Register a new userRole of interfaces in the biased composition of TbFe(Co) thin films
149
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
Ferrimagnetic TbFe or TbFeCo amorphous alloy thin films have been grown by co-evaporation in ultra-high vacuum. They exhibit an out-of-plane magnetic anisotropy up to their Curie temperature with a nucleation and propagation reversal mechanism suitable for current induced domain wall motion. Rutherford back scattering experiments confirmed a fine control of the Tb depth-integrated composition within the evaporation process. However, a large set of experimental techniques were used to evidence an interface related contribution in such thin films as compared to much thicker samples. In particular, scanning transmission electron microscopy experiments evidence a depth dependent composition and perturbed top and bottom interfaces with preferential oxidation and diffusion of terbium. Despite of that, amorphous and homogeneous alloy film remains in a bulk-like part. The composition of that bulk-like part of the magnetic layer, labeled as effective composition, is biased when compared with the depth-integrated composition. The magnetic properties of the film are mostly dictated by this effective composition, which we show changes with different top and bottom interfaces.
rate research
Read More
We demonstrate that room temperature ferromagnetic response (RT FR) of ZnCoO films grown at low temperature by the Atomic layer Deposition (ALD) method is due to Co metal accumulations at the ZnCoO/substrate interface region. The accumulated experimental evi evidences allow us to reject several other explanations of this effect in our samples, despite the fact that some of them are likely to be responsible for the low temperature FM in this class of the material.
Epitaxial thin films have been utilised to investigate the radiolytic dissolution of uranium dioxide interfaces. Thin films of UO$_2$ deposited on single crystal yttria stabilised zirconia substrates have been exposed to water in the presence of a high flux, monochromatic, synchrotron x-ray source. In particular, this technique was applied to induce dissolution of three UO$_2$ thin films, grown along the principle UO$_2$ crystallographic orientations: (001), (110) and (111). Dissolution of each film was induced for 9 accumulative corrosion periods, totalling 270s, after which XRR spectra were recorded to observe the change in morphology of the films as a function of exposure time. While the (001) and (110) oriented films were found to corrode almost linearly and at comparable rates, the (111) film was found to be significantly more corrosion resistant, with no loss of UO$_2$ material being observed after the initial 90s corrosion period. These results distinctly show the effect of crystallographic orientation on the rate of x-ray induced UO$_2$ dissolution. This result may have important consequences for theoretical dissolution models, as it is evident that orientation dependence must be taken into consideration to obtain accurate predictions of the dissolution behaviour of UO$_2$.
We present depth-resolved experimental results on the atomic and electronic structures of the Co-Cr interface on four IrMn/Cr/Co thin films with variable thickness of the Cr layer. Grazing incidence X-ray absorption near edge structure near the Cr K-edge was used, and an Angstrom resolved depth-profile for this layer was obtained. An interdiffusion between chromium and cobalt layers was observed in all films, being more pronounced for samples with thinner Cr layers, where Cr behaves as an amorphous material. This causes a contraction in coordination distances in Cr near the interface with Co. In this region, a change in the electronic structure of chromiums 3d orbitals is also observed, and it appears that Cr and Co form a covalent bond resulting in a CrCo alloy. Ab initio numerical simulations support such an interpretation of the obtained experimental results.
Uncompensated moments in antiferromagnets are responsible for exchange bias in antiferromagnet/ferromagnet heterostructures; however, they are difficult to directly detect because any signal they contribute is typically overwhelmed by the ferromagnetic layer. We use magneto-thermal microscopy to image uncompensated moments in thin films of FeRh, a room-temperature antiferromagnet that exhibits a 1st-order phase transition to a ferromagnetic state near 100~$^circ$C. FeRh provides the unique opportunity to study both uncompensated moments in the antiferromagnetic phase and the interaction of uncompensated moments with emergent ferromagnetism within a relatively broad (10-15~$^circ$C) temperature range near $T_C$. In the AF phase below $T_C$, we image both pinned UMs, which cause local vertical exchange bias, and unpinned UMs, which exhibit an enhanced coercive field that reflects exchange-coupling to the AF bulk. Near $T_C$, where AF and FM order coexist, we find that the emergent FM order is exchange-coupled to the bulk Neel order. This exchange coupling leads to the nucleation of unusual configurations in which different FM domains are pinned parallel, antiparallel, and perpendicular to the applied magnetic field before suddenly collapsing into a state uniformly parallel to the field.
Ultrafast control of the magnetization in ps timescales by fs laser pulses offers an attractive avenue for applications such as fast magnetic devices for logic and memory. However, ultrafast helicity-independent all-optical switching (HI-AOS) of the magnetization has thus far only been observed in Gd-based, ferrimagnetic amorphous (textit{a}-) rare earth-transition metal (textit{a}-RE-TM) systems, and a comprehensive understanding of the reversal mechanism remains elusive. Here, we report HI-AOS in ferrimagnetic textit{a}-Gd$_{22-x}$Tb$_x$Co$_{78}$ thin films, from x = 0 to x = 18, and elucidate the role of Gd in HI-AOS in textit{a}-RE-TM alloys and multilayers. Increasing Tb content results in increasing perpendicular magnetic anisotropy and coercivity, without modifying magnetization density, and slower remagnetization rates and higher critical fluences for switching but still shows picosecond HI-AOS. Simulations of the atomistic spin dynamics based on the two-temperature model reproduce these results qualitatively and predict that the lower damping on the RE sublattice arising from the small spin-orbit coupling of Gd (with $L = 0$) is instrumental for the faster dynamics and lower critical fluences of the Gd-rich alloys. Annealing textit{a}-Gd$_{10}$Tb$_{12}$Co$_{78}$ leads to slower dynamics which we argue is due to an increase in damping. These simulations strongly indicate that acounting for element-specific damping is crucial in understanding HI-AOS phenomena. The results suggest that engineering the element specific damping of materials can open up new classes of materials that exhibit low-energy, ultrafast HI-AOS.