We report a high-pressure transport study of the upper-critical field, $B_{c2}(T)$, of the topological superconductor Sr$_{0.15}$Bi$_2$Se$_3$ ($T_c = 3.0$ K). $B_{c2}(T)$ was measured for magnetic fields directed along two orthogonal directions, $a$ and $a^*$, in the trigonal basal plane. While superconductivity is rapidly suppressed at the critical pressure $p_c sim 3.5$ GPa, the pronounced two-fold basal-plane anisotropy $B_{c2}^a/B_{c2}^{a^*} = 3.2$ at $T=0.3$ K, recently reported at ambient pressure (Pan et al., 2016), is reinforced and attains a value of $sim 5$ at the highest pressure (2.2 GPa). The data reveal that the unconventional superconducting state with broken rotational symmetry is robust under pressure.
قيم البحث
اقرأ أيضاً
We report transverse-field (TF) muon spin rotation experiments on single crystals of the topological superconductor Sr$_x$Bi$_2$Se$_3$ with nominal concentrations $x=0.15$ and $0.18$ ($T_c sim 3$ K). The TF spectra ($B= 10$ mT), measured after coolin
g to below $T_c$ in field, did not show any additional damping of the muon precession signal due to the flux line lattice within the experimental uncertainty. This puts a lower bound on the magnetic penetration depth $lambda geq 2.3 ~mu$m. However, when we induce disorder in the vortex lattice by changing the magnetic field below $T_c$ a sizeable damping rate is obtained for $T rightarrow 0$. The data provide microscopic evidence for a superconducting volume fraction of $sim 70~ %$ in the $x=0.18$ crystal and thus bulk superconductivity.
The superconductor TmNi2B2C possesses a significant four-fold basal plane anisotropy, leading to a square Vortex Lattice (VL) at intermediate fields. However, unlike other members of the borocarbide superconductors, the anisotropy in TmNi2B2C appears
to decrease with increasing field, evident by a reentrance of the square VL phase. We have used Small Angle Neutron Scattering measurements of the VL to study the field dependence of the anisotropy. Our results provide a direct, quantitative measurement of the decreasing anisotropy. We attribute this reduction of the basal plane anisotropy to the strong Pauli paramagnetic effects observed in TmNi2B2C and the resulting expansion of vortex cores near Hc2.
The superconducting parameters and upper critical field of the noncentrosymmetric superconductor BiPd have proven contentious. This material is of particular interest because it is a singular example of a $4f$-electron-free noncentrosymmetric superco
nductor of which crystals may be grown and cleaved, enabling surface-sensitive spectroscopies. Here, using bulk probes augmented by tunnelling data on defects, we establish that the lower of the previously reported upper critical fields corresponds to the bulk transition. The material behaves as a nearly-weak-coupled BCS s-wave superconductor, and we report its superconducting parameters as drawn from the bulk upper critical field. Possible reasons behind the order-of-magnitude discrepancy in the reported upper critical fields are discussed.
We studied the anisotropy of the superconducting upper critical field $H_{rm c2}$ in the heavy-fermion superconductor UTe$_2$ under hydrostatic pressure by magnetoresistivity measurements. In agreement with previous experiments we confirm that superc
onductivity disappears near a critical pressure $p_{rm c} approx 1.5$~GPa, and a magnetically ordered state appears. The unusual $H_{rm c2}(T)$ at low temperatures for $H parallel a$ suggests that the multiple superconducting phases which appear under pressure have quite different $H_{rm c2}$. For a field applied along the hard magnetization $b$ axis $H_{rm c2} (0)$ is glued to the metamagnetic transition $H_{rm m}$ which is suppressed near $p_{rm c}$. The suppression of $H_{rm m}$ with pressure follows the decrease of temperature $T_{chi}^{rm max}$, at the maximum in the susceptibility along $b$. The strong reinforcement of $H_{rm c2}$ at ambient pressure for $H parallel b$ above 16~T is rapidly suppressed under pressure due to the increase of $T_{rm sc}$ and the decrease of $H_{rm m}$. The change in the hierarchy of the anisotropy of $H_{rm c2}(0)$ on approaching $p_{rm c}$ points out that the $c$ axis becomes the hard magnetization axis.
We have carried out high-field resistivity measurements up to 27,T in EuFe$_2$As$_2$ at $P$,=,2.5,GPa, a virtually optimal pressure for the $P$-induced superconductivity, where $T_mathrm{c}$,=,30,K. The $B_mathrm{c2}-T_mathrm{c}$ phase diagram has be
en constructed in a wide temperature range with a minimum temperature of 1.6 K ($approx 0.05 times T_mathrm{c}$), for both $B parallel ab$ ($B_mathrm{c2}^mathrm{ab}$) and $B parallel c$ ($B_mathrm{c2}^mathrm{c}$). The upper critical fields $B_mathrm{c2}^mathrm{ab}$(0) and $B_mathrm{c2}^mathrm{c}$(0), determined by the onset of resistive transitions, are 25 T and 22 T, respectively, which are significantly smaller than those of other Fe-based superconductors with similar values of $T_mathrm{c}$. The small $B_mathrm{c2}(0)$ values and the $B_mathrm{c2}(T)$ curves with positive curvature around 20 K can be explained by a multiple pair-breaking model that includes the exchange field due to the magnetic Eu$^{2+}$ moments. The anisotropy parameter, $Gamma=B_mathrm{c2}^{ab}/B_mathrm{c2}^{c}$, in EuFe$_2$As$_2$ at low temperatures is comparable to that of other 122 Fe-based systems.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها