Unusually high critical current of clean P-doped BaFe2As2 single crystalline thin film

188   0   0.0 ( 0 )
 نشر من قبل Fritz Kurth
 تاريخ النشر 2015
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

Microstructura lly clean, isov alently P-doped BaFe2As2 (Ba-122) single crystalline thin films have been prepared on MgO (001) substrates by molecular beam epitaxy. These films show a superconducting transition temperature (Tc) of over 30 K although P content is around 0.22, which is lower than the optimal one for single crystals (i.e., 0.33). The enhanced Tc at this doping level is attributed to the in-plane tensile strain. The strained film shows high transport self-field critical current densities (Jc) of over 6 MA/cm2 at 4.2 K, which are among the highest for Fe based superconductors (FeSCs). In-field Jc exceeds 0.1 MA/cm2 at m0H = 35 T for H||ab and m0H = 18 T for H||c at 4.2 K, respectively, in spite of moderate upper critical fields compared to other FeSCs with similar Tc. Structural investigations reveal no defects or misoriented grains pointing to strong pinning centers. We relate this unexpected high Jc to a strong enhancement of the vortex core energy at optimal Tc, driven by in-plane strain and doping. These unusually high Jc make P-doped Ba-122 very favorable for high-field magnet applications.



قيم البحث

اقرأ أيضاً

143 - S. Lee , J. Jiang , C. T. Nelson 2009
Understanding new superconductors requires high-quality epitaxial thin films to explore intrinsic electromagnetic properties, control grain boundaries and strain effects, and evaluate device applications. So far superconducting properties of ferropni ctide thin films appear compromised by imperfect epitaxial growth and poor connectivity of the superconducting phase. Here we report novel template engineering using single-crystal intermediate layers of (001) SrTiO3 and BaTiO3 grown on various perovskite substrates that enables genuine epitaxial films of Co-doped BaFe2As2 with high transition temperature (zero resistivity Tc of 21.5K), small transition widths (delta Tc = 1.3K), superior Jc of 4.5 MA/cm2 (4.2K, self field) and strong c-axis flux pinning. Implementing SrTiO3 or BaTiO3 templates to match the alkaline earth layer in the Ba-122 with the alkaline earth-oxygen layer in the templates opens new avenues for epitaxial growth of ferropnictides on multi-functional single crystal substrates. Beyond superconductors, it provides a framework for growing heteroepitaxial intermetallic compounds on various substrates by matching interfacial layers between templates and thin film overlayers.
For any practical superconductor the magnitude of the critical current density, $J_textrm{c}$, is crucially important. It sets the upper limit for current in the conductor. Usually $J_textrm{c}$ falls rapidly with increasing external magnetic field b ut even in zero external field the current flowing in the conductor generates a self-field which limits $J_textrm{c}$. Here we show for thin films of thickness less than the London penetration depth, $lambda$, this limiting $J_textrm{c}$ adopts a universal value for all superconductors - metals, oxides, cuprates, pnictides, borocarbides and heavy Fermions. For type I superconductors, it is $H_{textrm{c}}/lambda$ where $H_textrm{c}$ is the thermodynamic critical field. But surprisingly for type II superconductors we find the self-field $J_textrm{c}$ is $H_{textrm{c}1}/lambda$ where $H_{textrm{c}1}$ is the lower critical field. $J_textrm{c}$ is thus fundamentally determined and this provides a simple means to extract absolute values of $lambda(T)$ and, from its temperature dependence, the symmetry and magnitude of the superconducting gap.
128 - C. Tarantini , S. Lee , Y. Zhang 2010
We report measurements of the field and angular dependences of Jc of truly epitaxial Co-doped BaFe2As2 thin films grown on SrTiO3/(La,Sr)(Al,Ta)O3 with different SrTiO3 template thicknesses. The films show Jc comparable to Jc of single crystals and a maximum pinning force Fp(0.6Tc) > 5 GN/m3 at H/Hirr ~ 0.5 indicative of strong vortex pinning effective up to high fields. Due to the strong correlated c-axis pinning, Jc for field along the c-axis exceeds Jc for H//ab plane, inverting the expectation of the Hc2 anisotropy. HRTEM reveals that the strong vortex pinning is due to a high density of nanosize columnar defects.
The mixed-state Hall effect was examined in a Ba(Fe1-xCox)2As2 epitaxial film with a high critical current density. The transverse resistivity {rho}xy and the longitudinal resistivity {rho}xx follow power law scaling {rho}xy = A{rho}xx{beta}. In the temperature-sweep with a fixed field (T sweep), all of the {beta} values are independent of magnetic field up to 9 T, and are lower than 2.0 (around 1.8). In contrast, the {beta} values in the magnetic-field sweep with a fixed temperature (H sweep) change from 1.8 to 2.0 as the temperature increases from 13 to 16 K even in the T/H region that overlaps with the T sweep measurements. These results indicate that the vortices introduced at low temperatures are trapped by strong pinning centers, but a portion of the vortices introduced at high temperatures are not strongly trapped by the pinning centers. The sign of {rho}xy is negative, and a sign reversal is not detected. These distinct scaling behaviors, which sharply contrast cuprates and MgB2, are explained by high-density c-axis pinning centers in the Ba(Fe1-xCox)2As2 epitaxial film and are consistent with a wider vortex liquid phase.
We report on infrared studies of charge dynamics in a prototypical pnictide system: the BaFe2As2 family. Our experiments have identified hallmarks of the pseudogap state in the BaFe2As2 system that mirror the spectroscopic manifestations of the pseud ogap in the cuprates. The magnitude of the infrared pseudogap is in accord with that of the spin-density-wave gap of the parent compound. By monitoring the superconducting gap of both P- and Co-doped compounds, we find that the infrared pseudogap is unrelated to superconductivity. The appearance of the pseudogap is found to correlate with the evolution of the antiferromagnetic fluctuations associated with the spin-density-wave instability. The strong-coupling analysis of infrared data further reveals the interdependence between the magnetism and the pseudogap in the iron pnictides.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا