We report a study of the relaxation time of the restoration of the resistive superconducting state in single crystalline boron-doped diamond using amplitude-modulated absorption of (sub-)THz radiation (AMAR). The films grown on an insulating diamond substrate have a low carrier density of about 2.5x10^{21} cm^{-3} and a critical temperature of about 2 K. By changing the modulation frequency we find a high-frequency rolloff which we associate with the characterstic time of energy relaxation between the electron and the phonon systems or the relaxation time for nonequilibrium superconductivity. Our main result is that the electron-phonon scattering time varies clearly as T^{-2}, over the accessible temperature range of 1.7 to 2.2 K. In addition, we find, upon approaching the critical temperature T_c, evidence for an increasing relaxation time on both sides of T_c.
Boron-doped diamond granular thin films are known to exhibit superconductivity with an optimal critical temperature of Tc = 7.2K. Here we report the measured complex surface impedance of Boron-doped diamond films in the microwave frequency range usin
Superconductivity of boron-doped diamond, reported recently at T_c=4 K, is investigated exploiting its electronic and vibrational analogies to MgB2. The deformation potential of the hole states arising from the C-C bond stretch mode is 60% larger tha
Diamond is an excellent band insulator. However, boron (B) doping is known to induce superconductivity. We present two interesting effects in superconducting B doped diamond (BDD) thin films: i) Wohlleben effect (paramagnetic Meissner effect, PME) an
This work investigates the high-pressure structure of freestanding superconducting ($T_{c}$ = 4.3,K) boron doped diamond (BDD) and how it affects the electronic and vibrational properties using Raman spectroscopy and x-ray diffraction in the 0-30,GPa
We report on the direct measurement of the electron-phonon relaxation time, {tau}eph, in disordered TiN films. Measured values of {tau}eph are from 5.5 ns to 88 ns in the 4.2 to 1.7 K temperature range and consistent with a T-3 temperature dependence