تسجيل مستخدم جديدThe effect of (NH4)2Sx passivation on the (311)A GaAs surface and its use in AlGaAs/GaAs heterostructure devices
138
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We have studied the efficacy of (NH4)2Sx surface passivation on the (311)A GaAs surface. We report XPS studies of simultaneously-grown (311)A and (100) heterostructures showing that the (NH4)2Sx solution removes surface oxide and sulfidizes both surfaces. Passivation is often characterized using photoluminescence measurements, we show that while (NH4)2Sx treatment gives a 40 - 60 x increase in photoluminescence intensity for the (100) surface, an increase of only 2 - 3 x is obtained for the (311)A surface. A corresponding lack of reproducible improvement in the gate hysteresis of (311)A heterostructure transistor devices made with the passivation treatment performed immediately prior to gate deposition is also found. We discuss possible reasons why sulfur passivation is ineffective for (311)A GaAs, and propose alternative strategies for passivation of this surface.
قيم البحث
اقرأ أيضاً
We have fabricated AlGaAs/GaAs heterostructure devices in which the conduction channel can be populated with either electrons or holes simply by changing the polarity of a gate bias. The heterostructures are entirely undoped, and carriers are instead
induced electrostatically. We use these devices to perform a direct comparison of the scattering mechanisms of two-dimensional (2D) electrons ($mu_textrm{peak}=4times10^6textrm{cm}^2/textrm{Vs}$) and holes ($mu_textrm{peak}=0.8times10^6textrm{cm}^2/textrm{Vs}$) in the same conduction channel with nominally identical disorder potentials. We find significant discrepancies between electron and hole scattering, with the hole mobility being considerably lower than expected from simple theory.
The effect of a lateral electric current on the photoluminescence H-band of an AlGaAs/GaAs heterostructure is investigated. The photoluminescence intensity and optical orientation of electrons contributing to the H-band are studied by means of contin
uous wave and time-resolved photoluminescence spectroscopy and time-resolved Kerr rotation. It is shown that the H-band is due to recombination of the heavy holes localized at the heterointerface with photoexcited electrons attracted to the heterointerface from the GaAs layer. Two lines with significantly different decay times constitute the H-band: a short-lived high-energy one and a long-lived low-energy one. The high-energy line originates from recombination of electrons freely moving along the structure plane, while the low-energy one is due to recombination of donor-bound electrons near the interface. Application of the lateral electric field of ~ 100-200 V/cm results in a quenching of both lines. This quenching is due to a decrease of electron concentration near the heterointerface as a result of a photocurrent-induced heating of electrons in the GaAs layer. On the contrary, electrons near the heterointerface are effectively cooled, so the donors near the interface are not completely empty up to ~ 100 V/cm, which is in stark contrast with the case of bulk materials. The optical spin polarization of the donor-bound electrons near the heterointerface weakly depends on the electric field. Their polarization kinetics is determined by the spin dephasing in the hyperfine fields of the lattice nuclei. The long spin memory time (> 40 ns) can be associated with suppression of the Bir-Aronov-Pikus mechanism of spin relaxation for electrons.
We have studied the origin of switching (telegraph) noise at low temperature in lateral quantum structures defined electrostatically in GaAs/AlGaAs heterostructures by surface gates. The noise was measured by monitoring the conductance fluctuations a
round $e^2/h$ on the first step of a quantum point contact at around 1.2 K. Cooling with a positive bias on the gates dramatically reduces this noise, while an asymmetric bias exacerbates it. We propose a model in which the noise originates from a leakage current of electrons that tunnel through the Schottky barrier under the gate into the doped layer. The key to reducing noise is to keep this barrier opaque under experimental conditions. Bias cooling reduces the density of ionized donors, which builds in an effective negative gate voltage. A smaller negative bias is therefore needed to reach the desired operating point. This suppresses tunnelling from the gate and hence the noise. The reduction in the density of ionized donors also strengthens the barrier to tunneling at a given applied voltage. Support for the model comes from our direct observation of the leakage current into a closed quantum dot, around $10^{-20} mathrm{A}$ for this device. The current was detected by a neighboring quantum point contact, which showed monotonic steps in time associated with the tunneling of single electrons into the dot. If asymmetric gate voltages are applied, our model suggests that the noise will increase as a consequence of the more negative gate voltage applied to one of the gates to maintain the same device conductance. We observe exactly this behaviour in our experiments.
We demonstrate an efficient core-shell GaAs/AlGaAs nanowire photodetector operating at room temperature. The design of this nanoscale detector is based on a type-I heterostructure combined with a metal-semiconductor-metal (MSM) radial architecture, i
n which built-in electric fields at the semiconductor heterointerface and at the metal/semiconductor Schottky contact promote photogenerated charge separation, enhancing photosensitivity. The spectral photoconductive response shows that the nanowire supports resonant optical modes in the near-infrared region, which lead to large photocurrent density in agreement with the predictions of electromagnetic and transport computational models. The single nanowire photodetector shows remarkable peak photoresponsivity of 0.57 A/W, comparable to large-area planar GaAs photodetectors on the market, and a high detectivity of 7.2 10^10 cmsqrt{Hz}/W at {lambda}=855 nm. This is promising for the design of a new generation of highly sensitive single nanowire photodetectors by controlling optical mode confinement, bandgap, density of states, and electrode engineering.
We study 95 split gates of different size on a single chip using a multiplexing technique. Each split gate defines a one-dimensional channel on a modulation-doped GaAs/AlGaAs heterostructure, through which the conductance is quantized. The yield of d
evices showing good quantization decreases rapidly as the length of the split gates increases. However, for the subset of devices showing good quantization, there is no correlation between the electrostatic length of the one dimensional channel (estimated using a saddle point model), and the gate length. The variation in electrostatic length and the one-dimensional subband spacing for devices of the same gate length exceeds the variation in the average values between devices of different length. There is a clear correlation between the curvature of the potential barrier in the transport direction and the strength of the 0.7 anomaly: the conductance value of the 0.7 anomaly reduces as the barrier curvature becomes shallower. These results highlight the key role of the electrostatic environment in one-dimensional systems. Even in devices with clean conductance plateaus, random fluctuations in the background potential are crucial in determining the potential landscape in the active device area such that nominally identical gate structures have different characteristics.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها