In our article [1], we found that with increasing dissipation there is a clear, systematic shift and sharpening of the conductance peak along with the disappearance of the higher-bias dip/hump features (DHF), for a stack of intrinsic Josephson juncti
ons (IJJs) of intercalated Bi2Sr2CaCu2O8+{delta} (Bi2212). Our work agrees with Zhu et al [2] on unintercalated, pristine Bi2212, as both studies show the same systematic changes with dissipation. The broader peaks found with reduced dissipation [1,2] are consistent with broad peaks in the density-of-states (DOS) found among scanning tunneling spectroscopy [3] (STS), mechanical contact tunneling [4] (MCT) and inferred from angle (momentum) resolved photoemission spectroscopy [5] (ARPES); results that could not be ignored. Thus, sharp peaks are extrinsic and cannot correspond to the superconducting DOS. We suggested that the commonality of the sharp peaks in our conductance data, which is demonstrably shown to be heating-dominated, and the peaks of previous intrinsic tunneling spectroscopy (ITS) data implies that these ITS reports might need reinterpretation.
We are developing a model of vacuum arcs. This model assumes that arcs develop as a result of mechanical failure of the surface due to Coulomb explosions, followed by ionization of fragments by field emission and the development of a small, dense pla
sma that interacts with the surface primarily through self sputtering and terminates as a unipolar arc capable of producing breakdown sites with high enhancement factors. We have attempted to produce a self consistent picture of triggering, arc evolution and surface damage. We are modeling these mechanisms using Molecular Dynamics (mechanical failure, Coulomb explosions, self sputtering), Particle-In-Cell (PIC) codes (plasma evolution), mesoscale surface thermodynamics (surface evolution), and finite element electrostatic modeling (field enhancements). We can present a variety of numerical results. We identify where our model differs from other descriptions of this phenomenon.
Anomalously high and sharp peaks in the conductance of intrinsic Josephson junctions in Bi$_{2}$Sr$_{2}$CaCu$_{2}$O$_{8+delta}$ (Bi2212) mesas have been universally interpreted as superconducting energy gaps, but here we show they are a result of hea
ting. This interpretation follows from a direct comparison to the equilibrium gap, $mathit Delta$, measured in break junctions on similar Bi2212 crystals. As the dissipated power increases with a greater number of junctions in the mesa, the conductance peak abruptly sharpens and its voltage decreases to well below 2$mathit Delta$. This sharpening, found in our experimental data, defies conventional intuition of heating effects on tunneling spectra, but it can be understood as an instability into a nonequilibrium two-phase coexistent state. The measured peak positions occur accurately within the voltage range that an S-shaped backbending is found in the {it calculated} current-voltage curves for spatially {it uniform} self-heating and that S-shape implies the potential for the uniform state to be unstable.
A method to treat the surface of Nb is described which potentially can improve the performance of superconducting RF cavities. We present tunneling and x-ray photoemission spectroscopy (XPS) measurements at the surface of cavity-grade niobium samples
coated with a 3 nm alumina overlayer deposited by Atomic Layer Deposition (ALD). The coated samples baked in ultra high vacuum (UHV) at low temperature reveal at first degraded superconducting surface. However, at temperatures above 450C, the tunneling conductance curves show significant improvements of the superconducting density of states (DOS) compared with untreated surfaces.
Tunneling spectroscopy was performed on Nb pieces prepared by the same processes used to etch and clean superconducting radio frequency (SRF) cavities. Air exposed, electropolished Nb exhibited a surface superconducting gap delta=1.55 meV, characteri
stic of clean, bulk Nb. However the tunneling density of states (DOS) was broadened significantly. The Nb pieces treated with the same mild baking used to improve the Q-slope in SRF cavities, reveal a sharper DOS. Good fits to the DOS were obtained using Shiba theory, suggesting that magnetic scattering of quasiparticles is the origin of the gapless surface superconductivity and a heretofore unrecognized contributor to the Q-slope problem of Nb SRF cavities.