تسجيل مستخدم جديدUpper critical field, critical current density and activation energy of the new La1-xSmxOF0.5BiS2 (x = 0.2, 0.8) superconductor
197
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Critical current density (Jc), thermal activation energy (U0), and upper critical field (Hc2) of La1-xSmxO0.5F0.5BiS2 (x = 0.2, 0.8) superconductors are investigated from magnetic field dependent r{ho}(T) studies. The estimated upper critical field (Hc2) has low values of 1.04 T for x = 0.2 and 1.41 T for x = 0.8. These values are lower than Sm free LaO0.5F0.5BiS2 superconductor (1.9 T). The critical current density (Jc) is estimated to be 1.35*105 A/cm2 and 5.07 *105 A/cm2 (2 K) for x = 0.2 and 0.8 respectively, using the Beans model. The thermal activation energy (U0/kB) is 61 K for x = 0.2 and 140 K for x =0.8 as calculated from Arrhenius plots at low magnetic field (1 T) and indicates a strong flux pinning potential which might be co-existing with applied magnetic field.
قيم البحث
اقرأ أيضاً
We report the results from resistivity and magnetic measurements on polycrystalline Ce oxypnictide (CeFeAsO1-xFx) samples where x spans from 0.13 to 0.25. We find that the orbital limiting field is as high as 150 T and it systematically decreases wit
h increasing doping. The Maki parameter is greater than one across the phase diagram and the large Maki parameter suggests that orbital and Pauli limiting effects contribute to the upper critical field. The broadening of the superconducting transition in the resistivity data was interpreted using the thermally activated flux flow (TAFF) model where we find that the TAFF activation energy, U0(B), is proportional to B^{-(gamma)} from 1 T to high fields, and (gamma) does not significantly change with doping. However, U0 and the superconducting critical current, Jc, are peaked in the mid-doping region (x = 0.15 to x = 0.20), and not in the low (x < 0.15) or high doping (x > 0.20) regions. Furthermore, U0 is correlated with Jc and follows the two fluid model for granular samples.
The superconducting parameters and upper critical field of the noncentrosymmetric superconductor BiPd have proven contentious. This material is of particular interest because it is a singular example of a $4f$-electron-free noncentrosymmetric superco
nductor of which crystals may be grown and cleaved, enabling surface-sensitive spectroscopies. Here, using bulk probes augmented by tunnelling data on defects, we establish that the lower of the previously reported upper critical fields corresponds to the bulk transition. The material behaves as a nearly-weak-coupled BCS s-wave superconductor, and we report its superconducting parameters as drawn from the bulk upper critical field. Possible reasons behind the order-of-magnitude discrepancy in the reported upper critical fields are discussed.
The transport properties, upper critical fields, superconducting anisotropy, and critical current density in an iso-valent phosphorus-doped BaFe2As2 single crystal close to optimum doping are investigated in this report. Temperature dependent resisti
vity and susceptibility show a superconducting transition temperature, Tc, just below 31 K both with sharp transitions. The upper critical field parallel to the ab-plane, Hc2^ab, is above 77 Tesla while that along the c-axis direction, Hc2^c, is just above 36 Tesla, yielding a low superconducting anisotropy ratio ~ 2. The estimated inter-plane coherence length based on the Ginzburg-Landau (G-L) theory indicates BaFe2(As0.68P0.32)2 is still above the point for a dimensional crossover inferring the superconducting layers are not weakly-coupled in this system. The critical current density at 5 K obtained from magnetization loops measurement show a modest Jc as high as 10^5 A/cm2.
We study the effect of 100 MeV Silicon and 200 MeV Gold ion irradiation on the inter and intra grain properties of superconducting thin films of Magnesium Diboride. Substantial decrease in inter-grain connectivity is observed, depending on irradiatio
n dose and type of ions used. We establish that modification of sigma band scattering mechanism, and consequently the upper critical field and anisotropy, depends on the size and directional properties of the extrinsic defects. Post heavy ion irradiation, the upper critical field shows enhancement at a defect density that is five orders of magnitude less compared to neutron irradiation. The critical current density however is best improved through light ion irradiation.
We have investigated the pressure effect on the newly discovered samarium doped La1-xSmxO0.5F0.5BiS2 superconductors. More than threefold increase in Tc (10.3 K) is observed with external pressure (at ~1.74 GPa at a rate of 4.08 K/GPa)) for x = 0.2 c
omposition. There is a concomitant large improvement in the quality of the superconducting transition. Beyond this pressure Tc decreases monotonously at the rate of -2.09 K/GPa. In the x = 0.8 sample, we do not observe any enhancement in Tc with application of pressure (up to 1.76 GPa). The semiconducting behavior observed in the normal state resistivity of both of the samples is significantly subdued with the application of pressure which, if interpreted invoking thermal activation process, implies that the activation energy gap of the carriers is significantly reduced with pressure. We believe these observations should generate further interest in the La1-xSmxO0.5F0.5BiS2 superconductors.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها