Register a new userMorphology modifcation of Si nanopillars under ion irradiation at elevated temperatures: plastic deformation and controlled thinning to 10 nm
405
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
Si nanopillars of less than 50 nm diameter have been irradiated in a helium ion microscope with a focused Ne$^+$ beam. The morphological changes due to ion beam irradiation at room temperature and elevated temperatures have been studied with the transmission electron microscope. We found that the shape changes of the nanopillars depend on irradiation-induced amorphization and thermally driven dynamic annealing. While at room temperature, the nanopillars evolve to a conical shape due to ion-induced plastic deformation and viscous flow of amorphized Si, simultaneous dynamic annealing during the irradiation at elevated temperatures prevents amorphization which is necessary for the viscous flow. Above the critical temperature of ion-induced amorphization, a steady decrease of the diameter was observed as a result of the dominating forward sputtering process through the nanopillar sidewalls. Under these conditions the nanopillars can be thinned down to a diameter of 10 nm in a well-controlled manner. A deeper understanding of the pillar thinning process has been achieved by a comparison of experimental results with 3D computer simulations based on the binary collision approximation.
rate research
Read More
The shape and alignment of silver nanoparticles embedded in a glass matrix is controlled using silicon ion irradiation. Symmetric silver nanoparticles are transformed into anisotropic particles whose larger axis is along the ion beam. Upon irradiation, the surface plasmon resonance of symmetric particles splits into two resonances whose separation depends on the fluence of the ion irradiation. Simulations of the optical absorbance show that the anisotropy is caused by the deformation and alignment of the nanoparticles, and that both properties are controlled with the irradiation fluence.
A procedure to achieve the density-controlled growth of gold-catalyzed InP nanowires (NWs) on (111) silicon substrates using the vapor-liquid-solid method by molecular beam epitaxy is reported. We develop an effective and mask-free method based on controlling the number and the size of the Au-In catalyst droplets in addition to the conditions for the NW nucleation. We show that the NW density can be tuned with values in the range of 18 {mu}m-2 to < 0.1 {mu}m-2 by the suitable choice of the In/Au catalyst beam equivalent pressure (BEP) ratio, by the phosphorous BEP and the growth temperature. The same degree of control is transferred to InAs/InP quantum dot-nanowires, taking advantage of the ultra-low density to study by micro-photoluminescence the optical properties of a single quantum dot-nanowires emitting in the telecom band monolithically grown on silicon. Optical spectroscopy at cryogenic temperature successfully confirmed the relevance of our method to excite single InAs quantum dots on the as-grown sample, which opens the path for large-scale applications based on single quantum dot-nanowire devices integrated on silicon.
Hydroxyapatite synthesized by a wet chemical route was subjected to heavy Krypton ion irradiation of 4MeV at various fluences. Glancing incidence Xray diffraction results confirmed the phase purity of irradiated HA with a moderate contraction in lattice parameters, and further indicated the irradiation induced structural disorder, evidenced by broadening of the diffraction peaks. High resolution transmission electron microscopy observations indicated that the applied Kr irradiation induced significant damage in the hydroxyapatite lattice. Specifically, cavities were observed with their diameter and density varying with the irradiation fluences, while a radiation induced crystalline to amorphous transition with increasing ion dose was identified. Raman and Xray photoelectron spectroscopy analysis further indicated the presence of irradiation induced defects. Ion release from pristine and irradiated materials following immersion in Trisbuffer showed that dissolution in vitro was enhanced by irradiation. We examined the effects of irradiation on the early stages of the mouse osteoblast like cells response. A cell counting kit 8 assay was carried out to investigate the cytotoxicity of samples, and viable cells can be observed on the irradiated materials.
Despite recent significant developments of Si composites, use of silicon with significance in the anodes for Li-ion batteries is still limited. In fact, nominal energy density is to be saturated around ~750 Wh/L regardless of cell-types under the current material strategies. Use of Si-rich anode can push the limit; however, the prolonged irreversible Li consumption becomes more prominent. We previously showed that repeating c-Li3.75(+{delta})Si formation/decomposition, typically recognized to degrade the anodes, can improve the irreversibility and accumulatively minimize the gross consumption. Utilizing the insights combined with prelithiation techniques, here we provide prototypic cell designs that can nonlinearly deplete the consumption.
Amorphous hydrogenated silicon nitride ($textit{a}$-SiN$_mathrm{textit{x}}$:H) thin films irradiated with 100 MeV Ni$^{7+}$ results in the formation of continuous ion track structures at the lower fluence of $5times{10^{12}}$ ions/cm$^2$ whereas at higher fluence of $1times{10^{14}}$ ions/cm$^2$ the track structures fragment into discontinuous ion track like structures . The observation of the discontinuous ion track like structures at the high fluence of $1times{10^{14}}$ ions/cm$^2$ shows clearly that higher fluence irradiation may not always lead to dissolution of the microstructure formed at lower fluence. The results are understood on the basis of a dynamic electronic energy loss (S$_{e}$) in the course of irradiation resulting from the out-diffusion of hydrogen from the films and a continuous increase in density of $textit{a}$-SiN$_mathrm{textit{x}}$:H films.