Six-fold configurational anisotropy was studied in Permalloy triangles, in which the shape symmetry order yields two energetically non-degenerate micromagnetic configurations of the spins, the so-called Y and buckle states. A twelve pointed switching astroid was measured using magneto-optical experiments and successfully reproduced numerically, with different polar quadrants identified as specific magnetic transitions, thereby giving a comprehensive view of the magnetic reversal in these structures. A detailed analysis highlighted the necessity to include the physical rounding of the structures in the simulations to account for the instability of the Y state.
قيم البحث
اقرأ أيضاً
Transition metal dichalcogenides (TMDs) are promising materials for efficient generation of current-induced spin-orbit torques on an adjacent ferromagnetic layer. Numerous effects, both interfacial and bulk, have been put forward to explain the diffe
rent torques previously observed. Thus far, however, there is no clear consensus on the microscopic origin underlying the spin-orbit torques observed in these TMD/ferromagnet bilayers. To shine light on the microscopic mechanisms at play, here we perform thickness dependent spin-orbit torque measurements on the semiconducting WSe$_{2}$/permalloy bilayer with various WSe$_{2}$ layer thickness, down to the monolayer limit. We observe a large out-of-plane field-like torque with spin-torque conductivities up to $1times10^4 ({hbar}/2e) ({Omega}m)^{-1}$. For some devices, we also observe a smaller in-plane antidamping-like torque, with spin-torque conductivities up to $4times10^{3} ({hbar}/2e) ({Omega}m)^{-1}$, comparable to other TMD-based systems. Both torques show no clear dependence on the WSe$_{2}$ thickness, as expected for a Rashba system. Unexpectedly, we observe a strong in-plane magnetic anisotropy - up to about $6.6times10^{4} erg/cm^{3}$ - induced in permalloy by the underlying hexagonal WSe$_{2}$ crystal. Using scanning transmission electron microscopy, we confirm that the easy axis of the magnetic anisotropy is aligned to the armchair direction of the WSe$_{2}$. Our results indicate a strong interplay between the ferromagnet and TMD, and unveil the nature of the spin-orbit torques in TMD-based devices. These findings open new avenues for possible methods for optimizing the torques and the interaction with interfaced magnets, important for future non-volatile magnetic devices for data processing and storage.
Unconventional fermions, such as three-fold, four-fold, six-fold, and eight-fold fermions have attracted intense attention in recent years. However, the concrete materials hosting unconventional fermions are still in urgent scarcity. In this work, ba
sed first-principle calculations and symmetry analysis, we reveal rich unconventional fermions in existing compound Re2C3 (Re = Y, La, Ce, Pr, Nd, Sm, Tb, Dy, Ho, Er, Tm, Yb, Lu). We show that these compounds host quadratic dispersive three-fold (TP), linear dispersive four-fold (FP) and six-fold points (SP) near the Fermi level in their electric band structures when spin-orbital coupling (SOC) is not included. Notably, the FP is charge-2 Dirac-like point. More importantly, among compound Re2C3, the compound Yb2C3 has very clean band structure, and its unconventional fermions are closed to the Fermi level. We also find that a uniaxial strain can transform the unconventional fermions into other types fermions, depending on the directions of strain. When SOC is considered, a SP transform to an eightfold degenerate point and a fourfold degenerate point. Overall, our work provides a family of realistic materials to study the unconventional fermions.
Atomic Force Microscopy and Grazing incidence X-ray diffraction measurements have revealed the presence of ripples aligned along the $[1bar{1}0]$ direction on the surface of (Ga,Mn)As layers grown on GaAs(001) substrates and buffer layers, with perio
dicity of about 50 nm in all samples that have been studied. These samples show the strong symmetry breaking uniaxial magnetic anisotropy normally observed in such materials. We observe a clear correlation between the amplitude of the surface ripples and the strength of the uniaxial magnetic anisotropy component suggesting that these ripples might be the source of such anisotropy.
Transport and magnetic properties of LSMO manganite thin films and bicrystal junctions were investigated. Manganite films were epitaxially grown on STO, LAO, NGO and LSAT substrates and their magnetic anisotropy were determined by two techniques of m
agnetic resonance spectroscopy. Compare with cubic substrates a small (about 0.3 persentage), the anisotropy of the orthorhombic NGO substrate leads to a uniaxial anisotropy of the magnetic properties of the films in the plane of the substrate. Samples with different tilt of crystallographic basal planes of manganite as well as bicrystal junctions with rotation of the crystallographic axes (RB - junction) and with tilting of basal planes (TB - junction) were investigated. It was found that on vicinal NGO substrates the value of magnetic anisotropy could be varied by changing the substrate inclination angle from 0 to 25 degrees. Measurement of magnetic anisotropy of manganite bicrystal junction demonstrated the presence of two ferromagnetically ordered spin subsystems for both types of bicrystal boundaries RB and TB. The magnitude of the magnetoresistance for TB - junctions increased with decreasing temperature and with the misorientation angle even misorientation of easy axes in the parts of junction does not change. Analysis of the voltage dependencies of bicrystal junction conductivity show that the low value of the magnetoresistance for the LSMO bicrystal junctions can be caused by two scattering mechanisms with the spin- flip of spin - polarized carriers due to the strong electron - electron interactions in a disordered layer at the bicrystal boundary at low temperatures and the spin-flip by anti ferromagnetic magnons at high temperatures.
Magnetic-domain structure and dynamics play an important role in understanding and controlling the magnetic properties of two-dimensional magnets, which are of interest to both fundamental studies and applications[1-5]. However, the probe methods bas
ed on the spin-dependent optical permeability[1,2,6] and electrical conductivity[7-10] can neither provide quantitative information of the magnetization nor achieve nanoscale spatial resolution. These capabilities are essential to image and understand the rich properties of magnetic domains. Here, we employ cryogenic scanning magnetometry using a single-electron spin of a nitrogen-vacancy center in a diamond probe to unambiguously prove the existence of magnetic domains and study their dynamics in atomically thin CrBr$_3$. The high spatial resolution of this technique enables imaging of magnetic domains and allows to resolve domain walls pinned by defects. By controlling the magnetic domain evolution as a function of magnetic field, we find that the pinning effect is a dominant coercivity mechanism with a saturation magnetization of about 26~$mu_B$/nm$^2$ for bilayer CrBr$_3$. The magnetic-domain structure and pinning-effect dominated domain reversal process are verified by micromagnetic simulation. Our work highlights scanning nitrogen-vacancy center magnetometry as a quantitative probe to explore two-dimensional magnetism at the nanoscale.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها