Register a new userAn assessment of the effectiveness of using calcium phosphate bone cement in increasing the primary stability of orthodontic miniscrews - in-vitro study
تقييم فاعلية استخدام اسمنت فوسفات الكالسيوم العظمي في زيادة الاستقرار الأولي للزريعات التقويمية -دراسة مخبرية
1158
0 11
0
(
0
)
Created by
Shamra Editor
Ask ChatGPT about the research
تهدف هذه الدراسة إلى تقييم فعالية استخدام اسمنت فوسفات الكالسيوم العظمي في زيادة الاستقرار الأولي للزريعات التقويمية عن طريق اختبار مقاومتها لقوى الشد.
This study aims to assess the effectiveness of using calcium phosphate bone cement in increasing the primary stability of orthodontic miniscrews by testing its resistance to pullout forces.
Artificial intelligence review:
Research summary
تهدف هذه الدراسة إلى تقييم فعالية استخدام أسمنت فوسفات الكالسيوم العظمي في زيادة الاستقرار الأولي للزريعات التقويمية عن طريق اختبار مقاومتها لقوى الشد. تم اختيار 20 عينة عظمية بقرية بمتوسط تخانة العظم القشري 1.9 ± 0.7 ملم، وتم تقسيمها إلى مجموعتين: الأولى تم إدخال الزريعة مباشرة في الثقب، والثانية تم ملء الثقب بالأسمنت قبل إدخال الزريعة. أظهرت النتائج وجود فروق ذات دلالة إحصائية بين متوسط قيم قوة السحب في مجموعة الأسمنت (7.7) والمجموعة الشاهدة (3.3)، مما يدل على فعالية أسمنت فوسفات الكالسيوم العظمي في زيادة الاستقرار الأولي للزريعات. توصي الدراسة باستخدام هذا الأسمنت في تثبيت الزريعات التقويمية لزيادة الاستقرار الأولي، وتقترح إجراء دراسات سريرية ونسيجية إضافية لتقييم فعالية هذه الطريقة بشكل أوسع.
Critical review
دراسة نقدية: تعتبر هذه الدراسة خطوة مهمة نحو تحسين استقرار الزريعات التقويمية باستخدام أسمنت فوسفات الكالسيوم العظمي. ومع ذلك، هناك بعض النقاط التي يمكن تحسينها. أولاً، كان من الأفضل استخدام عينات عظمية بشرية بدلاً من العظم البقري لتحقيق نتائج أكثر دقة وقابلة للتطبيق السريري. ثانياً، لم تذكر الدراسة تأثيرات طويلة الأمد لاستخدام الأسمنت على العظم والزريعات، وهو ما يستدعي إجراء دراسات متابعة لتقييم هذه التأثيرات. أخيراً، كان من المفيد تضمين مجموعة مقارنة باستخدام أنواع أخرى من الأسمنت العظمي مثل أسمنت البولي ميتيل ميتا أكريلات (PMMA) لتقديم رؤية شاملة حول الفعالية النسبية لكل نوع.
Questions related to the research
-
ما هو الهدف الرئيسي من هذه الدراسة؟
الهدف الرئيسي هو تقييم فعالية استخدام أسمنت فوسفات الكالسيوم العظمي في زيادة الاستقرار الأولي للزريعات التقويمية عن طريق اختبار مقاومتها لقوى الشد.
-
ما هي النتائج الرئيسية التي توصلت إليها الدراسة؟
أظهرت النتائج أن هناك فروق ذات دلالة إحصائية بين متوسط قيم قوة السحب في مجموعة الأسمنت (7.7) والمجموعة الشاهدة (3.3)، مما يدل على فعالية أسمنت فوسفات الكالسيوم العظمي في زيادة الاستقرار الأولي للزريعات.
-
ما هي التوصيات التي قدمتها الدراسة؟
توصي الدراسة باستخدام أسمنت فوسفات الكالسيوم العظمي في تثبيت الزريعات التقويمية لزيادة الاستقرار الأولي، وتقترح إجراء دراسات سريرية ونسيجية إضافية لتقييم فعالية هذه الطريقة بشكل أوسع.
-
ما هي النقاط التي يمكن تحسينها في الدراسة؟
يمكن تحسين الدراسة باستخدام عينات عظمية بشرية بدلاً من العظم البقري، وتقييم التأثيرات طويلة الأمد لاستخدام الأسمنت، وتضمين مجموعة مقارنة باستخدام أنواع أخرى من الأسمنت العظمي مثل أسمنت البولي ميتيل ميتا أكريلات (PMMA).
