تسجيل مستخدم جديدCharacterization of Three-Dimensional Microstructures in Single Crystal Diamond
97
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We report on the Raman and photoluminescence characterization of three-dimensional microstructures created in single crystal diamond with a Focused Ion Beam (FIB) assisted lift-off technique. The method is based on MeV ion implantation to create a buried etchable layer, followed by FIB patterning and selective etching. In the applications of such microstructures where the properties of high quality single crystal diamond are most relevant, residual damage after the fabrication process represents a critical technological issue. The results of Raman and photoluminescence characterization indicate that the partial distortion of the sp3-bonded lattice and the formation of isolated point defects are effectively removed after thermal annealing, leaving low amounts of residual damage in the final structures. Three-dimensional microstructures in single-crystal diamond offer a large range of applications, such as quantum optics devices and fully integrated opto mechanical assemblies.
قيم البحث
اقرأ أيضاً
We report on the systematic characterization of conductive micro-channels fabricated in single-crystal diamond with direct ion microbeam writing. Focused high-energy (~MeV) helium ions are employed to selectively convert diamond with micrometric spat
ial accuracy to a stable graphitic phase upon thermal annealing, due to the induced structural damage occurring at the end-of-range. A variable-thickness mask allows the accurate modulation of the depth at which the microchannels are formed, from several {mu}m deep up to the very surface of the sample. By means of cross-sectional transmission electron microscopy (TEM) we demonstrate that the technique allows the direct writing of amorphous (and graphitic, upon suitable thermal annealing) microstructures extending within the insulating diamond matrix in the three spatial directions, and in particular that buried channels embedded in a highly insulating matrix emerge and electrically connect to the sample surface at specific locations. Moreover, by means of electrical characterization both at room temperature and variable temperature, we investigate the conductivity and the charge-transport mechanisms of microchannels obtained by implantation at different ion fluences and after subsequent thermal processes, demonstrating that upon high-temperature annealing, the channels implanted above a critical damage density convert to a stable graphitic phase. These structures have significant impact for different applications, such as compact ionizing radiation detectors, dosimeters, bio-sensors and more generally diamond-based devices with buried three-dimensional all-carbon electrodes.
We report on a novel method for the fabrication of three-dimensional buried graphitic micropaths in single crystal diamond with the employment of focused MeV ions. The use of implantation masks with graded thickness at the sub-micrometer scale allows
the formation of conductive channels which are embedded in the insulating matrix at controllable depths. In particular, the modulation of the channels depth at their endpoints allows the surface contacting of the channel terminations with no need of further fabrication stages. In the present work we describe the sample masking, which includes the deposition of semi spherical gold contacts on the sample surface, followed by MeV ion implantation. Because of the significant difference between the densities of pristine and amorphous or graphitized diamond, the formation of buried channels has a relevant mechanical effect on the diamond structure, causing localized surface swelling, which has been measured both with interferometric profilometry and atomic force microscopy. The electrical properties of the buried channels are then measured with a two point probe station: clear evidence is given that only the terminal points of the channels are electrically connected with the surface, while the rest of the channels extends below the surface. IV measurements are employed also to qualitatively investigate the electrical properties of the channels as a function of implantation fluence and annealing.
We demonstrate the fabrication of sub-micron layers of single-crystal diamond suitable for subsequent processing as demonstrated by this test ring structure. This method is a significant enabling technology for nanomechanical and photonic structures
incorporating colour-centres. The process uses a novel double implant process, annealing and chemical etching to produce membranes of diamond from single-crystal starting material, the thinnest layers achieved to date are 210 nm thick.
Boron-doped single crystal diamond films were grown homoepitaxially on synthetic (100) Type Ib diamond substrates using microwave plasma assisted chemical vapor deposition. A modification in surface morphology of the film with increasing boron concen
tration in the plasma has been observed using atomic force microscopy. Use of nitrogen during boron doping has been found to improve the surface morphology and the growth rate of films but it lowers the electrical conductivity of the film. The Raman spectra indicated a zone center optical phonon mode along with a few additional bands at the lower wavenumber regions. The change in the peak profile of the zone center optical phonon mode and its downshift were observed with the increasing boron content in the film. However, shrinkage and upshift of Raman line was observed in the film that was grown in presence of nitrogen along with diborane in process gas.
With the best overall electronic and thermal properties, single crystal diamond (SCD) is the extreme wide bandgap material that is expected to revolutionize power electronics and radio-frequency electronics in the future. However, turning SCD into us
eful semiconductors requires overcoming doping challenges, as conventional substitutional doping techniques, such as thermal diffusion and ion implantation, are not easily applicable to SCD. Here we report a simple and easily accessible doping strategy demonstrating that electrically activated, substitutional doping in SCD without inducing graphitization transition or lattice damage can be readily realized with thermal diffusion at relatively low temperatures by using heavily doped Si nanomembranes as a unique dopant carrying medium. Atomistic simulations elucidate a vacancy exchange boron doping mechanism that occur at the bonded interface between Si and diamond. We further demonstrate selectively doped high voltage diodes and half-wave rectifier circuits using such doped SCD. Our new doping strategy has established a reachable path toward using SCDs for future high voltage power conversion systems and for other novel diamond based electronic devices. The novel doping mechanism may find its critical use in other wide bandgap semiconductors.