The effect of catalyst and accelerator on mechanical properties Of Unsaturated Polyester Resin (UPR)

تأثير المادة البادئة و المادة المسرعة على الخواص الميكانيكية للبولي استر غير المشبع

1187   0   18   0 ( 0 )
 Publication date 2016
and research's language is العربية
 Created by Shamra Editor




Ask ChatGPT about the research

This search aims to study the effect of additive materials ( Ethyl Methyl Keton Peroxide MEKP , Cobalt Naphthenate ) at the important values of (stress-strain) curves ( stress and elongation at break ) for the preparing specimens from reinforced and nonreinforced with fiber glass unsaturated polyester resin. The result showed that the investigated parameters are clearly affected with using additive materials and the optimum concentration for non-reinforced specimens which was curing in room temperature was (1% MEKP + 1% Cobalt Naphthenate) and (0.8% MEKP + 1% Cobalt Naphthenate), and for reinforced specimens with fiber glass was:( 1% MEKP + 0.8% Cobalt Naphthenate) and ((0.2-0.4) % MEKP + 1% Cobalt Naphthenate). The results showed also that it is possible to get the better values of tensile stress at break when the specimens was curing in oven at 100 Cº and treated at this temperature for 15 min.


Artificial intelligence review:
Research summary
تهدف هذه الدراسة إلى تحليل تأثير المواد المضافة مثل بيروكسيد الميثيل إيثيل كيتون (MEKP) وكوبالت نفتتات على الخواص الميكانيكية للبولي استر غير المشبع (UPR)، سواء كان مسلحًا بطبقة من الألياف الزجاجية العشوائية أو غير مسلح. أظهرت النتائج أن هذه المواد تؤثر بشكل كبير على إجهاد الشد والاستطالة النسبية عند التحطم. تم تحديد النسب المثلى للمواد المضافة لتحقيق أفضل خواص ميكانيكية للعينات غير المسلحة والمسلحة. كما أظهرت الدراسة أن تحضير العينات على الساخن عند درجة حرارة 100 درجة مئوية يعزز من قيم إجهاد الشد عند التحطم بشكل ملحوظ مقارنة بالعينات المحضرة على البارد. توصلت الدراسة إلى أن النسب المثلى للمواد المضافة تتراوح بين 1% MEKP و1% كوبالت نفتتات للعينات غير المسلحة، و0.8% MEKP و1% كوبالت نفتتات للعينات المسلحة. كما أكدت النتائج أن المعالجة الحرارية عند درجة حرارة 100 درجة مئوية لمدة 15 دقيقة تؤدي إلى تحسين الخواص الميكانيكية للعينات بشكل كبير.
Critical review
دراسة نقدية: على الرغم من أن البحث قدم نتائج مفيدة حول تأثير المواد المضافة على الخواص الميكانيكية للبولي استر غير المشبع، إلا أنه كان من الممكن تحسينه من خلال تضمين المزيد من التفاصيل حول التطبيقات العملية لهذه النتائج في الصناعات المختلفة. كما أن الدراسة اعتمدت بشكل كبير على الاختبارات المخبرية، وكان من الأفضل إجراء تجارب ميدانية للتحقق من النتائج في ظروف تشغيل حقيقية. بالإضافة إلى ذلك، كان من الممكن توسيع نطاق الدراسة لتشمل مواد مضافة أخرى قد تكون لها تأثيرات مختلفة على الخواص الميكانيكية للبولي استر غير المشبع.
Questions related to the research
  1. ما هي المواد المضافة التي تم دراستها في البحث؟

    تم دراسة تأثير بيروكسيد الميثيل إيثيل كيتون (MEKP) وكوبالت نفتتات على الخواص الميكانيكية للبولي استر غير المشبع.

  2. ما هي النسب المثلى للمواد المضافة للعينات غير المسلحة؟

    النسب المثلى للعينات غير المسلحة هي 1% MEKP و1% كوبالت نفتتات.

  3. ما هو تأثير المعالجة الحرارية عند درجة حرارة 100 درجة مئوية على العينات؟

    المعالجة الحرارية عند درجة حرارة 100 درجة مئوية لمدة 15 دقيقة تؤدي إلى تحسين قيم إجهاد الشد عند التحطم بشكل ملحوظ.

  4. هل تم إجراء تجارب ميدانية للتحقق من النتائج؟

    لا، الدراسة اعتمدت بشكل كبير على الاختبارات المخبرية ولم تشمل تجارب ميدانية للتحقق من النتائج في ظروف تشغيل حقيقية.


