This work investigates the growth of B-C-N layers by chemical vapor deposition using methylamine borane (MeAB) as single-source precursor. MeAB has been synthesized and characterized, paying particular attention to the analysis of its thermolysis products, which are the gaseous precursors for B-C-N growth. Samples have been grown on Cu foils and transferred onto different substrates for their morphological, structural, chemical, electronic and optical characterizations. The results of these characterizations indicate a segregation of h-BN and Graphene-like (Gr) domains. However, there is an important presence of B and N interactions with C at the Gr borders, and of C interacting at the h-BN-edges, respectively, in the obtained nano-layers. In particular, there is significant presence of C-N bonds, at Gr/h-BN borders and in the form of N doping of Gr domains. The overall B:C:N contents in the layers is close to 1:3:1.5. A careful analysis of the optical bandgap determination of the obtained B-C-N layers is presented, discussed and compared with previous seminal works with samples of similar composition.
قيم البحث
اقرأ أيضاً
The deposition of boron-doped amorphous carbon thin films on SiO2 substrate was achieved via a focused ion beam-assisted chemical vapor deposition of triphenyl borane (C18H15B) and triphenyl borate (C18H15BO3). The existence of boron in the deposited
film from triphenyl borane, with a precursor temperature of 90 {deg}C, was confirmed by a core level X-ray photoelectron spectroscopy analysis. The film exhibited a semiconducting behavior with a band gap of 285 meV. Although the band gap was decreased to 197 meV after an annealing process, the film was still semiconductor. Additionally, a drastic reduction of the resistance on the deposited film by applying pressures was observed from an in-situ electrical transport measurements using a diamond anvil cell.
Combining MoS$_2$ monolayers to form multilayers allows to access new functionalities. In this work, we examine the correlation between the stacking order and the interlayer coupling of valence states in MoS$_2$ homobilayer samples grown by chemical
vapor deposition (CVD) and artificially stacked bilayers from CVD monolayers. We show that hole delocalization over the bilayer is allowed in 2H stacking and results in strong interlayer exciton absorption and also in a larger A-B exciton separation as compared to 3R bilayers, where both holes and electrons are confined to the individual layers. Comparing 2H and 3R reflectivity spectra allows to extract an interlayer coupling energy of about $t_perp=49$ meV. Obtaining very similar results for as-grown and artificially stacked bilayers is promising for assembling large area van der Waals structures with CVD material, using interlayer exciton absorption and A-B exciton separation as indicators for interlayer coupling. Beyond DFT calculations including excitonic effects confirm signatures of efficient interlayer coupling for 2H stacking in agreement with our experiments.
Fabrication of single nickel-nitrogen (NE8) defect centers in diamond by chemical vapor deposition is demonstrated. Under continuous-wave 745 nm laser excitation single defects were induced to emit single photon pulses at 797 nm with a linewidth of 1
.5 nm at room temperature. Photon antibunching of single centers was demonstrated using a Hanbury-Brown and Twiss interferometer. Confocal images revealed approximately 10^6 optically active sites/cm^2 in the synthesized films. The fabrication of an NE8 based single photon source in synthetic diamond is important for fiber based quantum cryptography. It can also be used as an ideal point-like source for near-field optical microscopy.
Direct growth of flat micrometer-sized bilayer graphene islands in between molybdenum disulfide sheets is achieved by chemical vapor deposition of ethylene at about 800 {deg}C. The temperature assisted decomposition of ethylene takes place mainly at
molybdenum disulfide step edges. The carbon atoms intercalate at this high temperature, and during the deposition process, through defects of the molybdenum disulfide surface such as steps and wrinkles. Post growth atomic force microscopy images reveal that circular flat graphene islands have grown at a high yield. They consist of two graphene layers stacked on top of each other with a total thickness of 0.74 nm. Our results demonstrate direct, simple and high yield growth of graphene/molybdenum disulfide heterostructures, which can be of high importance in future nanoelectronic and optoelectronic applications.
Nanographitic structures (NGSs) with multitude of morphological features are grown on SiO2/Si substrates by electron cyclotron resonance - plasma enhanced chemical vapor deposition (ECR-PECVD). CH4 is used as source gas with Ar and H2 as dilutants. F
ield emission scanning electron microscopy, high resolution transmission electron microscopy (HRTEM) and Raman spectroscopy are used to study the structural and morphological features of the grown films. Herein, we demonstrate, how the morphology can be tuned from planar to vertical structure using single control parameter namely, dilution of CH4 with Ar and/or H2. Our results show that the competitive growth and etching processes dictate the morphology of the NGSs. While Ar-rich composition favors vertically oriented graphene nanosheets, H2-rich composition aids growth of planar films. Raman analysis reveals dilution of CH4 with either Ar or H2 or in combination helps to improve the structural quality of the films. Line shape analysis of Raman 2D band shows nearly symmetric Lorentzian profile which confirms the turbostratic nature of the grown NGSs. Further, this aspect is elucidated by HRTEM studies by observing elliptical diffraction pattern. Based on these experiments, a comprehensive understanding is obtained on the growth and structural properties of NGSs grown over a wide range of feedstock compositions.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها