تسجيل مستخدم جديدFew-layer flakes of Molybdenum Disulphide produced by anodic arc discharge in pulsed mode
548
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Here, the synthesis of Molybdenum Disulphide (MoS2) flakes by means of anodic atmospheric arc discharge is reported for the first time. The vertical electrode configuration consisted of a compound anode (hollow graphite anode filled with MoS2 powder) and a solid graphite cathode placed just above of the compound anode. Arc processes were operated in pulsed mode to preferentially evaporate the powder component from the anode and to minimize Carbon ablation. Pulsed anodic arc discharges were conducted at 2 Hz and 10% duty cycle in 300 Torr of Helium with a peak current of 250-300 A and peak voltage of 35 V. A probe made of Tungsten wire was placed in the vicinity of the arc column to collect the evaporated material. The measured thickness profile was correlated to the particle flux distribution and it was fitted by a simple model of plasma expansion. During pulse phase, electron density was estimated around 5E22 m-3 or higher, and ion current density was of the order of 10 A/mm2. Morphology, structure and composition of the samples were characterized by Raman spectroscopy, atomic force microscopy (AFM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and x-ray diffraction (XRD). The study shows that pulsed arc discharge of the compound anode leads to moderate C deposition combined with MoS2 deposition in the form of fragmented nanocrystals and few atomic monolayers of MoS2. Such synthesis technique is promising to produce new 2D nanomaterials with tailored structure and functionality thanks to the flexibility of pulsed power.
قيم البحث
اقرأ أيضاً
Gallium selenide (GaSe) is one of layered group-III metal monochalcogenides, which has an indirect bandgap in monolayer and direct bandgap in bulk unlike other conventional transition metal dichalcogenides (TMDs) such as MoX2 and WX2 (X=S and Se). Fo
ur polytypes of bulk GaSe, designated as beta-, epsilon-, gamma-, and delta-GaSe, have been reported. Since different polytypes result in different optical and electrical properties even for the same thickness, identifying the polytype is essential in utilizing this material for various optoelectronic applications. We performed polarized Raman measurement on GaSe and found different ultra-low-frequency Raman spectra of inter-layer vibrational modes even for the same thickness due to different stacking sequences of the polytypes. By comparing the ultra-low-frequency Raman spectra with theoretical calculations and high-resolution electron microscopy measurements, we established the correlation between the ultra-low-frequency Raman spectra and the stacking sequences for trilayer GaSe. We further found that the AB-type stacking is more stable than the AA-type stacking in GaSe.
Polyynes are linear sp-carbon chains of finite length consisting in a sequence of alternated single and triple bonds and displaying appealing optical and electronic properties. A simple, low cost and scalable production technique for polyynes is the
submerged arc discharge (SAD) in liquid, which so far, has been mainly exploited in organic solvents. In this work, we investigated in detail SAD in water as a cheap and non-toxic solvent for the production of polyynes. The role of process parameters such as current (10-25 A) and voltage (20-25 V) in the production yield have been investigated, as well as polyynes stability. Polyynes terminated by hydrogen (CnH2: n=6-16) were identified by High-Performance Liquid Chromatography (HPLC) coupled with UV-Visible absorption spectroscopy and with the support of density functional theory (DFT) calculations. Size-selected polyynes separated by HPLC were analyzed by surface enhanced Raman spectroscopy (SERS). The formation process was monitored by in situ SERS using an immersed fiber-optic Raman probe and employing Ag nanoparticles directly produced in the solution by SAD.
Two-dimensional molybdenum disulphide on graphene grown by chemical vapour deposition is a promising van der Waals system for applications in optoelectronics and catalysis. To extend the fundamental understanding of growth and intrinsic properties of
molybdenum disulphide on graphene, molybdenum disulphide on highly oriented pyrolytic graphite is a suitable model system. Here we show, experimentally and by density-functional-theory calculations, that molybdenum disulphide flakes grow in two orientations. One of the orientations is energetically preferred, the other one is rotated by 30 degree. Because of a high energy barrier confirmed by our calculations both orientations are stable at room temperature and their switching can only be forced by external stimuli, i.e. by a scanning tunneling microscope tip. Combined Kelvin probe microscopy and Raman spectroscopy measurements show that the flakes with a typical size of a few hundred nanometers are less doped than the often studied exfoliated molybdenum disulphide single layer.
Micron-thick boron films have been deposited by Pulsed Laser Deposition in vacuum on several substrates at room temperature. The use of high energy pulses (>700 mJ) results in the deposition of smooth coatings with low oxygen uptake even at base pres
sures of 10$^{-4}$ - 10$^{-3}$ Pa. A detailed structural analysis, by X-Ray Diffraction and Raman, allowed to assess the amorphous nature of the deposited films as well as to determine the base pressure that prevents boron oxide formation. In addition the crystallization dynamics has been characterized showing that film crystallinity already improves at relatively low temperatures (800 {deg}C). Elastic properties of the boron films have been determined by Brillouin spectroscopy. Finally, micro-hardness tests have been used to explore cohesion and hardness of B films deposited on aluminum, silicon and alumina. The reported deposition strategy allows the growth of reliable boron coatings paving the way for their use in many technology fields.
Spark plasma discharges induce vortex rings and a hot gas kernel. We develop a model to describe the late stage of the spark induced flow and the role of the vortex rings in the entrainment of cold ambient gas and the cooling of the hot gas kernel. T
he model is tested in a plasma-induced flow, using density and velocity measurements obtained from simultaneous stereoscopic particle image velocimetry (S-PIV) and background oriented schlieren (BOS). We show that the spatial distribution of the hot kernel follows the motion of the vortex rings, whose radial expansion increases with the electrical energy deposited during the spark discharge. The vortex ring cooling model establishes that entrainment in the convective cooling regime is induced by the vortex rings and governs the cooling of the hot gas kernel, and the rate of cooling increases with the electrical energy deposited during the spark discharge.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها