تسجيل مستخدم جديدMobility Improvement and Temperature Dependence in MoSe2 Field-Effect Transistors on Parylene-C Substrate
171
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We report low temperature scanning tunneling microscopy characterization of MoSe2 crystals, and the fabrication and electrical characterization of MoSe2 field-effect transistors on both SiO2 and parylene-C substrates. We find that the multilayer MoSe2 devices on parylene-C show a room temperature mobility close to the mobility of bulk MoSe2 (100 cm2V-1s-1 - 160 cm2V-1s-1), which is significantly higher than that on SiO2 substrate (~50 cm2V-1s-1). The room temperature mobility on both types of substrates are nearly thickness independent. Our variable temperature transport measurements reveal a metal-insulator transition at a characteristic conductivity of e2/h. The mobility of MoSe2 devices extracted from the metallic region on both SiO2 and parylene-C increases up to ~ 500 cm2V-1s-1 as the temperature decreases to ~ 100 K, with the mobility of MoSe2 on SiO2 increasing more rapidly. In spite of the notable variation of charged impurities as indicated by the strongly sample dependent low temperature mobility, the mobility of all MoSe2 devices on SiO2 converges above 200 K, indicating that the high temperature (> 200 K) mobility in these devices is nearly independent of the charged impurities. Our atomic force microscopy study of SiO2 and parylene-C substrates further rule out the surface roughness scattering as a major cause of the substrate dependent mobility. We attribute the observed substrate dependence of MoSe2 mobility primarily to the surface polar optical phonon scattering originating from the SiO2 substrate, which is nearly absent in MoSe2 devices on parylene-C substrate.
قيم البحث
اقرأ أيضاً
We report the fabrication of back-gated field-effect transistors (FETs) using ultra-thin, mechanically exfoliated MoSe2 flakes. The MoSe2 FETs are n-type and possess a high gate modulation, with On/Off ratios larger than 106. The devices show asymmet
ric characteristics upon swapping the source and drain, a finding explained by the presence of Schottky barriers at the metal contact/MoSe2 interface. Using four-point, back-gated devices we measure the intrinsic conductivity and mobility of MoSe2 as a function of gate bias, and temperature. Samples with a room temperature mobility of ~50 cm2/V.s show a strong temperature dependence, suggesting phonons are a dominant scattering mechanism.
Transition-metal dichalcogenides (TMDCs) are important class of two-dimensional (2D) layered materials for electronic and optoelectronic applications, due to their ultimate body thickness, sizable and tunable bandgap, and decent theoretical room-temp
erature mobility of hundreds to thousands cm2/Vs. So far, however, all TMDCs show much lower mobility experimentally because of the collective effects by foreign impurities, which has become one of the most important limitations for their device applications. Here, taking MoS2 as an example, we review the key factors that bring down the mobility in TMDC transistors, including phonons, charged impurities, defects, and charge traps. We introduce a theoretical model that quantitatively captures the scaling of mobility with temperature, carrier density and thickness. By fitting the available mobility data from literature over the past few years, we are able to obtain the density of impurities and traps for a wide range of transistor structures. We show that interface engineering such as oxide surface passivation, high-k dielectrics and BN encapsulation could effectively reduce the impurities, leading to improved device performances. For few-layer TMDCs, we analytically model the lopsided carrier distribution to elucidate the experimental increase of mobility with the number of layers. From our analysis, it is clear that the charge transport in TMDC samples is a very complex problem that must be handled carefully. We hope that this Review can provide new insights and serve as a starting point for further improving the performance of TMDC transistors.
We utilize an organic polymer buffer layer between graphene and conventional gate dielectrics in top-gated graphene transistors. Unlike other insulators, this dielectric stack does not significantly degrade carrier mobility, allowing for high field-e
ffect mobilities to be retained in top-gate operation. This is demonstrated in both two-point and four-point analysis, and in the high-frequency operation of a graphene transistor. Temperature dependence of the carrier mobility suggests that phonons are the dominant scatterers in these devices.
Atomically-thin two-dimensional (2D) layered transition metal dichalcogenides (TMDs) have been extensively studied in recent years because of their appealing electrical and optical properties. Here, we report on the fabrication of ReS2 field-effect t
ransistors via the encapsulation of ReS2 nanosheets in a high-k{appa} Al2O3 dielectric environment. Low-temperature transport measurements allowed us to observe a direct metal-to-insulator transition originating from strong electron-electron interactions. Remarkably, the photodetectors based on ReS2 exhibit gate-tunable photoresponsivity up to 16.14 A/W and external quantum efficiency reaching 3,168 %, showing a competitive device performance to those reported in graphene, MoSe2, GaS and GaSe-based photodetectors. Our study unambiguously distinguishes ReS2 as a new candidate for future applications in electronics and optoelectronics.
We report the fabrication of both n-type and p-type WSe2 field effect transistors with hexagonal boron nitride passivated channels and ionic-liquid (IL)-gated graphene contacts. Our transport measurements reveal intrinsic channel properties including
a metal-insulator transition at a characteristic conductivity close to the quantum conductance e2/h, a high ON/OFF ratio of >107 at 170 K, and large electron and hole mobility of ~200 cm2V-1s-1 at 160 K. Decreasing the temperature to 77 K increases mobility of electrons to ~330 cm2V-1s-1 and that of holes to ~270 cm2V-1s-1. We attribute our ability to observe the intrinsic, phonon limited conduction in both the electron and hole channels to the drastic reduction of the Schottky barriers between the channel and the graphene contact electrodes using IL gating. We elucidate this process by studying a Schottky diode consisting of a single graphene/WSe2 Schottky junction. Our results indicate the possibility to utilize chemically or electrostatically highly doped graphene for versatile, flexible and transparent low-resistance Ohmic contacts to a wide range of quasi-2D semiconductors. KEYWORDS: MoS2, WSe2, field-effect transistors, graphene, Schottky barrier, ionic-liquid gate