References used
Proffit W. Mechanical principles in orthodontic force control.1993 . In: Proffit W, Fields HW, editors. Contemporary Orthodontics. Saint Louis: Mosby; Pg. 308
Kim JW, Ahn SJ, Chang YI. Histomorphometric and mechanical analyses of the drill-free screw as orthodontic anchorage. Am J Orthod Dentofacial Orthop 2005 Aug;128(2):190-4
Emily J. Hung, B.S. An evaluation of the effects of altering pilot hole size and bone density on primary stability of orthodontic miniscrews. A Thesis Presented to the Faculty of the Graduate School of Saint Louis University in Partial Fulfillment of the Requirements for the Degree of Master of Science in Dentistry 2009
rate research
Read More
The aim of the study was to determine the effect of Dual-Thread and diameter on the orthodontic miniscrew primary stability, and define the best shape and diameter of miniescrew can be used to give the best stability.
The study sample consisted of
(24) orthodontic miniscrews made of (Ti-6Al-4V) alloy with 2 shapes (regular and Dual-Thread) , and 2 diameters (1.6 , 1.8mm). The experiment has been divided into 3 tests : measuring the maximum insertion torque , the Periotest value , the maximum removal torque.
The results showed that the maximum insertion and removal torque were statistically higher while the Periotest values were statistically lower when using the Dual-Thread and the diameter of 1.8 mm than the regular shape and the diameter of 1.6 mm(P>0.01)
There is an increasing role for orthodontic mini implants as an anchorage device in orthodontic practice In many occasions, orthodontists may have to reuse orthodontic mini-implants (re-implanting again ) after sterilizing them by moist heat. The aim
of this research was investigating the effect of re-implantation and moist heat sterilization on the primary fixity of orthodontic mini-implants> Two lengths of mini-implants (6-7mm) (ti – 6A1 – 4A1 ) and two shapes (normal and dual thread ) were used and inserted in artificial bone (saw bone ) a first time and after sterilizing them by moist heat (Autoclave) a second time , in an insertion angle of 90 . The insertion and removal torque and periotest score (periodontium test device ) were measured to assess the primary fixity ( after implanting in the first time and the second time ) The results showed a decrease in the primary fixity after re-implanting and sterilizing by moist heat , but it still enough for using it a second time effectively to provide needed orthodontic anchorage for both two lengths and two shapes.
This study aims to know the effect of PRP on bone healing and regeneration after cystoectomy within studying clinical and radiological bone density changes. The research sample comprised 18 patients (14 males, 4 females) (20 cystic lesions in the upp
er jaw,1-3 cm diameter). This sample was divided into 2 similar groups :
The experimental group: Platelets-rich Plasma with Tri-Calcium Phosphate was applied.
The control group: only Tri-Calcium Phosphate, without Platelets-rich Plasma, was applied.
Both groups were observed clinically and radiologically. According to radiological observation, the digital panoramic radiographs were taken before, immediately after surgery, after 3 months, and after 6 months, respectively. Bone density measurements were done through Digora® digital program.
The present study showed that there is no statistical difference between the experimental group & the control group, regarding Pain Index and Infection Index; while there was a statistical difference between the experimental group & the control group, regarding bone density after 3 and 6 months after surgery.
Within the limitations of the present study, the application of autologous platelets-rich plasma (PRP) accelerates bone regeneration after cystoectomy.
Aim: The aim of this study was to detect the effect of dressing period of calcium
hydroxide medicament on the apical marginal leakage after obturation of root canal
system.
Materials and Methods: 80 freshly extracted single rooted human teeth were
selected ,all the root canals were hand-instrumented. They were randomly divided into four
groups of 20 teeth each. Group A has no intracanal medicament , groups (B,C,D) were
dressed with Ca(OH)2 paste for a different periods of time (7,14,30) days respectively,
groups (B,C,D) were divided into subgroups of 10 teeth according to removing of dressing
. The removal of ca(OH)2was done by two ways, 1- By irrigating with distilled water and
drying with paper points . 2- Size 40 k-file was used in slightly filing motion up to the
working length then irrigated with distilled water and drying with paper points. After that
all groups were obturated with lateral compaction technique using gutta-percha points and
zinc oxide-eugenol cement. Then the access was sealed with GIC cement. The teeth were
immersed into 2% mythylene blue solution ,The specimens were placed in an incubator at
37 C ,with moisture at 100%, for 7 days .After that the roots were sectioned
longitudinally and examined with stereomicroscope and liner leakage was measured.
The objective of the present study was to investigate, in a sub-sinus
bone augmentation model in rabbits, effect of Three Calcium Phosphate
beta at different stages of the osteogenesis process. Histological and
statistical analyses were performed.
Rabbits underwent sinus augmentation procedures using Three Calcium
Phosphate beta (Cerasorb) and Collagen membrane ( Gen Derm ) .