Linear thermal expansion coefficient (LTEC) of single crystal k-(D4-BEDT-TTF)2Cu[N(CN)2]Br was studied across the crystal layers in the temperature range 2-290 K using the method of precise capacitive dilatometry. Below Tc = 11,6 K the LTEC of the sample had a small negative value, which is apparently due to the transition from the paramagnetic metal in the superconducting state. There was a bend of temperature dependence of the LTEC, which shows broad peak around 40 K and can be attributed to the elastic lattice anomaly around the end-point of Mott boundary. A sharp jump in the LTEC values and hysteresis was observed in the area of Tg ~ 75-77 K, what is likely explained by the transition in a glass-like state. The isotope effect in the thermal expansion is discusses, which manifested itself in a shift of the phase transitions in comparison with fully deuterated BEDT-TTF sample.
قيم البحث
اقرأ أيضاً
The interplane optical spectrum of the organic superconductor kappa-(BEDT-TTF)2Cu[N(CN)2]Br was investigated in the frequency range from 40 to 40,000 cm-1. The optical conductivity was obtained by Kramers-Kronig analysis of the reflectance. The absen
ce of a Drude peak at low frequency is consistent with incoherent conductivity but in apparent contradiction to the metallic temperature dependence of the DC resistivity. We set an upper limit to the interplane transfer integral of tb = 0.1 meV. A model of defect-assisted interplane transport can account for this discrepancy. We also assign the phonon lines in the conductivity to the asymmetric modes of the ET molecule.
We report high-sensitivity AC susceptibility measurements of the penetration depth in the Meissner state of the layered organic superconductor kappa-(BEDT-TTF)2Cu[N(CN)2]Br. We have studied nominally pure single crystals from the two different synthe
ses and employed controlled cooling procedures in order to minimize intrinsic remnant disorder at low temperatures associated with the glass transition, caused by ordering of the ethylene moieties in BEDT-TTF molecule at T_G = 75 K. We find that the optimal cooling procedures (slow cooling of -0.2 K/h or annealing for 3 days in the region of T_G) needed to establish the ground state, depend critically on the sample origin indicating different relaxation times of terminal ethylene groups. We show that, in the ground state, the behavior observed for nominally pure single crystals from both syntheses is consistent with unconventional d-wave order parameter. The in-plane penetration depth lambda_in(T) is strongly linear, whereas the out-of-plane component lambda_out(T) varies as T^2. In contrast, the behavior of single crystals with long relaxation times observed after slow (-0.2 K/h) cooling is as expected for a d-wave superconductor with impurities (i.e. lambda_in(T) propto lambda_out(T) propto T^2) or might be also reasonably well described by the s-wave model. Our results might reconcile the contradictory findings previously reported by different authors.
Static susceptibility of kappa-[(BEDT-TTF)1-x(BEDSe-TTF)x]2Cu[N(CN)2]Br alloys with the BEDSe-TTF content near the border-line of ambient pressure superconductivity (x~0.3) has been measured as a function of temperature, magnetic field, and pressure.
A non-monotonic pressure dependence is observed for both the superconducting critical temperature and superconducting volume fraction, with both quantities showing growth under pressure in the initial pressure range P < 0.3 kbar. The results are discussed in comparison with the data on the related kappa-phase BEDT-TTF superconductors in which not a cation but anion sublattice is modified by alloying, namely the family kappa-(BEDT-TTF)2Cu[N(CN)2]Cl1-xBrx. PACS numbers: 74.62.Fj, 74.70.Kn.
The effect of disorder on the electronic properties near the Mott transition is studied in an organic superconductor $kappa$-(BEDT-TTF)$_{2}$Cu[N(CN)$_{2}$]Br, which is systematically irradiated by X-ray. We observe that X-ray irradiation causes Ande
rson-type electron localization due to molecular disorder. The resistivity at low temperatures demonstrates variable range hopping conduction with Coulomb interaction. The experimental results show clearly that the electron localization by disorder is enhanced by the Coulomb interaction near the Mott transition.
The magnetic field effect on the phase diagram of the organic Mott system $kappa$-(BEDT-TTF)$_{2}$Cu[N(CN)$_{2}$]Br in which the bandwidth was tuned by the substitution of deuterated molecules was studied by means of the resistivity measurements perf
ormed in magnetic fields. The lower critical point of the first-order Mott transition, which ended on the upper critical field $H_{rm c2}$-temperature plane of the superconductivity, was determined experimentally in addition to the previously observed upper critical end point. The lower critical end point moved to a lower temperature with the suppression of $T_{rm c}$ in magnetic fields and the Mott transition recognized so far as the $S$-shaped curve reached $T =$ 0 when $H > H_{rm c2}$ in the end.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها