOTHMANI, O. S., YOUSEF, M. K. (2015) Biodentine and Mineral Trioxide Aggregate: An Analysis of Solubility, pH Changes and Leaching Elements Life Science Journal, Vol. 12, 18-23
AL-HYALI, N. A. (2017) Comparison among pulp capping materials in: calcium ion release, pH change, solubility and water sorption (An in vitro study), Journal of baghdad college of dentistry, Vol. 29, 9-16
FOREMAN, P. C., BARNES, I. E. (1990) A review of calcium hydroxide, International Endodontic Journal, Vol. 23, 283-297
rate research

Read More

The research aims to evaluate the micro shear bond strength of the calcium silicate cement (Biodentine) and the glass ionomer cement (GIC) to dentine. The study was performed using upper or lower premolars, and samples were divided into six equal s ubgroups according to the time period (3 h, 1 day, 1 week, 2 weeks, 4 weeks, 8 weeks), in order to study changes in the values of shear bond strength with time. The comparative study showed that the success rate of adhesion in the Biodentine group was smaller than that in the GIC group for the tested premolars after 3 hours and one day, whereas the success rate in the Biodentine group was greater than that in the GIC group for the tested premolars after 8 weeks. Results showed a positive correlation between the mean values of shear bond strengths and the studied time in Biodentine group, which ranged from 1.49 ± 0.18 MPa at 3 hours to a maximum value of 2.65 ± 0.26 MPa after 8 weeks. While there was a negative correlation between the mean values and the studied time in the GIC group and values ranged from 3.02 ± 0.13 MPa at 3 hours and 2.06 ± 0.09 MPa at 8 weeks. The study showed the advantage of Biodentine compared with GIC in terms of micro-bonding to dentine, which can have a clinically significant importance in preventing the micro leakage and reducing bacterial contamination.
One aim of the root canal treatment is providing compact three dimensional seal for the canal system to prevent germs enter and its products across both the apical and coronal ways. Gutta-Percha is the most use material to fill the radicalism ca nals. It has limited importance in spite of many specifications as lack of the link to the ridge canal.
An appropriate bond between glass‑ionomer and the superficial resin materials is very important for the success of sandwich technique. The aim of the present in vitro study was to evaluate the effect of three surface treatments of conventional glass‑ionomer on its shear bond strength to giomer
The purpose of this study was to compare the shear bond strength to root dentin of a nano- ionomer material (Ketac N100,3M) and a fifth generation bonding material (Excite,Vivadent) applied with a resin composite (Tetric-ceram,Vivadent), in order to determine the material of choice for restoring root extended lesions.
Usually, it's hard to reach the final color identity with normal teeth when using full glass ceramic, but this matter is very important for the cosmetic successful of these restorations. This in vitro study evaluated the effect of cement color on the final color of full crown glass ceramic of system IPS e.max.
comments
Fetching comments Fetching comments
Sign in to be able to follow your search criteria
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا