Crystal and magnetic structures of the $x=0.2$ member of La$_{rm 0.8-x}$Tb$_{rm x}$Ca$_{0.2}$CoO$_3$ perovskite series have been determined from the powder neutron diffraction. Enhancement of the diffraction peaks due to ferromagnetic or cluster glass ordering is observed below $T_C=55$ K. The moments evolve at first on Co sites, and ordering of Ising-type Tb$^{3+}$ moments is induced at lower temperatures by a molecular field due to Co ions. The final magnetic configuration is collinear F$_x$ for cobalt subsystem, while it is canted F$_x$C$_y$ for terbium ions. The rare-earth moments align along local Ising axes within textit{ab}-plane of the orthorhombic $Pbnm$ structure. The behavior in external fields up to $70-90$ kOe has been probed by the magnetization and heat capacity measurements. The dilute terbium ions contribute to significant coercivity and remanence that both steeply increase with decreasing temperature. A remarkable manifestation of the Tb$^{3+}$ Ising character is the observation of a low-temperature region of anomalously large linear term of heat capacity and its field dependence. Similar behaviours are detected also for other terbium dopings $x=0.1$ and 0.3.
قيم البحث
اقرأ أيضاً
Temperature dependence of the X-ray absorption near-edge structure (XANES) spectra at the Pr $L_{3}$- and Tb $L_{3}$-edges was measured for the (Pr$_{1-y}$Tb$_{y})_{0.7}$Ca$_{0.3}$CoO$_{3}$ system, in which a metal-insulator (MI) and spin-state (SS)
transition took place simultaneously at a critical temperature $T_{rm MI}$. A small increase in the valence of the terbium ion was found below $T_{rm MI}$, besides the enhancement of the praseodymium valence; the trivalent states, which are stable at room temperature, change to a 3+/4+ ionic mixture at low temperatures. In particular for the $y$=0.2 sample, the average valence determined at 8 K amounts to 3.03+ and 3.25+ for the Tb and Pr ion, respectively. In analogous (Pr$_{1-y}$RE$_{y})_{0.7}$Ca$_{0.3}$CoO$_{3}$ samples (RE=Sm and Eu), in which the MI-SS transition also took place, no valence shift of the RE ion was detected in the XANES spectra at the RE ion $L_{3}$-edge. The role of the substituted RE ion for the Pr-site on the MI-SS transition is discussed.
The origin of both the Ising chain magnetism and ferroelectricity in Ca$_3$CoMnO$_6$ is studied by $ab$ $initio$ electronic structure calculations and x-ray absorption spectroscopy. We find that Ca$_3$CoMnO$_6$ has the alternate trigonal prismatic Co
$^{2+}$ and octahedral Mn$^{4+}$ sites in the spin chain. Both the Co$^{2+}$ and Mn$^{4+}$ are in the high spin state. In addition, the Co$^{2+}$ has a huge orbital moment of 1.7 $mu_B$ which is responsible for the significant Ising magnetism. The centrosymmetric crystal structure known so far is calculated to be unstable with respect to exchange striction in the experimentally observed $uparrowuparrowdownarrowdownarrow$ antiferromagnetic structure for the Ising chain. The calculated inequivalence of the Co-Mn distances accounts for the ferroelectricity.
The delicate balance between spin-orbit coupling, Coulomb repulsion and crystalline electric field interactions observed in Ir-based oxides is usually manifested as exotic magnetic behavior. Here we investigate the evolution of the exchange coupling
between Co and Ir for partial La substitution by Ca in La$_{2}$CoIrO$_6$. A great advantage of the use of Ca$^{2+}$ as replacement for La$^{3+}$ is the similarity of its ionic radii. Thus, the observed magnetic changes can more easily be associated to electronic variations. A thorough investigation of the structural, electronic and magnetic properties of the La$_{2-x}$Ca$_{x}$CoIrO$_6$ system was carried out by means of synchrotron x-ray powder diffraction, muon spin rotation and relaxation ($mu$SR), AC and DC magnetization, XAS, XMCD, Raman spectroscopy, electrical resistivity and dielectric permittivity. Our XAS results show that up to 25% of Ca substitution at the La site results in the emergence of Co$^{3+}$, possibly in high spin state, while the introduction of larger amount of Ca leads to the increase of Ir valence. The competing magnetic interactions resulting from the mixed valences lead to a coexistence of a magnetically ordered and an emerging spin glass (SG) state for the doped samples. Our $mu$SR results indicate that for La$_{2}$CoIrO$_6$ a nearly constant fraction of a paramagnetic (PM) phase persists down to low temperature, possibly related to the presence of a small amount of Ir$^{3+}$ and to the anti-site disorder at Co/Ir sites. For the doped compounds the PM phase freezes below 30 K, but there is still some dynamics associated with the SG. The dielectric data obtained for the parent compound and the one with 25% of Ca-doping indicate a possible magnetodielectric effect, which is discussed in terms of the electron hopping between the TM ions, the anti-site disorder and the distorted crystalline structure.
The stability of Cr, V, Al carbide MAX phases, materials of interest for a variety of magnetic as well as high temperature applications, has been studied using density-functional-theory first-principles calculations. The enthalpy of mixing predicts t
hese alloys to be unstable towards unmixing at 0 K. The calculations also predict, however, that these phases would be thermally stabilised by configurational entropy at temperatures well below the values used for synthesis. The temperature Ts below which they become unstable is found to be quite sensitive to the presence of magnetic moments on Cr ions, as well as to the materials magnetic order, in addition to chemical order and composition. Allowing for magnetism, the value of Ts for helf V and half Cr with chemically disordered Cr and V atoms, is estimated to be between 516 K and 645 K depending on the level of theory, while, if constrained to spin-paired, Ts drops to 142 K. Antiferromagnetic spin arrangements are found to be favoured at low temperatures, but they are most likely lost at synthesis temperatures, and probably at room temperature as well. However, the combination of antiferromagnetic frustration and configurational disorder should give rise to interesting spin textures at low temperatures.
We have studied a non volatile memory effect in the mixed valent compound La$_{0.5}$Ca$_{0.5}$MnO$_{3}$ induced by magnetic field (H). In a previous work [R.S. Freitas et al., Phys. Rev. B 65 (2002) 104403], it has been shown that the response of thi
s system upon application of H strongly depends on the temperature range, related to three well differentiated regimes of phase separation occurring below 220 K. In this work we compare memory capabilities of the compound, determined following two different experimental procedures for applying H, namely zero field cooling and field cooling the sample. These results are analyzed and discussed within the scenario of phase separation.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها