The high temperature magnetic order in SrRu$_2$O$_6$ was studied by measuring magnetization and neutron powder diffraction with both polarized and unpolarized neutrons. SrRu$_2$O$_6$ crystallizes into the hexagonal lead antimonate (PbSb$_2$O$_6$, spa
ce group textit{P}$overline{3}$1textit{m}) structure with layers of edge-sharing RuO$_6$ octahedra separated by Sr$^{2+}$ ions. SrRu$_2$O$_6$ orders at $T_N$=565,K with Ru moments coupled antiferromagnetically both in-plane and out-of-plane. The magnetic moment is 1.30(2) $mu_mathrm{B}$/Ru at room temperature and is along the crystallographic textit{c}-axis in the G-type magnetic structure. We performed density functional calculations with constrained RPA to obtain the electronic structure and effective intra- and inter-orbital interaction parameters. The projected density of states show strong hybridization between Ru 4$d$ and O 2$p$. By downfolding to the target $t_{2g}$ bands we extracted the effective magnetic Hamiltonian. We performed Monte Carlo simulations to determine the transition temperature as a function of inter- and intra-plane couplings and find weak inter plane coupling, 3% of the intra-plane coupling, permits three dimensional magnetic order at $T_N$. As suggested by the magnetic susceptibility, two-dimensional correlations persist above $T_N$ due to the strong intra-plane coupling.
High quality single crystals of BaFe$_{12}$O$_{19}$ were grown using the floating zone technique in flowing oxygen pressurized to 100 atm. Single crystal neutron diffraction was used to determine the nuclear and magnetic structure of BaFe$_{12}$O$_{1
9}$ at 4 K and 295 K. At both temperatures, there exist local electric dipoles formed by the off-mirror-plane displacements of magnetic Fe$^{3+}$ ions at the bipyramidal sites. The displacement at 4 K is about half of that at room temperature. The temperature dependence of the specific heat shows no anomaly associated with long range polar ordering in the temperature range from 1.90-300 K. The inverse dielectric permittivity, $1/varepsilon$, along the c-axis shows a $T^2$ temperature dependence between 10 K and 20 K, with a significantly reduced temperature dependence displayed below 10 K. Moreover, as the sample is cooled below 1.4 K there is an anomalous sharp upturn in $1/varepsilon$. These features resemble those of classic quantum paraelectrics such as SrTiO$_3$. The presence of the upturn in $1/varepsilon$ indicates that BaFe$_{12}$O$_{19}$ is a critical quantum paraelectric system with Fe$^{3+}$ ions involved in both magnetic and electric dipole formation.
La$_{0.4}$Na$_{0.6}$Fe$_2$As$_2$ single crystals have been grown out of an NaAs flux in an alumina crucible and characterized by measuring magnetic susceptibility, electrical resistivity, specific heat, as well as single crystal x-ray and neutron dif
fraction. La$_{0.4}$Na$_{0.6}$Fe$_2$As$_2$ single crystals show a structural phase transition from a high temperature tetragonal phase to a low-temperature orthorhombic phase at T$_s$,=,125,K. This structural transition is accompanied by an anomaly in the temperature dependence of electrical resistivity, anisotropic magnetic susceptibility, and specific heat. Concomitant with the structural phase transition, the Fe moments order along the emph{a} direction with an ordered moment of 0.7(1),$mu_{textup{B}}$ at emph{T},=,5 K. The low temperature stripe antiferromagnetic structure is the same as that in other emph{A}Fe$_{2}$As$_{2}$ (emph{A},=,Ca, Sr, Ba) compounds. La$_{0.5-x}$Na$_{0.5+x}$Fe$_2$As$_2$ provides a new material platform for the study of iron-based superconductors where the electron-hole asymmetry could be studied by simply varying La/Na ratio.
Millimeter-sized single crystals of LaFeAsO, LaFeAsO1-xFx, and LaFe1-xCoxAsO were grown in NaAs flux at ambient pressure. The detailed growth procedure and crystal characterizations are reported. The as-grown crystals have typical dimensions of 3 * 4
* 0.05-0.3 mm3 with the crystallographic c-axis perpendicular to the plane of the plate-like single crystals. Some crystals manifest linear dimensions as large as 4-5 mm. X-ray and neutron single crystal scattering confirmed that LaFeAsO crystals exhibit a structural phase transition at Ts ~ 154 K and a magnetic phase transition at TSDW ~ 140 K. The transition temperatures agree with those determined by anisotropic magnetization, in-plane electrical resistivity and specific heat measurements and are consistent with previous reports on polycrystalline samples. Co and F were successfully introduced into the lattice leading to superconducting LaFe1-xCoxAsO and LaFeAsO1-xFx single crystals, respectively. This growth protocol has been successfully employed to grow single crystals of NdFeAsO. Thus it is expected to be broadly applicable to grow other RMAsO (R = rare earth, M = transition metal) compounds. These large crystals will facilitate the efforts of unraveling the underlying physics of iron pniticide superconductors.
Plate-like single crystals of SrFe2As2 as large as 3x3x0.5 mm3 have been grown out of Sn flux. The SrFe2As2 single crystals show a structural phase transition from a high temperature tetragonal phase to a low temperature orthorhombic phase at To = 19
8 K, and do not show any sign of superconductivity down to 1.8 K. The structural transition is accompanied by an anomaly in the electrical resistivity, Hall resistivity, specific heat, and the anisotropic magnetic susceptibility. In an intermediate temperature range from 198 K to 160 K, single crystal X-ray diffraction suggests a coexistence of the high-temperature tetragonal and the low-temperature orthorhombic phases.