تم في هذا البحث تعديل البنية الكيميائية للكيتوزان عن طريق تفاعل الأسترة المتصالبة "Trans Esterification" مع الاستر المتيلي لكل من حمض الأوكتانوئيك و الدوديكانوئيك، باستخدام كربونات البوتاسيوم كوسط أساسي كما تم تحديد درجة الإستبدال لناتج الأسترة المتصالبة من أجل تغيير الخصائص المحبة للماء "hydrophilic properties", بعد ذلك تم تحديد بعض الخصائص الفيزيائية لنواتج الأسترة المتصالبة من خلال قياس المزوجة الكيناميكية و درجة العكارة و الكثافة لمحاليلها المائية.
In this paper, the chemical structure of chitosan has been modified by trans esterification reaction with methyl esters both of octanoic and dodecanoic acid, using potassium carbonate as a based catalyst, the degree of substitution has been determinated to change hydrophilic properties, Some physical properties of trans esterification products has been determined by measuring the Kinematic viscosity, degree of turbidity and density of their water solutions.
Artificial intelligence review:
Research summary
في هذا البحث، تم تعديل البنية الكيميائية للكيتوزان من خلال تفاعل الأسترة المتصالبة مع استرات الميثيل لكل من حمض الأوكتانوئيك والدوديكانوئيك، باستخدام كربونات البوتاسيوم كعامل محفز. تم تحديد درجة الاستبدال الناتجة لتغيير الخصائص المحبة للماء. تم قياس بعض الخصائص الفيزيائية للنواتج من خلال قياس اللزوجة الكيناميكية ودرجة العكارة والكثافة لمحاليلها المائية. كما تم دراسة حركية تحرر المادة الدوائية (الأسبرين) من خلال مقارنة زمن التحرر عند تحميل المادة الدوائية على نواتج التفاعل وتشكيل حبيبات في وسط مائي ملحي. أظهرت النتائج زيادة زمن تحرر المادة الدوائية بزيادة الخصائص الكارهة للماء للكيتوزان المعدل بسلاسل ألكيلية. تم تحديد بنى المركبات الناتجة باستخدام تقنيات FT-IR وH-NMR.
Critical review
دراسة نقدية: يعتبر هذا البحث خطوة مهمة في مجال تعديل البوليمرات الطبيعية لتحسين خصائصها وتطبيقاتها. ومع ذلك، يمكن الإشارة إلى بعض النقاط التي قد تحتاج إلى مزيد من التوضيح أو البحث المستقبلي. أولاً، لم يتم توضيح بشكل كافٍ تأثير درجة الاستبدال على الخصائص الميكانيكية للكيتوزان المعدل، والتي قد تكون مهمة لتطبيقات معينة. ثانياً، قد يكون من المفيد دراسة تأثير العوامل البيئية مثل درجة الحرارة والـpH على استقرار وفعالية المواد المعدلة. وأخيراً، يمكن أن يكون هناك اهتمام بدراسة تأثير هذه التعديلات على التوافق الحيوي والسلامة عند استخدامها في التطبيقات الطبية.
Questions related to the research
-
ما هو الهدف الرئيسي من البحث؟
الهدف الرئيسي هو تعديل بنية الكيتوزان باستخدام سلاسل ألكيلية مختلفة ودراسة تأثير ذلك على بعض خصائصه الفيزيائية وحركية تحرر المادة الدوائية (الأسبرين).
-
ما هي الطرق المستخدمة لتحديد بنية المركبات الناتجة؟
تم استخدام تقنيات FT-IR وH-NMR لتحديد بنية المركبات الناتجة.
-
ما هي النتائج الرئيسية المتعلقة بتحرر المادة الدوائية؟
أظهرت النتائج أن زمن تحرر المادة الدوائية (الأسبرين) يزداد بزيادة الخصائص الكارهة للماء للكيتوزان المعدل بسلاسل ألكيلية.
-
ما هي الخصائص الفيزيائية التي تم قياسها للمركبات الناتجة؟
تم قياس اللزوجة الكيناميكية ودرجة العكارة والكثافة لمحاليل المركبات الناتجة.
References used
A. Durand and E. Dellacherie, “Neutral amphiphilic polysaccharides: Chemical structure and emulsifying properties,” Colloid Polym. Sci., vol. 284, no. 5, pp. 536–545, 2006
Se-Kwon Kim, Chitin, Chitosan, Oligosaccharides and Their Derivatives: Biological Activities and Applications. 2011
M. a C. Stuart and J. W. Mulder, “Adsorbed Polymers in Aqueous Media,” Colloids and Surfaces, vol. 15, 1985
rate research
Read More
In this paper, the chemical structure of pectin has been
modified by reacting of carboxyl group in pectin with tetrabutyl
ammonium hydroxide [TBA-OH], (acid-base) reaction, to change
hydrophilic properties by adding hydrophobic alkyl chains to the
polymer chain in pectin, Some physical properties of both: pectin
and tetrabutyl ammonium pectin; has been determined by
measuring the Kinematic viscosity, degree of turbidity and density
of their water solutions at different concentration.
In this work, several samples of poly(propylene itaconat ortho
phthalate) based on itaconic acid and 1,2-propylene glycol were
prepared by polycondensation.
This Study focused on the lithostratigraphic properties of Mamlaht
Al-Kom structure, for evaluating the hydrocarbon potential of this
important structure. In order to achieve this goal, the time and depth
maps are constructed, through revaluating
and interpreting the
seismic sections, correlating the drilled wells, and appraising the
available well rock samples. The obtained data permit to ensure the
hydrocarbon potential of the K.D formation, because of its suitable
thickness, presence of cover, and source rock. On the other hand,
the entire shape of the structure is not defined accurately as all the
exploration wells were drilled along the axis North East – South
west. Thus these results should be checked by reinterpreting the
available seismic data depending on the geological and
lithostratigraphic data, and drill exploration wells on the axis North
– South to define the depth and structure of the reservoir reliably.
This research deals with producing structural lightweight aggregates concrete (the
density is less than 1920kg/m3 and compressive strength is more than 17.2Mpa according
to ACI 213R-03) by using scoria aggregates. Several concrete mixes have been d
esigned
with different proportions of scoria aggregates. The cement content (c=450 kg/m3), the
ratio (w/c = 0.36) were kept constant in all the mixes.
Different tests were performed to determine some properties of product concrete
such as density, compressive strength and splitting tensile strength. The density of product
concrete was in the range of (1752-1917 kg/m3), compressive strength was in the range of
(22.2-32.8Mpa), and the splitting strength was in the range of (2.3-3.2Mpa). The study
demonstrated the possibility of production concrete achieved the Requirements of the
American code ACI 213R-03 for structural lightweight concrete.
Event driven embedded systems are one of the essential structures of heterogeneous embedded systems. The difference behavior of hardware and software motivates the usage of high-level system design approaches such as Hardware Software co-design Model
. The objective of this paper is to obtain a new Co-design model for discrete-events embedded systems based on Markov chains, and then using the heterogeneous modeling by composing the discrete-times model within discrete-events model to apply it on anti‐lock braking system (ABS). To achieve the model, we use Ptolemy II which is a Java-based software framework developed as part of the Ptolemy Project by University of California, Berkeley. The importance of this paper is to be the kernel for heterogeneous co-design modeling for heterogeneous embedded systems in future works.
Log in to be able to interact and post comments
comments
Fetching comments
Sign in to be able to follow your search criteria