Skyrmions are emerging topological spin structures that are potentially revolutionary for future data storage and spintronics applications. The existence and stability of skyrmions in magnetic materials is usually associated to the presence of the Dzyaloshinskii-Moriya interaction (DMI) in bulk magnets or in magnetic thin films lacking inversion symmetry. While some methods have already been proposed to generate isolated skyrmions in thin films with DMI, a thorough study of the conditions under which the skyrmions will remain stable in order to be manipulated in an integrated spintronic device are still an open problem. The stability of such structures is believed to be a result of ideal combinations of perpendicular magnetic anisotropy (PMA), DMI and the interplay between geometry and magnetostatics. In the present work we show some micromagnetic results supporting previous experimental observations of magnetic skyrmions in spin-valve stacks with a wide range of DMI values. Using micromagnetic simulations of cobalt-based disks, we obtain the magnetic ground state configuration for several values of PMA, DMI and geometric parameters. Skyrmion numbers, corresponding to the topological charge, are calculated in all cases and confirm the occurrence of isolated, stable, axially symmetric skyrmions for several combinations of DMI and anisotropy constant. The stability of the skyrmions in disks is then investigated under magnetic field and spin-polarized current, in finite temperature, highlighting the limits of applicability of these spin textures in spintronic devices.
قيم البحث
اقرأ أيضاً
Magnetic skyrmions are localized swirls of magnetization with a non-trivial topological winding number. This winding increases their robustness to superparamagnetism and gives rise to a myriad of novel dynamical properties, making them attractive as
next-generation information carriers. Recently the equation of motion for a skyrmion was derived using the approach pioneered by Thiele, allowing for macroscopic skyrmion systems to be modeled efficiently. This powerful technique suffers from the prerequisite that one must have a priori knowledge of the functional form of the interaction between a skyrmion and all other magnetic structures in its environment. Here we attempt to alleviate this problem by providing a simple analytic expression which can generate arbitrary repulsive interaction potentials from the micromagnetic Hamiltonian. We also discuss a toy model of the radial profile of a skyrmion which is accurate for a wide range of material parameters.
The understanding of the dynamical properties of skyrmion is a fundamental aspect for the realization of a competitive skyrmion based technology beyond CMOS. Most of the theoretical approaches are based on the approximation of a rigid skyrmion. Howev
er, thermal fluctuations can drive a continuous change of the skyrmion size via the excitation of thermal modes. Here, by taking advantage of the Hilbert-Huang transform, we demonstrate that at least two thermal modes can be excited which are non-stationary in time. In addition, one limit of the rigid skyrmion approximation is that this hypothesis does not allow for correctly describing the recent experimental evidence of skyrmion Hall angle dependence on the amplitude of the driving force, which is proportional to the injected current. In this work, we show that, in an ideal sample, the combined effect of field-like and damping-like torques on a breathing skyrmion can indeed give rise to such a current dependent skyrmion Hall angle. While here we design and control the breathing mode of the skyrmion, our results can be linked to the experiments by considering that the thermal fluctuations and/or disorder can excite the breathing mode. We also propose an experiment to validate our findings.
We experimentally study spin-Hall nano-oscillators based on [Co/Ni] multilayers with perpendicular magnetic anisotropy. We show that these devices are capable of single-frequency auto-oscillations at current densities comparable to those in the in-pl
ane magnetized oscillators. The demonstrated oscillators exhibit large magnetization precession amplitudes, and their oscillation frequency is highly tunable by the electric current. These features make them promising for applications in high-speed integrated microwave circuits.
Magnetic skyrmions are particle-like chiral spin textures found in a magnetic film with out-of-planeanisotropy and are considered to be potential candidates as information carriers in next generationdata storage devices. Despite intense research into
the nature of skyrmions and their dynamic prop-erties, there are several key challenges that still need to be addressed. In particular, the outstandingissues are the reproducible generation, stabilization and confinement of skyrmions at room tempera-ture. Here, we present a method for the capture of nanometer sized magnetic skyrmions in an arrayof magnetic topological defects in the form of an antidot lattice. With micromagnetic simulations,we elucidate the skyrmion formation in the antidot lattice and show that the capture is dependenton the antidot lattice parameters. This behavior is confirmed with scanning transmission x-ray mi-croscopy measurements. This demonstration that a magnetic antidot lattice can be implemented asa host to capture skyrmions provides a new platform for experimental investigations of skyrmionsand skyrmion based devices.
Magnetoresistance loops under in-plane applied field were measured on perpendicularly magnetized magnetic tunnel junction (pMTJ) pillars with nominal diameters ranging from 50 to 150 nm. By fitting the hard-axis magnetoresistance loops to an analytic
al model, the effective anisotropy fields in both free and reference layers were derived and their variations in temperature range between 340K and 5K were determined. It is found that an accurate fitting is possible only if a second-order anisotropy term of the form $-K_{2}cos^4{theta}$, is added to the fitting model. This higher order contribution exists both in the free and reference layers and its sign is opposite to that of the first order anisotropy constant, $K_{1}$. At room temperatures the estimated $-K_{2}/K_{1}$ ratios are 0.1 and 0.24 for the free and reference layers, respectively. The ratio is more than doubled at low temperatures altering the ground state of the reference layer from easy-axis to easy-cone regime. Easy-cone state has clear signatures in the shape of the hard-axis magnetoresistance loops. The same behavior was observed in all measured devices regardless of their diameter. The existence of this higher order anisotropy was confirmed experimentally on FeCoB/MgO sheet films by ferromagnetic resonance technique. It is of interfacial nature and is believed to be linked to spatial fluctuations at the nanoscale of the anisotropy parameter at the FeCoB/MgO interface, in agreement with Dieny-Vedyayev model.