We report on a novel method for the fabrication of three-dimensional buried graphitic micropaths in single crystal diamond with the employment of focused MeV ions. The use of implantation masks with graded thickness at the sub-micrometer scale allows the formation of conductive channels which are embedded in the insulating matrix at controllable depths. In particular, the modulation of the channels depth at their endpoints allows the surface contacting of the channel terminations with no need of further fabrication stages. In the present work we describe the sample masking, which includes the deposition of semi spherical gold contacts on the sample surface, followed by MeV ion implantation. Because of the significant difference between the densities of pristine and amorphous or graphitized diamond, the formation of buried channels has a relevant mechanical effect on the diamond structure, causing localized surface swelling, which has been measured both with interferometric profilometry and atomic force microscopy. The electrical properties of the buried channels are then measured with a two point probe station: clear evidence is given that only the terminal points of the channels are electrically connected with the surface, while the rest of the channels extends below the surface. IV measurements are employed also to qualitatively investigate the electrical properties of the channels as a function of implantation fluence and annealing.
قيم البحث
اقرأ أيضاً
In the present work we report about the investigation of the conduction mechanism of sp2 carbon micro-channels buried in single crystal diamond. The structures are fabricated with a novel technique which employs a MeV focused ion-beam to damage diamo
nd in conjunction with variable thickness masks. This process changes significantly the structural proprieties of the target material, because the ion nuclear energy loss induces carbon conversion from sp3 to sp2 state mainly at the end of range of the ions (few micrometers). Furthermore, placing a mask with increasing thickness on the sample it is possible to modulate the channels depth at their endpoints, allowing their electrical connection with the surface. A single-crystal HPHT diamond sample was implanted with 1.8 MeV He+ ions at room temperature, the implantation fluence was set in the range 2.1x10^16 - 6.3x10^17 ions cm^-2, determining the formation of buried micro-channels at 3 um. After deposition of metallic contacts at the channels endpoints, the electrical characterization was performed measuring the I-V curves at variable temperatures in the 80-690 K range. The Variable Range Hopping model was used to fit the experimental data in the ohmic regime, allowing the estimation of characteristic parameters such as the density of localized states at the Fermi level. A value of 5.5x10^17 states cm-3 eV-1 was obtained, in satisfactory agreement with values previously reported in literature. The power-law dependence between current and voltage is consistent with the space charge limited mechanism at moderate electric fields.
As demonstrated in previous works, implantation with a MeV ion microbeam through masks with graded thickness allows the formation of conductive micro-channels in diamond which are embedded in the insulating matrix at controllable depths [P. Olivero e
t al., Diamond Relat. Mater. 18 (5-8), 870-876 (2009)]. In the present work we report about the systematic electrical characterization of such micro-channels as a function of several implantation conditions, namely: ion species and energy, implantation fluence. The current-voltage (IV) characteristics of the buried channels were measured at room temperature with a two point probe station. Significant parameters such as the sheet resistance and the characteristic exponent (alpha) of the IV power-law trend were expressed as a function of damage density, with satisfactory compatibility between the results obtained in different implantation conditions.
We report on the systematic characterization of conductive micro-channels fabricated in single-crystal diamond with direct ion microbeam writing. Focused high-energy (~MeV) helium ions are employed to selectively convert diamond with micrometric spat
ial accuracy to a stable graphitic phase upon thermal annealing, due to the induced structural damage occurring at the end-of-range. A variable-thickness mask allows the accurate modulation of the depth at which the microchannels are formed, from several {mu}m deep up to the very surface of the sample. By means of cross-sectional transmission electron microscopy (TEM) we demonstrate that the technique allows the direct writing of amorphous (and graphitic, upon suitable thermal annealing) microstructures extending within the insulating diamond matrix in the three spatial directions, and in particular that buried channels embedded in a highly insulating matrix emerge and electrically connect to the sample surface at specific locations. Moreover, by means of electrical characterization both at room temperature and variable temperature, we investigate the conductivity and the charge-transport mechanisms of microchannels obtained by implantation at different ion fluences and after subsequent thermal processes, demonstrating that upon high-temperature annealing, the channels implanted above a critical damage density convert to a stable graphitic phase. These structures have significant impact for different applications, such as compact ionizing radiation detectors, dosimeters, bio-sensors and more generally diamond-based devices with buried three-dimensional all-carbon electrodes.
We report on the Raman and photoluminescence characterization of three-dimensional microstructures created in single crystal diamond with a Focused Ion Beam (FIB) assisted lift-off technique. The method is based on MeV ion implantation to create a bu
ried etchable layer, followed by FIB patterning and selective etching. In the applications of such microstructures where the properties of high quality single crystal diamond are most relevant, residual damage after the fabrication process represents a critical technological issue. The results of Raman and photoluminescence characterization indicate that the partial distortion of the sp3-bonded lattice and the formation of isolated point defects are effectively removed after thermal annealing, leaving low amounts of residual damage in the final structures. Three-dimensional microstructures in single-crystal diamond offer a large range of applications, such as quantum optics devices and fully integrated opto mechanical assemblies.
We demonstrate the fabrication of sub-micron layers of single-crystal diamond suitable for subsequent processing as demonstrated by this test ring structure. This method is a significant enabling technology for nanomechanical and photonic structures
incorporating colour-centres. The process uses a novel double implant process, annealing and chemical etching to produce membranes of diamond from single-crystal starting material, the thinnest layers achieved to date are 210 nm thick.