تسجيل مستخدم جديدObservation of double superconducting transition in Y0.55Pr0.45Ba2Cu3O7-d polycrystalline sample by Hall effect measurement
46
0
0.0
(
0
)
نشر من قبل
Antonio Jefferson S Machado A.J.S.Machado
تاريخ النشر
2006
مجال البحث
فيزياء
والبحث باللغة
English
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
This work reports longitudinal (RXX) and transverse (RXY) resistance as a function of the temperature measured at low magnetic fields for a Y0.55Pr0.45Ba2Cu3O7-d polycrystalline sample. It is observed nonzero transverse voltage at zero external magnetic below superconducting transition and above no such voltage was detected. Comparing RXX (T) and RXY (T) curves it was possible to observe a correlation between Hall resistance and double resistive superconducting transition. Magneto-resistance RXX(H) measurements showed that the dissipation is dominated by weak coupling between superconducting clusters. I-V and R(T) curves of both components suggest that the positive Hall voltage at superconducting state must be related to quasiparticle currents.
قيم البحث
اقرأ أيضاً
We report results of dc magnetic and ac linear low-frequency study of a polycrystalline MgB$_2$ sample. AC susceptibility measurements at low frequencies, performed under dc fields parallel to the sample surface, provide a clear evidence for surface superconducting states in MgB$_2$.
We investigated the influence of different Ag additions (up to 10 wt %) on the superconducting properties of FeSe0.94. The structural investigations (XRD and SEM) indicated that Ag is present in three different forms. Ag at grain boundaries supports
the excellent intergrain connections and reduces superconducting transition width to values smaller than 1K at B=0 and smaller than 2.74 K at B=14 T. Ag insertion in the crystal lattice unit cell provides additional carriers and changes the electron hole imbalance in FeSe0.94. This results in an increase in the magnetoresistive effect (MR) and critical temperature (Tc). Reacted Ag forms a small amount (~1%) of Ag2Se impurity phase, which may increase the pinning energy in comparison with that of the undoped sample. The enhanced upper critical field (Bc2) is also a result of the increased impurity scattering. Thus, unlike cuprates Ag addition enhances the Tc, Bc2, pinning energy and MR making the properties of polycrystalline FeSe0.94 similar to those of single crystals.
Here we describe the results of an atomic resolution study of oxygen incorporation into bulk MgB2. We find that ~20-100 nm sized precipitates are formed by ordered substitution of oxygen atoms onto boron lattice sites, while the basic bulk MgB2 cryst
al structure and orientation is preserved. The periodicity of the oxygen ordering is dictated by the oxygen concentration in the precipitates and primarily occurs in the (010) plane. The presence of these precipitates correlates well with an improved critical current density and superconducting transition behavior, implying that they act as pinning centers.
The Hall resistivity rho_{xy} of LuNi_2B_2C is negative in the normal as well as in the mixed state and has no sign reversal typical for high-T_c superconductors. A distinct nonlinearity in the rho_{xy} dependence on field H was found in the normal s
tate for T < 40K, accompanied by a large magnetoresistance reaching +90% for mu_0H=16T at T=20K. The scaling relation rho_{xy} ~ rho_{xx}^beta (rho_{xx} is the longitudinal resistivity) was found in the mixed state, the value of beta being dependent on the degree of disorder.
Heterostructures of superconducting and ferromagnetic materials are of fundamental interest because of the mutual interaction of antagonistic kinds of ordering at the S-F interface. Normally, the superconducting transition temperature Tc should be st
rongly suppressed at the S-F interface owing to the penetration of Cooper pairs into the ferromagnetic side. Nevertheless, constructive interactions between S and F orders have been suggested to occur via the modification of ferromagnetic order by the superconducting state. This may induce an inhomogeneous magnetic state, often called a cryptoferromagnetic state, and the relevant domain wall effect, which will lead to a local decrease of the pair-breaking parameter. However, the domain wall effect, even if it exists, is quite subtle from the experimental view point and is normally difficult to observe. Here we show that the defect-related d0 ferromagnetism in MgO and the superconductivity in MgB2 do not antagonize, but rather enhance the superconducting transition temperature Tc to any significant degree. We found in superconducting MgB2-d0 ferromagnetic MgO composites that the superconducting transition proceeds in two steps. The first at the S-F interface, between 110-120 K, then in the rest of the bulk at 39 K, which is the Tc of single phase MgB2 superconductor. Moreover, the additional transition emerges at 60 K at the S-F interface especially in the ferromagnetic side, showing a spin-glass-like magnetic state. Our findings reveal that the proximity effect in the superconductor-d0 ferromagnet heterostructures will provide the knowledge and basis to enhance the Tc value of the existing superconductors.