References used
SMITH, C. -Design of marine structures in composite materials, Elsevier Applied Science, London, 2005, 110-130
Li, L.; Sun, X.; Lee, L. -Thermoset Polymers, Dow Chemical, Technical Information, 1999, 39(4):646–6
CZVIKOVSZKY, T. -The chemistry and technology of the wood reinforced polymer composites, Műanyagipari Kutató Intézet, Budapest, 1987, 45-50
rate research

Read More

As a result of the development of the use of reinforced Composites with fibers in practical applications continuously, research aims to study the effect of proportion piroxide additives to unsaturated polyester resin on the tensile properties of th e samples prepared from unsaturated polyester resin reinforced with glass fiber used in wind turbine blades manufacturing, and also studying the effect of for the application of heat treatment operations on the hardening of the unsaturated polyester and tensile properties after heat treatment process the application in order to improve the properties of these blades. Test samples were prepared containing ratios (1% - 1.5% - 2%) of methyl Etel ketone piroxide MEKP and test results showed that the best ratio at 1.5%. While the heat treatment results showed that the best values for tensile strength at break of the samples are treated to a time of / 48 hours /.
This research aims to study the effect of addition the filling materials (sodium aluminosilicate, Talc) to the unsaturated polyester(unsaturated polyester resign)(UPR) first, and unsaturated polyester reinforced by fiberglass (20%) secondly, Number o f mechanical tests were done, they included (Tensile, Flexural Strength). The effect of addition of filling materials sodium aluminosilicate (SAS), Talc, and a mixture of sodium aluminosilicate and Talc to the unreinforced polyester with fiberglass was studied in the first step of the research, and the results showed that the best values were gotten when adding a mixture of ((SAS) and Talc) at ratio (10% SAS,5% Talc), where the tensile strength value raised up from (31.2 MPa) to (33 MPa), and the elastic module value also raised up from (2330 MPa) to (2750.5 MPa) , and the flexural strength value also raised up from (0.057 GPa) to (0.0729 GPa). The effect of addition of filling materials (sodium aluminosilicate, Talc, and a mixture of sodium aluminosilicate and Talc ) to the reinforced polyester with fiberglass (20%) was studied in the second step of the research, and the results showed that the best values were gotten when adding a mixture of ((SAS) and Talc) at ratio (5% SAS,5% Talc), where the tensile strength value raised up from (101.7 MPa) to (108.8 MPa), and the elastic module value also raised up from (5616 MPa) to (6367.9 MPa), and the flexural strength value raised up from (0.1203 GPa) to (0.1597 GPa).
In this paper an experimental investigation of unsaturated polyester(UPR) with different weight fractions(2,4,5,7 )wt% of (Al2O3,MgO,TiO2) as powders ,has been done. the identification of their flammability and fire resistance ranges are found out . the time needed to puncture the samples, the mass loss, the diameter variation ,and the flame effect on the samples surface are measured. the samples were tested by Oxyacetylene flame using a device which is designed in the Faculty of Mechanical and Electrical Engineering labs. The results showed that (MgO) is the best one for its flammability and fire resistance. The longest time before puncture , and the lowest mass loss were achieved by( UPR+ 7% MgO) with(16% mass loss in 112 sec ), while pure UPR has ( 27% mass loss in 45 sec).
This research includes an experimental study for the manufacture of a composite material based on polymer (unsaturated polyester), reinforced with random fiberglass at different weight fractions. By suite, it has been studied some mechanical prope rties of the models manufactured, to determine the effect of glass fiber content on the tensile strength, hardness and impact resistance. This study has shown that the best results were for samples reinforced by 40% fiberglass, where the tensile strength increased about 70%, hardness up to 30%, and impact resistance about 43%. It will be observed that the mechanical properties decrease clearly at 60% of weight fraction of fiberglass. This fact can be related to the quantity of unsaturated polyester become inadequate for recharge of the fibers, which leads to weakness in the forces bonding in composite materials.
In this paper an experimental investigation of unsaturated polyester(UPR) with different weight fractions(2,4,5,7 )wt% of (Al2O3,MgO,TiO2) as powders ,has been done. the identification of their flammability and fire resistance ranges are found out . the time needed to puncture the samples, the mass loss, the diameter variation ,and the flame effect on the samples surface are measured. the samples were tested by Oxyacetylene flame using a device which is designed in the Faculty of Mechanical and Electrical Engineering labs. The results showed that (MgO) is the best one for its flammability and fire resistance. The longest time before puncture , and the lowest mass loss were achieved by( UPR+ 7% MgO) with(16% mass loss in 112 sec ), while pure UPR has ( 27% mass loss in 45 sec).
comments
Fetching comments Fetching comments
Sign in to be able to follow your search criteria
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا