The deposition of boron-doped amorphous carbon thin films on SiO2 substrate was achieved via a focused ion beam-assisted chemical vapor deposition of triphenyl borane (C18H15B) and triphenyl borate (C18H15BO3). The existence of boron in the deposited film from triphenyl borane, with a precursor temperature of 90 {deg}C, was confirmed by a core level X-ray photoelectron spectroscopy analysis. The film exhibited a semiconducting behavior with a band gap of 285 meV. Although the band gap was decreased to 197 meV after an annealing process, the film was still semiconductor. Additionally, a drastic reduction of the resistance on the deposited film by applying pressures was observed from an in-situ electrical transport measurements using a diamond anvil cell.
قيم البحث
اقرأ أيضاً
This work investigates the growth of B-C-N layers by chemical vapor deposition using methylamine borane (MeAB) as single-source precursor. MeAB has been synthesized and characterized, paying particular attention to the analysis of its thermolysis pro
ducts, which are the gaseous precursors for B-C-N growth. Samples have been grown on Cu foils and transferred onto different substrates for their morphological, structural, chemical, electronic and optical characterizations. The results of these characterizations indicate a segregation of h-BN and Graphene-like (Gr) domains. However, there is an important presence of B and N interactions with C at the Gr borders, and of C interacting at the h-BN-edges, respectively, in the obtained nano-layers. In particular, there is significant presence of C-N bonds, at Gr/h-BN borders and in the form of N doping of Gr domains. The overall B:C:N contents in the layers is close to 1:3:1.5. A careful analysis of the optical bandgap determination of the obtained B-C-N layers is presented, discussed and compared with previous seminal works with samples of similar composition.
We introduce a novel nanofabrication technique to directly deposit catalyst pads for the chemical vapor deposition synthesis of single-walled carbon nanotubes (SWCNTs) at any desired position on a substrate by Gallium focused ion beam (FIB) induced d
eposition of silicon oxide thin films from the metalorganic Tetraethyl orthosilicate (TEOS) precursor. A high resolution in the positioning of the SWCNTs is naturally achieved as the imaging and deposition by FIB are conducted concurrently in situ at the same selected point on the substrate. This technique has substantial advantages over the current state-of-the-art methods that are based on complex and multistep lithography processes.
Superconducting nanowires, with a critical temperature of 5.2 K, have been synthesized using an ion-beam-induced deposition, with a Gallium focused ion beam and Tungsten Carboxyl, W(CO)6, as precursor. The films are amorphous, with atomic concentrati
ons of about 40, 40, and 20 % for W, C, and Ga, respectively. Zero Kelvin values of the upper critical field and coherence length of 9.5 T and 5.9 nm, respectively, are deduced from the resistivity data at different applied magnetic fields. The critical current density is Jc= 1.5 10^5 A/cm2 at 3 K. This technique can be used as a template-free fabrication method for superconducting devices.
Recent advances in focused ion beam technology have enabled high-resolution, direct-write nanofabrication using light ions. Studies with light ions to date have, however, focused on milling of materials where sub-surface ion beam damage does not inhi
bit device performance. Here we report on direct-write milling of single crystal diamond using a focused beam of oxygen ions. Material quality is assessed by Raman and luminescence analysis, and reveals that the damage layer generated by oxygen ions can be removed by nonintrusive post-processing methods such as localised electron beam induced chemical etching.
A direct patterning technique of gallium-irradiated superconducting silicon has been established by focused gallium-ion beam without any mask-based lithography process. The electrical transport measurements for line and square shaped patterns of gall
ium-irradiated silicon were carried out under self-field and magnetic field up to 7 T. Sharp superconducting transitions were observed in both patterns at temperature of 7 K. The line pattern exhibited a signature of higher onset temperature above 10 K. A critical dose amount to obtain the superconducting gallium-irradiated silicon was investigated by the fabrication of various samples with different doses. This technique can be used as a simple fabrication method for superconducting device.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها