The transport properties, upper critical fields, superconducting anisotropy, and critical current density in an iso-valent phosphorus-doped BaFe2As2 single crystal close to optimum doping are investigated in this report. Temperature dependent resistivity and susceptibility show a superconducting transition temperature, Tc, just below 31 K both with sharp transitions. The upper critical field parallel to the ab-plane, Hc2^ab, is above 77 Tesla while that along the c-axis direction, Hc2^c, is just above 36 Tesla, yielding a low superconducting anisotropy ratio ~ 2. The estimated inter-plane coherence length based on the Ginzburg-Landau (G-L) theory indicates BaFe2(As0.68P0.32)2 is still above the point for a dimensional crossover inferring the superconducting layers are not weakly-coupled in this system. The critical current density at 5 K obtained from magnetization loops measurement show a modest Jc as high as 10^5 A/cm2.
قيم البحث
اقرأ أيضاً
We present measurements of the resistivity and the upper critical field H_c2 of Nd(O_0.7F_0.3)FeAs single crystals in strong DC and pulsed magnetic fields up to 45 T and 60 T, respectively. We found that the field scale of H_c2 is comparable to ~100
T of high T_c cuprates. H_c2(T) parallel to the c-axis exhibits a pronounced upward curvature similar to what was extracted from earlier measurements on polycrystalline samples. Thus this behavior is indeed an intrinsic feature of oxypnictides, rather than manifestation of vortex lattice melting or granularity. The orientational dependence of H_c2 shows deviations from the one-band Ginzburg-Landau scaling. The mass anisotropy decreases as T decreases, from 9.2 at 44K to 5 at 34K. Spin dependent magnetoresistance and nonlinearities in the Hall coefficient suggest contribution to the conductivity from electron-electron interactions modified by disorder reminiscent that of diluted magnetic semiconductors. The Ohmic resistivity measured below T_c but above the irreversibility field exhibits a clear Arrhenius thermally activated behavior over 4-5 decades. The activation energy has very different field dependencies for H||ab and Hperp ab. We discuss to what extent different pairing scenarios can manifest themselves in the observed behavior of H_{c2}, using the two-band model of superconductivity. The results indicate the importance of paramagnetic effects on H_c2(T),which may significantly reduce H_c2(0) as compared toH_c2(0)~200-300 T based on extrapolations of H_c2(T) near T_c down to low temperatures.
Superconductivity of Ca1-xLaxFe2As2 single crystals with various doping level were investigated via electromagnetic measurements for out-plane (H//c) and in-plane (H//ab) directions. Obvious double superconducting transitions, which can survive in ma
gnetic fields up to several Tesla, were observed in the medium-doped (x = 0.13) sample. Two kinds of distinct Hc2 phase diagrams were established for the low superconducting phase with Tc lower than 15 K and the high superconducting phase with Tc of over 40 K, respectively. Both the two kinds of phase diagrams exist in the medium-doped sample. Unusual upward curvature near Tc was observed in Hc2 phase diagrams and analyzed in detail. Temperature dependences of anisotropy for different doping concentrations were obtained and compared. Both superconducting phases manifest extremely large anisotropies, which may originate from the interface or intercalation superconductivity.
We report the results of an experimental study of dc and low frequencies magnetic properties of K$_{0.8}$Fe$_{2}$Se$_2$ single crystal when the dc magnetic field is applied parallel to the $bf{ab}$ plane. From the data obtained, we deduce the full H-
T phase diagram which consists of all three H$_{c1}$(T), H$_{c2}(T)$ and H$_{c3}(T)$ critical magnetic field plots. The two H$_{c1}$(T) and H$_{c2}$(T) curves were obtained from dc magnetic measurements, whereas the surface critical field H$_{c3}$(T) line was extracted by ac susceptibility studies. It appears that near T$_c$, the H$_{c3}$(T)/H$_{c2}$(T) ratio is $approx 4.4$ which is much larger than expected.
We study the effect of 100 MeV Silicon and 200 MeV Gold ion irradiation on the inter and intra grain properties of superconducting thin films of Magnesium Diboride. Substantial decrease in inter-grain connectivity is observed, depending on irradiatio
n dose and type of ions used. We establish that modification of sigma band scattering mechanism, and consequently the upper critical field and anisotropy, depends on the size and directional properties of the extrinsic defects. Post heavy ion irradiation, the upper critical field shows enhancement at a defect density that is five orders of magnitude less compared to neutron irradiation. The critical current density however is best improved through light ion irradiation.
In this report, we comprehensively study the effect of H$^+$ irradiation on the critical current density, $J_c$, and vortex pinning in FeSe single crystal. It is found that the value of $J_c$ for FeSe is enhanced more than twice after 3-MeV H$^+$ irr
adiation. The scaling analyses of the vortex pinning force based on the Dew-Hughes model reveal that the H$^+$ irradiation successfully introduce point pinning centers into the crystal. We also find that the vortex creep rates are strongly suppressed after irradiation. Detailed analyses of the critical current dependent pinning energy based on the collective creep theory and extend Maleys method show that the H$^+$ irradiation enhances the value of $J_c$ before the flux creep, and also reduces the size of flux bundle, which will further reduce the field dependence of $J_c$ due to vortex motion.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها