Skyrmions in ultrathin ferromagnetic metal (FM)/heavy metal (HM) multilayer systems produced by conventional sputtering methods have recently generated huge interest due to their applications in the field of spintronics. The sandwich structure with two correctly-chosen heavy metal layers provides an additive interfacial exchange interaction which promotes domain wall or skyrmion spin textures that are Neel in character and with a fixed chirality. Lorentz transmission electron microscopy (TEM) is a high resolution method ideally suited to quantitatively image such chiral magnetic configurations. When allied with physical and chemical TEM analysis of both planar and cross-sectional samples, key length scales such as grain size and the chiral variation of the magnetisation variation have been identified and measured. We present data showing the importance of the grain size (mostly < 10nm) measured from direct imaging and its potential role in describing observed behaviour of isolated skyrmions (diameter < 100nm). In the latter the region in which the magnetization rotates is measured to be around 30 nm. Such quantitative information on the multiscale magnetisation variations in the system is key to understanding and exploiting the behaviour of skyrmions for future device applications.
rate research
Read More
The interfacial Dzyaloshinskii-Moriya interaction (DMI) in multilayers of heavy metal and ferromagnetic metals enables the stabilization of novel chiral spin structures such as skyrmions. Magnetic insulators, on the other hand can exhibit enhanced dynamics and properties such as lower magnetic damping and therefore it is of interest to combine the properties enabled by interfacial DMI with insulating systems. Here, we demonstrate the presence of interfacial DMI in heterostructures that include insulating magnetic layers. We use a bilayer of perpendicularly magnetized insulating thulium iron garnet (TmIG) and the heavy metal platinum, and find a surprisingly strong interfacial DMI that, combined with spin-orbit torque results, in efficient switching. The interfacial origin is confirmed through thickness dependence measurements of the DMI, revealing the characteristic 1/thickness dependence with one order of magnitude longer decay length compared to metallic layers. We combine chiral spin structures and spin-orbit torques for efficient switching and identify skyrmions that allow us to establish the GGG/TmIG interface as the origin of the DMI.
Chiral magnetic Mn$_x$Fe$_{1-x}$Ge compounds have an antisymmetric exchange interaction that is tunable with the manganese stoichiometric fraction, $x$. Although millimeter-scale, polycrystalline bulk samples of this family of compounds have been produced, thin-fi
Facing the ever-growing demand for data storage will most probably require a new paradigm. Nanoscale magnetic skyrmions are anticipated to solve this issue as they are arguably the smallest spin textures in magnetic thin films in nature. We designed cobalt-based multilayered thin films where the cobalt layer is sandwiched between two heavy metals providing additive interfacial Dzyaloshinskii-Moriya interactions, which reach a value close to 2 mJ m-2 in the case of the Ir|Co|Pt asymmetric multilayers. Using a magnetization-sensitive scanning x-ray transmission microscopy technique, we imaged small magnetic domains at very low field in these multilayers. The study of their behavior in perpendicular magnetic field allows us to conclude that they are actually magnetic skyrmions stabilized by the large Dzyaloshinskii-Moriya interaction. This discovery of stable sub-100 nm individual skyrmions at room temperature in a technologically relevant material opens the way for device applications in a near future.
The current driven motion of skyrmions in MnSi and FeGe thinned single crystals could be initiated at current densities of the order of $10^6$ A/m, five orders of magnitude smaller than for magnetic domain walls. The technologically crucial step of replicating these results in thin films has not been successful to date, but the reasons are not clear. Elucidating them requires analyzing system characteristics at scales of few nm where the key Dzyaloshinskii Moriya (DM) interactions vary, and doing so in near application conditions, i.e. oxidation protected systems at room temperature. In this works magnetic force microscopy (MFM) studies of magnetron sputtered Ir/Co/Pt multilayers we show skyrmions that are smaller than previously observed, are not circularly symmetric, and are pinned to 50 nm wide areas of 75 percent higher than average DM interaction. This finding matches our measurement of Co layer thickness inhomogeneity of the order of $pm$1.2 atomic monolayers per 0.6 nm layer, and indicates that layer flatness must be controlled with greater precision to preclude skyrmion pinning.
Magnetic skyrmions hold promise for spintronic devices. To explore the dynamical properties of skyrmions in devices, a nanoscale method to image spin textures in response to a stimulus is essential. Here, we apply a technique for operando electrical current pulsing of chiral magnetic devices in a Lorentz transmission electron microscope. In ferromagnetic multilayers with interfacial Dzyaloshinskii-Moriya interaction (DMI), we study the creation and annihilation of skyrmions localized by point-like pinning sites due to defects. Using a combination of experimental and micromagnetic techniques, we establish a thermal contribution for the creation and annihilation of skyrmions in our study. Our work reveals a mechanism for controlling skyrmion density, which enables an examination of skyrmion magnetic field stability as a function of density. We find that high-density skyrmion states are more stable than low-density states or isolated skyrmions resisting annihilation over a magnetic field range that increases monotonically with density.