تسجيل مستخدم جديدDefect structures in MgB2 wires introduced by hot isostatic pressing
107
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
The microstructures of MgB2 wires prepared by the powder-in-tube technique and subsequent hot isostatic pressing were investigated using transmission electron microscopy. Large amount of crystalline defects including small angle twisting, tilting, and bending boundaries, in which high densities of dislocations reside, were found forming sub-grains within MgB2 grains. It is believed that these defects resulted from particle deformation during the hot isostatic pressing process and are effective flux pinning centers that contribute to the high critical current densities of the wires at high temperatures and at high fields.
قيم البحث
اقرأ أيضاً
The critical current density (Jc) of hot isostatic pressed (HIPed) MgB2 wires, measured by d.c. transport and magnetization, is compared with that of similar wires annealed at ambient pressure. The HIPed wires have a higher Jc than the annealed wires
, especially at high temperatures and magnetic fields, and higher irreversibility field (Hirr). The HIPed wires are promising for applications, with Jc>106 A/cm2 at 5 K and zero field and >104 A/cm2 at 1.5 T and 26.5 K, and Hirr ~ 17 T at 4 K. The improvement is attributed to a high density of structural defects, which are the likely source of vortex pinning. These defects, observed by transmission electron microscopy, include small angle twisting, tilting, and bending boundaries, resulting in the formation of sub-grains within MgB2 crystallites.
A trapped field of over 3 T has been measured at 17.5 K in a magnetised stack of two disc-shaped bulk MgB2 superconductors of diameter 25 mm and thickness 5.4 mm. The bulk MgB2 samples were fabricated by uniaxial hot pressing, which is a readily scal
able, industrial technique, to 91% of their maximum theoretical density. The macroscopic critical current density derived from the trapped field data using the Biot-Savart law is consistent with the measured local critical current density. From this we conclude that critical current density, and therefore trapped field performance, is limited by the flux pinning available in MgB2, rather than by lack of connectivity. This suggests strongly that both increasing sample size and enhancing pinning through doping will allow further increases in trapped field performance of bulk MgB2.
MgB2 samples prepared by solid-state reaction were investigated using high-resolution transmission electron microscopy (HREM), X-ray energy-dispersive spectroscopy (EDX), electron energy-loss spectroscopy (EELS), and energy-filtered imaging. Large am
ounts of coherent precipitates with a size range from about 5 nm up to about 100 nm were found in the MgB2 crystallite matrices. The precipitates are of different shapes including sphere, ellipsoid, and faceted polyhedron depending on the size of the precipitates. EDX and EELS analyses confirm that smaller precipitates contain magnesium, boron and oxygen while larger faceted precipitates contain mainly magnesium and oxygen, implying that the oxygen content increases with precipitate size. HREM and electron diffraction investigations found that the precipitates have the same crystal lattice structure as that of MgB2 but with various composition modulations depending on the composition of the precipitates. The precipitates transform to the MgO phase after long exposure to residual oxygen in flowing Ar gas at high temperatures. The effect of the precipitates in different size ranges on flux pinning is discussed.
The zone-center $E_{2g}$ modes play a crucial role in MgB$_2$, controlling the scattering mechanisms in the normal state as well the superconducting pairing. Here, we demonstrate via first-principles quantum-field theory calculations that, due to the
anisotropic electron-phonon interaction, a $hot$-$phonon$ regime where the $E_{2g}$ phonons can achieve significantly larger effective populations than other modes, is triggered in MgB$_2$ by the interaction with an ultra-short laser pulse. Spectral signatures of this scenario in ultrafast pump-probe Raman spectroscopy are discussed in detail, revealing also a fundamental role of nonadiabatic processes in the optical features of the $E_{2g}$ mode.
The superconductivities of samples prepared by several procedures were found to degrade under ambient environment. The degradation mechanism was studied by measuring the change of surface chemical composition of dense MgB2 pellets (prepared by hot is
ostatic pressure, HIPed) under atmospheric exposure using X-ray Photoelectron Spectroscopy (XPS). Results showed that samples with poor connectivity between grains and with smaller grain sizes degrade with time when exposed to ambient conditions. In these samples, the Tc did not change with time, but the superconducting transition became broader and the Meissner fraction decreased. In contrast, our well-sintered and the HIPed samples remained stable for several months under ambient condition. The degradation was found to be related to surface decomposition as observed by XPS. We observed the formation of oxidized Mg, primarily in the form of a Mg hydroxide, the increase of C and O contents, and the reduction of B concentration in the surface layer of MgB2 samples.