Piezoresistance in Silicon and its nanostructures

94   0   0.0 ( 0 )
 نشر من قبل Alistair Rowe
 تاريخ النشر 2013
  مجال البحث فيزياء
والبحث باللغة English
 تأليف A. C. H. Rowe




اسأل ChatGPT حول البحث

Piezoresistance is the change in the electrical resistance, or more specifically the resistivity, of a solid induced by an applied mechanical stress. The origin of this effect in bulk, crystalline materials like Silicon, is principally a change in the electronic structure which leads to a modification of the charge carriers effective mass. The last few years have seen a rising interest in the piezoresistive properties of semiconductor nanostructures, motivated in large part by claims of a giant piezoresistance effect in Silicon nanowires that is more than two orders of magnitude bigger than the known bulk effect. This review aims to present the controversy surrounding claims and counter-claims of giant piezoresistance in Silicon nanostructures by presenting a summary of the major works carried out over the last 10 years. The main conclusions that can be drawn from the literature are that i) reproducible evidence for a giant piezoresistance effect in un-gated Silicon nanowires is limited, ii) in gated nanowires a giant effect has been reproduced by several authors, iii) the giant effect is fundamentally different from either the bulk Silicon piezoresistance or that due to quantum confinement in accumulation layers and heterostructures, the evidence pointing to an electrostatic origin for the piezoresistance, iv) released nanowires tend to have slightly larger piezoresistance coefficients than un-released nanowires, and v) insufficient work has been performed on bottom-up grown nanowires to be able to rule out a fundamental difference in their properties when compared with top-down nanowires. On the basis of this, future possible research directions are suggested.

قيم البحث

اقرأ أيضاً

The giant piezoresistance (PZR) previously reported in silicon nanowires is experimentally investigated in a large number of surface depleted silicon nano- and micro-structures. The resistance is shown to vary strongly with time due to electron and h ole trapping at the sample surfaces. Importantly, this time varying resistance manifests itself as an apparent giant PZR identical to that reported elsewhere. By modulating the applied stress in time, the true PZR of the structures is found to be comparable with that of bulk silicon.
In this work we report new silicon and germanium tubular nanostructures with no corresponding stable carbon analogues. The electronic and mechanical properties of these new tubes were investigated through ab initio methods. Our results show that the structures have lower energy than their corresponding nanoribbon structures and are stable up to high temperatures (500 and 1000 K, for silicon and germanium tubes, respectively). Both tubes are semiconducting with small indirect band gaps, which can be significantly altered by both compressive and tensile strains. Large bandgap variations of almost 50% were observed for strain rates as small as 3%, suggesting possible applications in sensor devices. They also present high Youngs modulus values (0.25 and 0.15 TPa, respectively). TEM images were simulated to help the identification of these new structures.
A wide variety of apparently contradictory piezoresistance (PZR) behaviors have been reported in p-type silicon nanowires (SiNW), from the usual positive bulk effect to anomalous (negative) PZR and giant PZR. The origin of such a range of diverse phe nomena is unclear, and consequently so too is the importance of a number of parameters including SiNW type (top down or bottom up), stress concentration, electrostatic field effects, or surface chemistry. Here we observe all these PZR behaviors in a single set of nominally p-type, $langle 110 rangle$ oriented, top-down SiNWs at uniaxial tensile stresses up to 0.5 MPa. Longitudinal $pi$-coefficients varying from $-800times10^{-11}$ Pa$^{-1}$ to $3000times10^{-11}$ Pa$^{-1}$ are measured. Micro-Raman spectroscopy on chemically treated nanowires reveals that stress concentration is the principal source of giant PZR. The sign and an excess PZR similar in magnitude to the bulk effect are related to the chemical treatment of the SiNW.
111 - H. Li , A. Thayil , C.T.K. Lew 2020
The steady-state, space-charge-limited piezoresistance (PZR) of defect-engineered, silicon-on-insulator device layers containing silicon divacancy defects changes sign as a function of applied bias. Above a punch-through voltage ($V_t$) corresponding to the onset of a space-charge-limited hole current, the longitudinal $langle 110 rangle$ PZR $pi$-coefficient is $pi approx 65 times 10^{-11}$~Pa$^{-1}$, similar to the value obtained in charge-neutral, p-type silicon. Below $V_t$, the mechanical stress dependence of the Shockley-Read-Hall (SRH) recombination parameters, specifically the divacancy trap energy $E_T$ which is estimated to vary by $approx 30$~$mu$V/MPa, yields $pi approx -25 times 10^{-11}$~Pa$^{-1}$. The combination of space-charge-limited transport and defect engineering which significantly reduces SRH recombination lifetimes makes this work directly relevant to discussions of giant or anomalous PZR at small strains in nano-silicon whose characteristic dimension is larger than a few nanometers. In this limit the reduced electrostatic dimensionality lowers $V_t$ and amplifies space-charge-limited currents and efficient SRH recombination occurs via surface defects. The results reinforce the growing evidence that in steady state, electro-mechanically active defects can result in anomalous, but not giant, PZR.
We report a new approach for progressive and well-controlled downsizing of nanostructures below the 10 nm scale. Low energetic ion beam (Ar+) is used for gentle surface erosion, progressively shrinking the dimensions with ~ 1 nm accuracy. The method enables shaping of nanostructure geometry and polishing the surface. The process is clean room / high vacuum compatible being suitable for various applications. Apart from technological advantages, the method enables study of various size phenomena on the same sample between sessions of ion beam treatment.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا