We report a study in which the effect of defects/impurities, growth process, off-stoichiometry, and presence of impurity phases on the superconducting properties of noncentrosymmetric CePt3Si is analysed by means of the temperature dependence of the magnetic penetration depth. We found that the linear low-temperature response of the penetration depth -indicative of line nodes in this material- is robust regarding sample quality, in contrast to what is observed in unconventional centrosymmetric superconductors with line nodes. We discuss evidence that the broadness of the superconducting transition may be intrinsic, though not implying the existence of a second superconducting transition. The superconducting transition temperature systematically occurs around 0.75 K in our measurements, in agreement with resistivity and ac magnetic susceptibility data but in conflict with specific heat, thermal conductivity and NMR data in which Tc is about 0.5 K. Random defects do not change the linear low-temperature dependence of the penetration depth in the heavy-fermion CePt3Si with line nodes, as they do in unconventional centrosymmetric superconductors with line nodes.
قيم البحث
اقرأ أيضاً
We report the measurements of the $^{29}$Si Knight shift $^{29}K$ on the noncentrosymmetric heavy-fermion compound CePt$_{3}$Si in which antiferromagnetism (AFM) with $T_{rm N}=2.2$ K coexists with superconductivity (SC) with $T_{c}=0.75$ K. Its spin
part $^{29}K_{rm s}$, which is deduced to be $K_{rm s}^{c}ge 0.11$ and 0.16% at respective magnetic fields $H=2.0061$ and 0.8671 T, does not decrease across the superconducting transition temperature $T_{c}$ for the field along the c-axis. The temperature dependence of nuclear spin-lattice relaxation of $^{195}$Pt below $T_{c}$ has been accounted for by a Cooper pairing model with a two-component order parameter composed of spin-singlet and spin-triplet pairing components. From this result, it is shown that the Knight-shift data are consistent with the occurrence of the two-component order parameter for CePt$_{3}$Si.
Combining multiple emergent correlated properties such as superconductivity and magnetism within the topological matrix can have exceptional consequences in garnering new and exotic physics. Here, we study the topological surface states from a noncen
trosymmetric $alpha$-BiPd superconductor by employing angle-resolved photoemission spectroscopy (ARPES) and first principle calculations. We observe that the Dirac surface states of this system have several interesting and unusual properties, compared to other topological surface states. The surface state is strongly anisotropic and the in-plane Fermi velocity varies rigorously on rotating the crystal about the $y$-axis. Moreover, it acquires an unusual band gap as a function of $k_y$, possibly due to hybridization with bulk bands, detected upon varying the excitation energy. Coexistence of all the functional properties, in addition to the unusual surface state characteristics make this an interesting material.
We report on measurements of the temperature dependence of the magnetic penetration depth of a very high quality single crystal of nonmagnetic superconductor LaPt3Si without inversion symmetry. The results are compared with those previously reported
for the isostructural antiferromagnetic superconductor CePt3Si. At low temperatures, the penetration depth follows a BCS exponential behavior that implies an isotropic energy gap in LaPt3Si, in contrast to a linear response that indicates line nodes in CePt3Si. These line nodes have been argued to be protected by symmetry or accidentally generated by parity mixing. The present results provide support for the viewpoint that parity mixing alone does not seem to lead to unconventionality in CePt3Si and that it requires the antiferromagnetic order to be included.
Recent superconducting transition temperatures (Tc) over 100 K for monolayer FeSe on SrTiO3 have renewed interest in the bulk parent compound. In KCl:AlCl3 flux-transport-grown crystals of FeSe0.94Be0.06, FeSe0.97Be0.03 and, for comparison, FeSe, thi
s work reports doping of FeSe using Be, among the smallest of possible dopants, corresponding to an effective chemical pressure. According to lattice parameter measurements, 6% Be doping shrank the tetragonal FeSe lattice equivalent to a physical pressure of 0.75 GPa. Using this flux-transport method of sample preparation, 6% of Be was the maximum amount of dopant achievable. At this maximal composition of FeSe0.94Be0.06, the lattice unit cell shrinks by 2.4%, Tc - measured in the bulk via specific heat - increases by almost 10%, the Tc vs pressure behavior shifts its peak Tconset downwards by ~1 GPa, the high temperature structural transition around TS = 89 K increases by 1.9 K (in contrast to other dopants in FeSe which uniformly depress TS), and the low temperature specific heat gamma increases by 10 % compared to pure FeSe. Also, upon doping by 6% Be the residual resistivity ratio, rho(300K)/rho(T->0), increases by almost a factor of four, while rho(300K)/rho(T=Tc+) increases by 50%.
We report on novel antiferromagnetic (AFM) and superconducting (SC) properties of noncentrosymmetric CePt3Si through measurements of the 195Pt nuclear spin-lattice relaxation rate 1/T_1. In the normal state, the temperature (T) dependence of 1/T1 unr
aveled the existence of low-lying levels in crystal-electric-field multiplets and the formation of a heavy fermion (HF) state. The coexistence of AFM and SC phases, that emerge at TN = 2.2 K and Tc = 0.75 K, respectively, takes place on a microscopic level. CePt3Si is the first HF superconductor that reveals a peak in 1/T1 just below Tc and, additionally, does not follow the T^3 law that used to be reported for most unconventional HF superconductors. We remark that this unexpected SC characteristics may be related with the lack of an inversion center in its crystal structure.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها