We report a detailed study of the electric transport and magnetic properties of the LaNdCaMnO manganite system. Substitution of LaIII by smaller NdIII ions, reduces the mean ionic radius of the A site ion. We have studied samples in the entire range between rich La and rich Nd compounds. Results of DC magnetization and resistivity show that doping destabilize the FM character of the pure La compound and triggers the formation of a phase separated state at intermediate doping. We have also found evidence of a dynamical behaviour within the phase separated state. A phase diagram is constructed, summarizing the effect of chemical substitution on the system.
قيم البحث
اقرأ أيضاً
We measured thermal conductivity, k, thermoelectric power, S, and dc electric conductivity, sigma, of La_{5/8-x}Pr_{x}Ca_{3/8}MnO_{3}, showing an intricate interplay between metallic ferromagnetism (FM) and charge ordering (CO) instability. The chang
e of k, S and sigma with temperature (T) and x agrees well with the effective medium theories for binary metal-insulator mixtures. This agreement clearly demonstrates that with the variation of T as well as x, the relative volumes of FM and CO phases drastically change and percolative metal-insulator transition occurs in the mixture of FM and CO domains.
We report on DC and pulsed electric field sensitivity of the resistance of mixed valent Mn oxide based La(5/8-y)Pr(y)Ca(3/8)MnO(3) (y = 0.4) single crystals as a function of temperature. The low temperature regime of the resistivity is highly current
and voltage dependent. An irreversible transition from high (HR) to a low resistivity (LR) is obtained upon the increase of the electric field up to a temperature dependent critical value (V_c). The current-voltage characteristics in the LR regime as well as the lack of a variation in the magnetization response when V_c is reached indicate the formation of a non-single connected filamentary conducting path. The temperature dependence of V_c indicates the existence of a consolute point where the conducting and insulating phases produce a critical behavior as a consequence of their separation.
We investigate the ultra-sharp jump in the isothermal magnetization and the resistivity in the polycrystalline $Sm_{0.5}(Ca_{0.5-y}Sr_{y})MnO_3$ $(y = 0, 0.1, 0.2, 0.25, 0.3, 0.5)$ compounds. The critical field $(H_{cr})$, required for the ultra-shar
p jump, decreases with increase of `Sr concentration, i.e. with increase of average A-site ionic radius $langle r_Arangle$. The magnetotransport data indicate that the phase separation increases with the increase of $langle r_Arangle$, i.e. with $y$. The dependency of $H_{cr}$ with magnetic field sweep rate reveals that the ultra-sharp jump from antiferromagnetic (AFM) state to the ferromagnetic (FM) state is of martensitic in nature. Our two-band double exchange model Hamiltonian calculations show that the `Sr doping induces the ferromagnetic clusters in the antiferromagnetic insulating phase and in turn reduces the critical field. In the end we present a phenomenological picture obtained from our combined experimental and theoretical study.
$La_{0.7}Ca_{0.3}MnO_3$ samples were prepared in nano- and polycrystalline forms by sol-gel and solid state reaction methods, respectively, and structurally characterized by synchrotron X-ray diffraction. The magnetic properties determined by ac susc
eptibility and dc magnetization measurements are discussed. The magnetocaloric effect in this nanocrystalline manganite is spread over a broader temperature interval than in the polycrystalline case. The relative cooling power of the poly- and nanocrystalline manganites is used to evaluate a possible application for magnetic cooling below room temperature.
We have resolved a controversial issue concerning the oxygen-isotope shift of the ferromagnetic transition temperature T_{C} in the manganite La_{0.8}Ca_{0.2}MnO_{3+y}. We show that the giant oxygen-isotope shift of T_C observed in the normal oxygen-
isotope exchanged samples is indeed intrinsic, while a much smaller shift observed in the argon annealed samples is an artifact. The argon annealing causes the 18O sample to partially exchange back to the 16O isotope due to a small 16O contamination in the Ar gas. Such a contamination is commonly caused by the oxygen outgas that is trapped in the tubes, connectors and valves. The present results thus umambiguously demonstrate that the observed large oxygen isotope effect is an intrinsic property of manganites, and places an important constraint on the basic physics of these materials.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها